Doped lithium positive electrode active material and process for manufacture thereof

Patent metadata

Field	Value
Publication number	US-10601041-B2
Application number	US-201916371474-A
Country	US
Kind code	B2
Filing date	Apr 1, 2019
Priority date	May 9, 2018
Publication date	Mar 24, 2020
Grant date	Mar 24, 2020

Abstract

A lithium positive electrode active material including at least 95 wt % spinel having a chemical composition of LixNiyMn2-y-z1-z2D1z1D2z2O4, wherein 0.9≤x≤1.1, 0.4≤y≤0.5, 0.005≤z1≤0.2, 0≤z2≤0.2, wherein D1 and D2 are dopants chosen between the following elements: Co, Cu, Ti, Zn, Mg, Fe or combinations thereof. D1 and D2 are different dopants, and the lithium positive electrode active material is a powder composed of material particles, wherein the distribution of dopant D1 is non-uniform along a radial axis of the material particles and the distribution of the dopant D2 is substantially uniform along the radial axis of the material particles. Also, a process for preparing the lithium positive electrode active material and a secondary battery comprising the lithium positive electrode active material.

First claim

The invention claimed is:

1. A lithium positive electrode active material comprising at least 95 wt % spinel having a chemical composition of Li x Ni y Mn 2-y-z1-z2 D1 z1 D2 z2 O 4 ,
wherein 0.9≤x≤1.1, 0.4≤y≤0.5, 0.005≤z1≤0.2, 0≤z2≤0.2,
wherein D1 and D2 are dopants chosen between the following elements: Co, Cu, Ti, Zn, Mg, Fe or combinations thereof, where D1 and D2 are different dopants,
wherein the lithium positive electrode active material is a powder composed of material particles,
wherein the distribution of dopant D1 is non-uniform along a radial axis of the material particles and wherein the distribution of the dopant D2 is substantially uniform along the radial axis of the material particles.

2. The lithium positive electrode active material according to claim 1 , wherein said material particles of said lithium positive electrode active material are primary particles, where the primary particles form secondary particles, wherein at least 95% of the primary particles have a diameter or a volume equivalent diameter of between 100 nm and 2 μm and where at least 95% of the secondary particles have a diameter or volume equivalent diameter of between 1 μm and 25 μm.

3. The lithium positive electrode active material according to claim 2 , wherein the primary particles of the lithium positive electrode active material are surface modified with the dopant D1.

4. The lithium positive electrode active material according to claim 2 , wherein the dopant D1 is present in the outermost 20% of the primary particles.

5. The lithium positive electrode active material according claim 2 , wherein the dopant D1 is part of the spinel.

6. The lithium positive electrode active material according to claim 1 , wherein said material particles of said lithium positive electrode active material are secondary particles made up of primary particles, wherein the diameter or the volume equivalent diameter of the primary particles is between 100 nm and 2 μm and where the diameter or the volume equivalent diameter of the secondary particles is between 1 μm and 25 μm.

7. The lithium positive electrode active material according to claim 6 , wherein the secondary particles of the lithium positive electrode active material are surface modified with the dopant D1.

8. The lithium positive electrode active material according to claim 6 , wherein the dopant D1 is present in the outermost 20% of the secondary particles.

9. The lithium positive electrode active material according to claim 6 , wherein the dopant D1 is part of the spinel.

10. The lithium positive electrode active material according to claim 1 , wherein the oxidation state of the dopant D1 is larger than 2.

11. The lithium positive electrode active material according claim 1 , wherein said lithium positive electrode active material is cation disordered.

12. The lithium positive electrode active material according claim 1 , wherein said lithium positive electrode active material has a tap density of at least 1.9 g/cm 3 .

13. The lithium positive electrode active material according to claim 1 , wherein the BET surface area of the secondary particles is below 0.25 m 2 /g.

14. The lithium positive electrode active material according to claim 2 , wherein the secondary particles have an average circularity higher than 0.90 and simultaneously an average aspect ratio lower than 1.50.

15. The lithium positive electrode active material according to claim 2 , wherein D50 of the secondary particles is between 3 and 50 μm.

16. The lithium positive electrode active material according to claim 15 , wherein the distribution of the agglomerate size of the secondary particles is such that the ratio between D90 and D10 is smaller than or equal to 4.

17. The lithium positive electrode active material according to claim 1 , wherein the capacity of the lithium positive electrode active material is above 120 mAh/g.

18. The lithium positive electrode active material according to claim 1 , wherein the separation between the two Ni-plateaus around 4.7 V of the lithium positive electrode active material is at least 50 mV.

19. A process for preparing the lithium positive electrode active material of claim 1 ,
said process comprising the steps of:
a) providing a lithium positive electrode active material comprising at least 95 wt % spinel having a chemical composition of Li x Ni y Mn 2-y-z2 D2 z2 O 4 , wherein 0.9≤x≤1.1, 0.4≤y≤0.5, and 0≤z2≤0.2,
b) mixing the lithium positive electrode active material of step a) with a dopant precursor of the dopant D1,
c) heating the mixture of step b) to a temperature of between 300° C. and 700° C.

20. The process according to claim 19 , wherein the temperature of step c) and the duration in time of step c) are controlled so as to prevent uniform distribution of the dopant D1 throughout the lithium positive electrode material.

21. A secondary battery comprising a positive electrode which comprises the lithium positive electrode active material according to claim 1 .

Assignees

• Haldor Topsoe As

Inventors

• H∅Jberg Jonathan
• Høj Jakob Weiland
• Dahl Søren
• Elkjær Christian Fink

Classifications

• H01M4/525 Primary

  of mixed oxides or hydroxides containing iron, cobalt or nickel for inserting or intercalating light metals, e.g. LiNiO2, LiCoO2 or LiCoOxFy · CPC title

• H01M4/505

  of mixed oxides or hydroxides containing manganese for inserting or intercalating light metals, e.g. LiMn2O4 or LiMn2OxFy · CPC title

• H01M4/485 Primary

  of mixed oxides or hydroxides for inserting or intercalating light metals, e.g. LiTi2O4 or LiTi2OxFy (H01M4/505, H01M4/525 take precedence) · CPC title

• H01M10/0525

  Rocking-chair batteries, i.e. batteries with lithium insertion or intercalation in both electrodes; Lithium-ion batteries · CPC title

• H01M4/362

  Composites · CPC title