Surface treatment method for lithium cobalt oxide, and lithium secondary battery comprising same

Patent metadata

Field	Value
Publication number	US-10593943-B2
Application number	US-201615553614-A
Country	US
Kind code	B2
Filing date	Jan 11, 2016
Priority date	Apr 27, 2015
Publication date	Mar 17, 2020
Grant date	Mar 17, 2020

Abstract

The present invention relates to a surface treatment method for lithium cobalt oxide, comprising the steps of: (S1) mixing lithium cobalt oxide and an organic phosphoric acid compound; and (S2) heat treating and calcining the mixture prepared in step (S1). The surface treatment method of the present invention is simpler and has higher reproducibility than a conventional surface coating and doping technique, and can improve electrochemical characteristics by reinforcing the structural stability of lithium cobalt oxide. In addition, LiCoO2 prepared by the surface treatment method of the present invention is structurally stable during charging/discharging and does not cause unnecessary phase transition, and thus has excellent lifetime characteristics.

First claim

What is claimed is:

1. A surface treatment method for lithium cobalt oxide, comprising the steps of:
mixing lithium cobalt oxide with an organic phosphoric acid compound (S1); and
calcinating the mixture prepared in step S1 through thermal treatment.

2. The surface treatment method of claim 1 , wherein the lithium cobalt oxide is Li x CoO 2 (0.5<x≤1) or Li x Ni 1/3 Co 1/3 Mn 1/3 O 2 (0.5<x≤1).

3. The surface treatment method of claim 1 , wherein the organic phosphoric acid compound is one or a mixture of two or more selected from the group consisting of trioctylphosphine, trioctylphosphine oxide, triphenylphosphine, triphenylphosphate, parathion, and aminophosphonates.

4. The surface treatment method of claim 1 , wherein 5 parts by weight to 20 parts by weight of the organic phosphoric acid compound are mixed with respect to 100 parts by weight of the lithium cobalt oxide.

5. The surface treatment method of claim 1 , wherein 0.0001 moles to 0.0010 moles of phosphorous (P) are substituted with respect to cobalt (Co) in the lithium cobalt oxide.

6. The surface treatment method of claim 1 , wherein a temperature of the thermal treatment is 300° C. to 700° C.

7. The surface treatment method of claim 1 , wherein an atmosphere of the thermal treatment is an inert gas atmosphere.

8. The surface treatment method of claim 7 , wherein the inert gas is a gas selected from among helium, nitrogen, argon, neon, and xenon.

9. A method for preparing a cathode active material for a lithium secondary battery, the method comprising the steps of:
mixing lithium cobalt oxide with an organic phosphoric acid compound (S1); and
calcinating the mixture prepared in step S1 through thermal treatment.

10. The method of claim 9 , wherein the lithium cobalt oxide is LiCoO 2 .

11. The method of claim 9 , wherein the organic phosphoric acid compound is one or a mixture of two or more selected from the group consisting of trioctylphosphine, trioctylphosphine oxide, triphenylphosphine, triphenylphosphate, parathion, and aminophosphonates.

12. The method of claim 9 , wherein 5 parts by weight to 20 parts by weight of the organic phosphoric acid compound are mixed with respect to 100 parts by weight of the lithium cobalt oxide.

13. The method of claim 9 , wherein a temperature of the thermal treatment is 300° C. to 700° C.

Assignees

• Univ Dongguk Ind Acad Coop

Inventors

• Kang Yong-Mook
• Min Seul-Hee
• Jo Mi-Ru

Classifications

• C01P2002/54

  one element only · CPC title

• C01G53/42

  containing alkali metals, e.g. LiNiO2 · CPC title

• H01M4/525 Primary

  of mixed oxides or hydroxides containing iron, cobalt or nickel for inserting or intercalating light metals, e.g. LiNiO2, LiCoO2 or LiCoOxFy · CPC title

• H01M4/505

  of mixed oxides or hydroxides containing manganese for inserting or intercalating light metals, e.g. LiMn2O4 or LiMn2OxFy · CPC title

• H01M10/0525

  Rocking-chair batteries, i.e. batteries with lithium insertion or intercalation in both electrodes; Lithium-ion batteries · CPC title