Cermet, and method for manufacturing same, as well as cutting tool

Patent metadata

Field	Value
Publication number	US-10570486-B2
Application number	US-201414899097-A
Country	US
Kind code	B2
Filing date	Jun 19, 2014
Priority date	Jun 28, 2013
Publication date	Feb 25, 2020
Grant date	Feb 25, 2020

Abstract

A cermet ( 1 ) includes a bonding phase ( 2 ) and a hard phase ( 4 ). The hard phase ( 4 ) includes: a first hard phase ( 5 ) composed of TiCN; and a second hard phase ( 6 ) composed of a composite carbonitride of Ti, which is greater than the average particle diameter of the first hard phase ( 5 ). The cermet ( 1 ) further includes an aggregate part ( 10 ) formed by interlinking parts of the second hard phase ( 6 ). The second hard phase ( 6 ) forming the aggregate part ( 10 ) includes a 2a-th hard phase ( 7 ) having a maximum W content of an inner part thereof that is more than 1.1 times as great as an average W content of an outer circumferential part thereof, in terms of mass ratio. The aggregate part ( 10 ) composes a proportion of from 20% to 60% of the cermet ( 1 ) in terms of surface area.

First claim

The invention claimed is:

1. A cermet comprising:
a bonding phase comprising at least one of Co and Ni as a main component;
first hard particles composed of TiCN having a first average particle diameter of from 0.05 μm to 1 μm;
second hard particles having a second average particle diameter of from 0.2 μm to 2 μm which is greater than the first average particle diameter, and composed of a composite carbonitride of Ti, W and at least one metal other than Ti and W selected from among group IV, group V, and group VI metals of the periodic table; an
an interlinked region consisting of the second hard particles that are interlinked,
the interlinked region having a maximum length that is at least three times as great as the second average particle diameter,

wherein
the second hard particles comprise a 2a-th hard particles having a 2a-th W content of an inner part thereof that is more than 1.1 times as great as an 2a-th average W content of an outer circumferential part thereof,
the interlinked region composes a proportion of from 20 area % to 60 area % of the cermet, and
a carbon content of the cermet is from 6.00% to 6.50% in terms of mass of the cermet.

2. The cermet according to claim 1 , wherein
the second hard particles comprises a 2b-th hard particles having a 2b-th W content of an inner part thereof that is equal to or less than 1.1 times as great as an 2b-th average W content of an outer circumferential part thereof.

3. The cermet according to claim 1 , further comprising third hard particles formed of:
a core part that is composed of TiCN; and
an outer circumferential part that surrounds the core part, and that is composed of a composite carbonitride of Ti and at least one metal other than Ti selected from among group IV, group V, and group VI metals of the periodic table.

4. The cermet according to claim 1 , wherein
residual stress on the TiCN is from −500 MPa to −1200 MPa, residual stress on the composite carbonitride is from −1000 MPa to −1500 MPa, and residual stress on the bonding phase is from −400 MPa to −800 MPa.

5. The cermet according to claim 1 , wherein
the first hard particles have a surface area proportion ranging from 20 area % to 38 area % of the cermet.

6. A cutting tool comprising:
the cermet according to claim 1 ; and
a layer on the cermet.

Assignees

• Kyocera Corp

Inventors

• Kinoshita Hideyoshi

Classifications

• B22F2005/001

  Cutting tools, earth boring or grinding tool other than table ware · CPC title

• C22C29/04 Primary

  based on carbonitrides · CPC title

• C04B2235/3839

  Refractory metal carbides · CPC title

• B23B2222/16

  Cermet · CPC title

• C04B2235/6562

  Heating rate · CPC title