Magnetic tape and method of manufacturing the same

Patent metadata

Field	Value
Publication number	US-10573341-B2
Application number	US-201615388911-A
Country	US
Kind code	B2
Filing date	Dec 22, 2016
Priority date	Dec 25, 2015
Publication date	Feb 25, 2020
Grant date	Feb 25, 2020

Abstract

The magnetic tape has a nonmagnetic layer containing nonmagnetic powder and binder on a nonmagnetic support and a magnetic layer containing ferromagnetic powder and binder on the nonmagnetic layer, wherein a fatty acid ester is contained in at least the magnetic layer, the ferromagnetic powder is ferromagnetic hexagonal ferrite powder, the ferromagnetic hexagonal ferrite powder has a crystallite volume as determined by X-ray diffraction analysis ranges from 1,000 nm3 to 2,400 nm3, and a ratio of the crystallite size Dx(107) obtained from a diffraction peak of a (107) plane to a particle size in a direction of an easy axis of magnetization DTEM as determined by observation with a transmission electron microscope, Dx(107)/DTEM, is greater than or equal to 1.1, and ΔSFD in a longitudinal direction of the magnetic tape as calculated with Equation 1: ΔSFD=SFD25° C.−SFD−190° C., ranges from 0.50 to 1.60.

First claim

What is claimed is:

1. A magnetic tape,
which comprises a nonmagnetic layer comprising nonmagnetic powder and binder on a nonmagnetic support and a magnetic layer comprising ferromagnetic powder and binder on the nonmagnetic layer, wherein
a fatty acid ester is contained in at least the magnetic layer;
the ferromagnetic powder is ferromagnetic hexagonal ferrite powder;
the ferromagnetic hexagonal ferrite powder has a crystallite volume as determined by X-ray diffraction analysis ranges from 1,000 nm 3 to 2,400 nm 3 , and a ratio of a crystallite size D x(107) obtained from a diffraction peak of a (107) plane to a particle size in a direction of an easy axis of magnetization D TEM as determined by observation with a transmission electron microscope, D x(107 /D TEM , is greater than or equal to 1.1; and
ΔSFD in a longitudinal direction of the magnetic tape as calculated with Equation 1 ranges from 0.50 to 1.60:
Equation 1
Δ SFD=SFD 25° C. −SFD −190° C.

wherein, in Equation 1, SFD 25° C. denotes a switching field distribution SFD as measured in the longitudinal direction of the magnetic tape in an environment with a temperature of 25° C., and SFD −190° C. denotes a switching field distribution SFD as measured in the longitudinal direction of the magnetic tape in an environment with a temperature of −190° C.

2. The magnetic tape according to claim 1 ,
wherein the D x(107) /D TEM of the ferromagnetic hexagonal ferrite powder falls within a range of 1.1 to 1.5.

3. The magnetic tape according to claim 1 ,
wherein the crystallite volume as determined by X-ray diffraction of the ferromagnetic hexagonal ferrite powder falls within a range of 1,000 nm 3 to 1,500 nm 3 .

4. The magnetic tape according to claim 2 ,
wherein the crystallite volume as determined by X-ray diffraction of the ferromagnetic hexagonal ferrite powder falls within a range of 1,000 nm 3 to 1,500 nm 3 .

