Foil printing

Patent metadata

Field	Value
Publication number	US-10618258-B2
Application number	US-201615772079-A
Country	US
Kind code	B2
Filing date	Jan 14, 2016
Priority date	Jan 14, 2016
Publication date	Apr 14, 2020
Grant date	Apr 14, 2020

Abstract

Herein is described a method of applying foil from a foil web to a substrate. The method may comprise: ink-jet printing a UV-curable adhesive onto the substrate in a predetermined image area; subjecting the adhesive to a first curing by exposing the adhesive to UV light in a dosage range of 140-170 mJ/cm 2 ; passing the substrate and a foil web through a nip where the foil web is pressed against the adhesive; subjecting the adhesive disposed between the substrate and the foil web to a second curing by exposing the adhesive to UV light in a dosage of at least 250 mJ/cm 2 ; and separating excess foil from the substrate, to leave foil on the predetermined image area. Substrates and UV-curable adhesives are also described.

First claim

The invention claimed is:

1. A method of applying foil from a foil web to a substrate, the method comprising:
ink-jet printing a UV-curable adhesive onto the substrate in a predetermined image area, wherein the UV-curable adhesive comprises:
a non-curable acrylic polymer;
a monofunctional monomer;
a multifunctional monomer; and
a photoinitiator;

subjecting the adhesive to a first curing by exposing the adhesive to UV light in a dosage range of 140-170 mJ/cm 2 ;
passing the substrate and a foil web through a nip where the foil web is pressed against the adhesive;
subjecting the adhesive disposed between the substrate and the foil web to a second curing by exposing the adhesive to UV light in a dosage of at least 250 mJ/cm 2 ; and
separating excess foil from the substrate, to leave foil on the predetermined image area;
wherein the non-curable acrylic polymer is a resin that does not polymerize with the monofunctional monomer or the multifunctional monomer during either of the first or second curing.

2. The method of claim 1 , wherein the non-curable acrylic polymer is present in the UV-curable adhesive in an amount representing from about 1% to about 10% of the total weight of the UV-curable adhesive.

3. The method of claim 1 , wherein the non-curable acrylic polymer has a molecular weight in the range of from about 5,000 to about 20,000 Daltons and/or has a glass transition temperature (T g ) that is below 60° C.

4. The method of claim 1 , wherein the non-curable acrylic polymer is selected from the group consisting of styrene acrylic resins, butyl methacrylate resins, ethyl methacrylate resins, isobutyl methacrylate resins, methyl methacrylate resins, styrene acrylates, and copolymers thereof.

5. The method of claim 1 , wherein the non-curable acrylic polymer comprises a copolymer of methyl methacrylate and butyl methacrylate.

6. The method of claim 1 , wherein the UV-curable adhesive has a viscosity, before the first curing and when measured at the temperature at which the adhesive will be when ink-jet printed onto the substrate (the jetting temperature), of from about 5 cP to about 20 cP.

7. The method of claim 1 , wherein the adhesive is printed in a thickness of about 95 μm or less.

8. The method of claim 1 , wherein the monofunctional monomer and the multifunctional monomer each comprise at least one acrylate group.

9. The method of claim 1 , wherein the foil that is left on the predetermined image area comprises a film or sheet having a thickness of about 200 μm or less.

10. The method of claim 1 , wherein the UV light source is an LED UV source.

11. The method of claim 1 , wherein the UV light has a wavelength in a range of from 315 nm to 450 nm.

12. The method of claim 1 , wherein the non-curable acrylic polymer comprises an isobutyl methacrylate resin.

Assignees

• Hp Scitex Ltd

Inventors

• Cohen Eytan
• Trubnikov Alex
• Dayan Benjamin
• Soroker Efrat
• Rubin Shimrit

Classifications

• B32B2255/12

  on paper layer · CPC title

• B32B15/046

  of foam · CPC title

• B32B2307/406

  Bright, glossy, shiny surface · CPC title

• B32B15/12

  of paper or cardboard · CPC title

• B32B27/365

  comprising polycarbonates · CPC title