Production method of soft magnetic metal powder

Patent metadata

Field	Value
Publication number	US-10607757-B1
Application number	US-201715639001-A
Country	US
Kind code	B1
Filing date	Jun 30, 2017
Priority date	Jun 30, 2017
Publication date	Mar 31, 2020
Grant date	Mar 31, 2020

Abstract

The present invention is a method of producing a soft magnetic metal powder comprising, a material powder preparation step of preparing a material powder comprising a particle including a boron and a soft magnetic metal including an iron, a first nitriding step of nitriding the boron included in said particle by carrying out a heat treatment to said material powder under a non-oxidizing atmosphere including nitrogen, and a spheroidizing step of spheroidizing said particle by carrying out a heat treatment to said material powder of after said first nitriding step under a non-oxidizing atmosphere having lower nitrogen partial pressure than a nitrogen partial pressure of the non-oxidizing atmosphere during said first nitriding step. According to the present invention, the soft magnetic metal powder comprising the particle having a shape of a complete sphere or close to complete sphere, and comprising the small standard deviation of the particle size distribution of the powder can be obtained.

First claim

What is claimed is:

1. A method of producing a soft magnetic metal powder comprising:
a material powder preparation step of preparing a material powder comprising particles that include boron and a soft magnetic metal including iron,
a first nitriding step of nitriding the boron included in said particles by carrying out a heat treatment on said material powder under a non-oxidizing atmosphere including nitrogen,
a spheroidizing step of spheroidizing said particles to obtain spheroidized particles by carrying out a heat treatment on said material powder after said first nitriding step under a non-oxidizing atmosphere having lower nitrogen partial pressure than a nitrogen partial pressure of the non-oxidizing atmosphere during said first nitriding step, and
a second nitriding step of nitriding the boron included in said spheroidized particles by carrying out a heat treatment on the material powder comprising said spheroidized particles under a non-oxidizing atmosphere having higher nitrogen partial pressure than the nitrogen partial pressure of the non-oxidizing atmosphere during said spheroidizing step, wherein a temperature of the heat treatment during said second nitriding step is within a range from 1200° C. to 1350° C.

2. The method of producing the soft magnetic metal powder as set forth in claim 1 further comprising a boron nitride removal step of removing a part of the boron nitride included in said spheroidized particles.

3. The method of producing the soft magnetic metal powder as set forth in claim 1 , wherein a coating including boron nitride is formed on surfaces of said particles during said first nitriding step.

4. The method of producing the soft magnetic metal powder as set forth in claim 1 , wherein a coating including boron nitride is formed on surfaces of said spheroidized particles during said second nitriding step.

5. The method of producing the soft magnetic metal powder as set forth in claim 1 , wherein a content of said boron included in the material powder is within a range from 0.4 mass % to 2.0 mass % during said material powder preparation step.

6. The method of producing the soft magnetic metal powder as set forth in claim 1 , wherein said soft magnetic metal is crystalline.

7. The method of producing the soft magnetic metal powder as set forth in claim 1 , wherein said material powder is contained in a container during said first nitriding step and said spheroidizing step.

8. The method of producing the soft magnetic metal powder as set forth in claim 1 , wherein said material powder is contained in a crucible during said first nitriding step and said spheroidizing step.

9. The method of producing the soft magnetic metal powder as set forth in claim 1 , wherein 90% or more of said spheroidized particles have a roundness of 0.80 or more and the method is performed without classifying said spheroidized particles.

10. The method of producing the soft magnetic metal powder as set forth in claim 1 , wherein a temperature of the heat treatment during said spheroidizing step is within a range from 1100° C. to 1300° C.

11. The method of producing the soft magnetic metal powder as set forth in claim 1 , wherein the non-oxidizing atmosphere during said spheroidizing step has an oxygen partial pressure of 0.0001 atm or less.

12. The method of producing the soft magnetic metal powder as set forth in claim 1 , wherein the non-oxidizing atmosphere during said spheroidizing step is an argon atmosphere having 100% argon or a mixed atmosphere of argon and nitrogen with a nitrogen partial pressure of less than 0.01 atm.

Assignees

• Tdk Corp

Inventors

• Sakurai Yu
• Kuroda Tomofumi
• Itoh Hideyuki

Classifications

• H01F1/20

  in the form of particles, e.g. powder (H01F1/147 takes precedence) · CPC title

• C23C8/24 Primary

  Nitriding · CPC title

• C23C8/80

  After-treatment · CPC title

• H01F41/0246

  Manufacturing of magnetic circuits by moulding or by pressing powder (magnetic cores made by moulding or by pressing powder H01F27/255; soft magnetic particles H01F1/20, H01F1/36) · CPC title

• B22F1/0048

  Operations & Transport · mapped topic