High Al-content vibration-damping ferritic stainless steel material, and production method

Patent metadata

Field	Value
Publication number	US-10570979-B2
Application number	US-201615751917-A
Country	US
Kind code	B2
Filing date	Aug 10, 2016
Priority date	Aug 17, 2015
Publication date	Feb 25, 2020
Grant date	Feb 25, 2020

Abstract

A ferritic stainless steel material excellent in vibration damping capability has a composition containing, by mass %, from 0.001 to 0.04% of C, from 0.1 to 2.0% of Si, from 0.1 to 1.0% of Mn, from 0.01 to 0.6% of Ni, from 10.5 to 20.0% of Cr, from 0.5 to 5.0% of Al, from 0.001 to 0.03% of N, from 0 to 0.8% of Nb, from 0 to 0.5% of Ti, from 0 to 0.3% of Cu, from 0 to 0.3% of Mo, from 0 to 0.3% of V, from 0 to 0.3% of Zr, from 0 to 0.6% of Co, from 0 to 0.1% of REM, from 0 to 0.1% of Ca, the balance of Fe and unavoidable impurities, and has ferrite single phase matrix with crystal grains of average crystal grain diameter of from 0.3 to 3.0 mm and a residual magnetic flux density of 45 mT or less.

First claim

The invention claimed is:

1. A vibration-damping ferritic stainless steel material having a chemical composition containing, in terms of percentage by mass, from 0.001 to 0.04% of C, from 0.1 to 2.0% of Si, from 0.1 to 1.0% of Mn, from 0.01 to 0.6% of Ni, from 10.5 to 20.0% of Cr, from 0.5 to 5.0% of Al, from 0.001 to 0.03% of N, from 0 to 0.8% of Nb, from 0 to 0.5% of Ti, from 0 to 0.3% of Cu, from 0 to 0.3% of Mo, from 0 to 0.3% of V, from 0 to 0.3% of Zr, from 0 to 0.6% of Co, from 0 to 0.1% of REM (rare earth element), from 0 to 0.1% of Ca, and the balance of Fe, with unavoidable impurities, having a metal structure containing a ferrite single phase as a matrix and ferrite crystal grains having an average crystal grain diameter of from 0.3 to 3.0 mm, and having a residual magnetic flux density of 45 mT or less.

2. A production method for a vibration-damping ferritic stainless steel material, comprising subjecting a steel material having a chemical composition containing, in terms of percentage by mass, from 0.001 to 0.04% of C, from 0.1 to 2.0% of Si, from 0.1 to 1.0% of Mn, from 0.01 to 0.6% of Ni, from 10.5 to 20.0% of Cr, from 0.5 to 5.0% of Al, from 0.001 to 0.03% of N, from 0 to 0.8% of Nb, from 0 to 0.5% of Ti, from 0 to 0.3% of Cu, from 0 to 0.3% of Mo, from 0 to 0.3% of V, from 0 to 0.3% of Zr, from 0 to 0.6% of Co, from 0 to 0.1% of REM (rare earth element), from 0 to 0.1% of Ca, and the balance of Fe, with unavoidable impurities, to final annealing in a non-oxidative atmosphere under a condition of retaining the steel material in a temperature range of from 900 to 1,250° C. for 10 minutes or more, so as to make an average crystal grain diameter of ferrite crystal grains of from 0.3 to 3.0 mm.

3. The production method for a vibration-damping ferritic stainless steel material according to claim 2 , wherein the final annealing is performed in an air atmosphere instead of the non-oxidative atmosphere, and acid cleaning is performed after the final annealing.

4. The production method for a vibration-damping ferritic stainless steel material according to claim 2 or 3 , wherein the steel material subjected to the final annealing is a steel material obtained by working a steel sheet material.

Assignees

• Nisshin Steel Co Ltd
• Nippon Steel Nisshin Co Ltd

Inventors

• Hori Yoshiaki
• Imakawa Kazunari
• Suzuki Satoshi

Classifications

• C22C38/04

  containing manganese · CPC title

• C22C38/40 Primary

  with nickel · CPC title

• C22C38/02

  containing silicon · CPC title

• C21D2211/005

  Ferrite · CPC title

• C22C38/44

  with molybdenum or tungsten · CPC title