Dimensionally stable geopolymer composition and method

Patent metadata

Field	Value
Publication number	US-10597327-B2
Application number	US-201916244689-A
Country	US
Kind code	B2
Filing date	Jan 10, 2019
Priority date	Apr 27, 2012
Publication date	Mar 24, 2020
Grant date	Mar 24, 2020

Abstract

A method for making geopolymer cementitious binder compositions for cementitious products such as concrete, precast construction elements and panels, mortar and repair materials, and the like is disclosed. The geopolymer cementitious compositions of some embodiments are made by mixing a synergistic mixture of thermally activated aluminosilicate mineral, calcium aluminate cement, a calcium sulfate and a chemical activator with water.

First claim

What is claimed is:

1. An aluminosilicate geopolymer cementitious composition comprising a reaction product of:
a cementitious reactive powder comprising:
about 35 to about 90% by weight a thermally activated aluminosilicate mineral;
about 9 to about 45% by weight a calcium aluminate cement in an amount of 1-100 parts by weight per 100 parts by weight of thermally activated aluminosilicate mineral; and
about 1 to about 45% by weight a calcium sulfate selected from the group consisting of calcium sulfate dihydrate, calcium sulfate hemihydrate, anhydrous calcium sulfate and mixtures thereof, the calcium sulfate in an amount of 2 to 100 parts by weight per 100 parts by weight of calcium aluminate cement; and

a chemical activator selected from the group consisting of alkali metal salt, alkali metal base, and mixtures thereof in an amount equal to about 1.0 to about 6.0% by weight based on total weight of the cementitious reactive powder; and
at least one member of the group consisting of superplasticizers, air entraining agents, defoaming agents, organic rheology control agents, and film-forming polymers; and
water.

2. The composition of claim 1 , wherein the cementitious reactive powder contains calcium sulfate dihydrate.

3. The composition of claim 1 , wherein the chemical activator is present in an amount equal to about 1.25 to 4.00% by weight based on total weight of the cementitious reactive powder, wherein the chemical activator is selected from at least one member of the group consisting of alkali metal citrate, alkali metal silicate, and alkali metal hydroxide.

4. The composition of claim 1 , wherein the cementitious reactive powder contains calcium sulfate hemihydrate.

5. The composition of claim 1 , wherein the cementitious reactive powder contains anhydrous calcium sulfate.

6. The composition of claim 1 , wherein the reactive powder contains from about 10 to about 40 wt. % lime.

7. The composition of claim 1 ,
wherein the cementitious reactive powder comprises about 10% to about 36% by weight calcium aluminate cement,
wherein the chemical activator is selected from the group consisting of alkali metal citrate, alkali metal silicate, alkali metal hydroxide, and mixtures thereof,
wherein calcium sulfate dihydrate is present in an amount equal to 5 to 30 wt. % of the total of the fly ash and calcium aluminate cement, and
wherein the composition comprises said superplasticizer.

8. The composition of claim 1 , wherein the thermally activated aluminosilicate mineral comprises Class F fly ash.

9. The composition of claim 1 , wherein the reaction product is formed from
the water;
the cementitious reactive powder comprising:
about 40% to about 85% by weight thermally activated aluminosilicate mineral, wherein the thermally activated aluminosilicate mineral comprises about 75 parts to about 100 parts fly ash per 100 parts thermally activated aluminosilicate mineral;
about 9% to about 40% by weight calcium aluminate cement, and
about 3.0% to about 24% by weight calcium sulfate; and

about 1.25 to 4.00% by weight said chemical activator activator based on weight of the cementitious reactive powder.

10. The composition of claim 1 , wherein the reaction product is formed from
the water;
the cementitious reactive powder comprising:
about 50% to about 80% by weight thermally activated aluminosilicate mineral, wherein said thermally activated aluminosilicate mineral comprises about 75 parts to about 100 parts fly ash per 100 parts thermally activated aluminosilicate mineral,
about 10% to about 36% by weight calcium aluminate cement, and
about 5.0% to about 18% by weight calcium sulfate; and

about 1.25 to 4.00% by weight said chemical activator activator based on weight of the cementitious reactive powder, said chemical activator selected from at least one member of the group consisting of alkali metal citrate, alkali metal silicate, alkali metal hydroxide and mixtures thereof.

11. The composition of claim 8 , wherein the cementitious reactive powder comprises about 10 to about 40 wt. % lime.

12. The composition of claim 1 , wherein the weight ratio of water to the cementitious reactive powder is about 0.15 to about 0.4.

13. The composition of claim 1 , further comprising calcium sulfoaluminate cement.

14. The composition of claim 1 , further comprising lithium carbonate.

15. A method of preparing the aluminosilicate geopolymer cementitious composition of claim 1 , comprising:
reacting
the cementitious reactive powder comprises thermally activated aluminosilicate mineral, the calcium aluminate cement, the calcium sulfate selected from the group consisting of calcium sulfate dihydrate, calcium sulfate hemihydrate, anhydrous calcium sulfate, and mixtures thereof,
the chemical activator selected from the group consisting of the alkali metal citrate, alkali metal silicate, alkali metal hydroxide, and mixtures thereof,
the at least one member of the group consisting of superplasticizers, air entraining agents, defoaming agents, organic rheology control agents, and film-forming polymers; and
the water.

16. A settable composition for forming an aluminosilicate geopolymer cementitious composition when reacted in water, comprising
a settable mixture of:
a cementitious reactive powder comprising:
about 35 to about 90% by weight of a thermally activated aluminosilicate mineral;
about 9 to about 45% by weight of a calcium aluminate cement;
about 1 to about 45% by weight of a calcium sulfate selected from the group consisting of calcium sulfate dihydrate, calcium sulfate hemihydrate, anhydrous calcium sulfate and mixtures thereof; and

a chemical activator selected from the group consisting of an alkali metal salt and an alkali metal base, or mixtures thereof in an amount equal to about 1.0 to about 6.0% by weight based on total weight of the cementitious reactive powder; and
at least one member of the group consisting of superplasticizers, air entraining agents, defoaming agents, organic rheology control agents, and film-forming polymers.

17. An aluminosilicate geopolymer composition formed from the reaction of the settable composition of claim 16 with water,
wherein the weight ratio of the water to cementitious reactive powder is about 0.15 to about 0.4:1,
wherein the thermally activated aluminosilicate mineral comprises fly ash,
wherein the cementitious reactive powder has at most 5 wt. % Portland cement,
wherein the chemical activator is selected from the group consisting of alkali metal citrate, alkali metal silicate, alkali metal hydroxide, and mixtures thereof.

Assignees

• United States Gypsum Co

Inventors

• Dubey Ashish

Classifications

• C04B7/02

  Portland cement · CPC title

• C04B18/081

  from brown coal or lignite · CPC title

• C04B28/006 Primary

  containing mineral polymers, e.g. geopolymers of the Davidovits type · CPC title

• C04B24/04

  Carboxylic acids; Salts, anhydrides or esters thereof · CPC title

• C04B2201/05

  Materials having an early high strength, e.g. allowing fast demoulding or formless casting · CPC title