5. The magnetic tape according to claim 1 ,
wherein the ΔSFD falls within a range of 0.50 to 1.00.

6. The magnetic tape according to claim 2 ,
wherein. the ΔSFD falls within a range of 0.50 to 1.00.

7. The magnetic tape according to claim 3 ,
wherein the ΔSFD falls within a range of 0.50 to 1.00.

8. The magnetic tape according to claim 4 ,
wherein the ΔSFD falls within a range of 0.50 to 1.00.

9. A method of manufacturing a magnetic tape,
wherein the magnetic tape is a magnetic tape which comprises a nonmagnetic layer comprising nonmagnetic powder and binder on a nonmagnetic support and a magnetic layer comprising ferromagnetic powder and binder on the nonmagnetic layer, wherein
a fatty acid ester is contained in at least the magnetic layer;
the ferromagnetic powder is ferromagnetic hexagonal ferrite powder;
the ferromagnetic hexagonal ferrite powder has a crystallite volume as determined by X-ray diffraction analysis ranges from 1,000 nm 3 to 2,400 nm 3 , and a ratio of a crystallite size D x(107) obtained from a diffraction peak. of a (107) plane to a particle size in a direction of an easy axis of magnetization D TEM as determined by observation with a transmission electron microscope, D x(107) /D TEM , is greater than or equal to 1.1; and
ΔSFD in a longitudinal direction of the magnetic tape as calculated with Equation 1 ranges from 0.50 to 1.60:
Equation 1
Δ SFD=SFD 25° C. −SFD 190° C.

wherein, in Equation 1, SFD 25° C. denotes a switching field distribution SFD as measured in the longitudinal direction of the magnetic tape in an environment with a temperature of 25° C., and SFD −190° C. denotes a switching field distribution SFD as measured in the longitudinal direction of the magnetic tape in an environment with a temperature of −190° C.; and
wherein the method comprises forming a magnetic layer through preparation of a magnetic, layer-forming composition and coating of the magnetic layer-forming composition that has been prepared on a nonmagnetic layer that has been formed on a nonmagnetic support,
wherein the preparation of the magnetic layer-forming composition comprises:
a first stage of dispersing ferromagnetic hexagonal ferrite powder, binder, and solvent in the presence of first dispersion beads to obtain a dispersion, and
a second stage of dispersing the dispersion obtained in the first stage in the presence of second dispersion beads of smaller bead diameter and lower density than the first dispersion beads.

10. The method of manufacturing a magnetic tape according to claim 9 ,
wherein the second stage is conducted in the presence of a quantity of second dispersion beads that is greater than or equal to 10-fold the quantity of ferromagnetic hexagonal ferrite powder based on weight.

11. The method of manufacturing a magnetic tape according to claim 9 ,
wherein the bead diameter of the second dispersion beads is less than or equal to 1/100 the bead diameter of the first dispersion beads.

12. The method of manufacturing a magnetic tape according to claim 9 ,
wherein the bead diameter of the second dispersion beads falls within a range of 80 nm to 1,000 nm.

13. The method of manufacturing a magnetic tape according to claim 9 ,
wherein the density of the second dispersion beads is less than or equal to 3.7 g/cm 3 .

14. The method of manufacturing a magnetic tape according to claim 9 ,
wherein the second dispersion beads are diamond beads.

15. The method of manufacturing a magnetic tape according to claim 9 ,
wherein the first stage obtains a liquid dispersion by dispersion processing solvent, binder, and ferromagnetic hexagonal ferrite powder having a ΔSFD powder as calculated by Equation 2 that falls within a range of 0.05 to 1.90:
Equation 2
Δ SFD powder =SFD powder100° C. −SFD powder25° C.

in the presence of first dispersion beads, wherein, in Equation 2, SFD powder100° C. denotes a switching field distribution SFD of the ferromagnetic hexagonal ferrite powder as measured in an environment with a temperature of 100° C., and SFD powder25° C. denotes a switching field distribution SFD of the, ferromagnetic hexagonal ferrite powder as measured in an environment with a temperature of 25° C.

16. The method of manufacturing a magnetic tape according to claim 9 ,
wherein the D x(107) /D TEM of the ferromagnetic hexagonal ferrite powder contained in the magnetic layer of the magnetic tape falls within a range of 1/1 to 1.5.

17. The method of manufacturing a magnetic tape according to claim 9 ,
wherein the crystallite volume as determined by X-ray diffraction of the ferromagnetic hexagonal ferrite powder contained in the magnetic layer of the magnetic tape falls within a range of 1,000 nm 3 to 1,500 nm 3 .

Assignees

• Fujifilm Corp

Inventors

• Tada Toshio
• Kasada Norihito
• Oyanagi Masahito

Classifications

• G11B5/845

  in a magnetic field · CPC title

• G11B5/78

  Tape carriers · CPC title

• G11B5/70678

  Ferrites · CPC title

• G11B5/714 Primary

  characterised by the dimension of the magnetic particles · CPC title

• G11B5/712

  characterised by the surface treatment or coating of magnetic particles · CPC title