Iminodiacetate chelating resin and manufacturing method therefor

Patent metadata

Field	Value
Publication number	US-10577480-B2
Application number	US-201715839111-A
Country	US
Kind code	B2
Filing date	Dec 12, 2017
Priority date	Jun 22, 2015
Publication date	Mar 3, 2020
Grant date	Mar 3, 2020

Abstract

The present invention relates to an iminodiacetic acid chelating resin, wherein the water amount in the resin is from 50 to 75% and the volume ratio of Na form/H form is from 1.4 to 1.8. Furthermore, the present invention relates to a method for producing an iminodiacetic acid chelating resin, wherein an alcohol is used as a solvent for the amination reaction of a chloromethylated styrene crosslinked copolymer with iminodiacetonitrile or sodium iodide and/or potassium iodide is used as a catalyst for the amination reaction.

First claim

The invention claimed is:

1. An iminodiacetic acid chelating resin, wherein a water amount in the resin is from 50 to 75% and a volume ratio of Na form/H form is from 1.4 to 1.8, and
wherein infrared absorption spectrum obtained by infrared absorption analysis has a downwardly convex peak in the range of 2,100 to 2,300 cm −1 .

2. The iminodiacetic acid chelating resin according to claim 1 , wherein a degree of porosity of the iminodiacetic acid chelating resin is from 60 to 90%.

3. The iminodiacetic acid chelating resin according to claim 1 , wherein a degree of crosslinking of the iminodiacetic acid chelating resin is from 4 to 7%.

4. A method for producing the iminodiacetic acid chelating resin of claim 1 , the method comprising:
aminating a chloromethylated styrene crosslinked copolymer with iminodiacetonitrile, to obtain an aminated styrene crosslinked copolymer; and
hydrolyzing the aminated styrene crosslinked copolymer,
wherein an alcohol is used as a solvent for aminating the chloromethylated styrene crosslinked copolymer.

5. The method according to claim 4 , wherein sodium iodide and/or potassium iodide is used as a catalyst for aminating the chloromethylated styrene crosslinked copolymer.

6. A method for producing the iminodiacetic acid chelating resin according to claim 1 , the method comprising:
aminating a chloromethylated styrene crosslinked copolymer with iminodiacetonitrile, to obtain an aminated styrene crosslinked copolymer; and
hydrolyzing the aminated styrene crosslinked copolymer,
wherein sodium iodide and/or potassium iodide is used as a catalyst for aminating the chloromethylated styrene crosslinked copolymer.

7. The method according to claim 5 , wherein the catalyst is used in an amount from 0.1 to 30 parts by weight per 100 parts by weight (on dry resin basis) of the chloromethylated styrene crosslinked copolymer.

8. The method according to claim 4 , wherein the iminodiacetonitrile is used in an amount from 40 to 200 parts by weight per 100 parts by weight (on dry resin basis) of the chloromethylated styrene crosslinked copolymer.

9. The method according to claim 4 , wherein a reaction temperature for aminating the chloromethylated styrene crosslinked copolymer is from 40 to 120° C. and a reaction time for aminating the chloromethylated styrene crosslinked copolymer is from 0.5 to 15 hours.

10. The method according to claim 4 , wherein a boiling point of the solvent for aminating the chloromethylated styrene crosslinked copolymer is from 30 to 180° C. and the solvent is used in an amount from 100 to 3,000 parts by weight per 100 parts by weight (on dry resin basis) of the chloromethylated styrene crosslinked copolymer.

11. The method according to claim 4 , wherein an aliphatic alcohol containing branched chain and having a carbon number of 3 to 4 is used as the solvent for aminating the chloromethylated styrene crosslinked copolymer.

12. The method according to claim 4 , wherein the hydrolyzing of the aminated styrene crosslinked copolymer is performed in the presence of at least one aqueous alkali solution selected from the group consisting of an aqueous sodium hydroxide solution, an aqueous potassium hydroxide solution, and an aqueous calcium hydroxide solution, or at least one strong acid selected from the group consisting of sulfuric acid, hydrochloric acid, and nitric acid.

13. The iminodiacetic acid chelating resin according to claim 1 , wherein a degree of crosslinking of the iminodiacetic acid chelating resin is from 4 to 6%.

Assignees

• Mitsubishi Chem Corp

Inventors

• Tsuhara Ryosuke
• Hashiguchi Masahiko
• Kubota Hirohisa

Classifications

• C08K5/175 Primary

  containing COOH-groups; Esters or salts thereof · CPC title

• C07C229/24

  having more than one carboxyl group bound to the carbon skeleton, e.g. aspartic acid · CPC title

• C08J7/14

  with acids, their salts or anhydrides · CPC title

• C08F8/24

  Haloalkylation · CPC title

• C08G69/26

  derived from polyamines and polycarboxylic acids · CPC title