Glossy container

Patent metadata

Field	Value
Publication number	US-10556371-B2
Application number	US-201615191767-A
Country	US
Kind code	B2
Filing date	Jun 24, 2016
Priority date	Jun 26, 2015
Publication date	Feb 11, 2020
Grant date	Feb 11, 2020

Abstract

A method of blow molding a glossy article having at least one layer of thermoplastic material. The method comprises the steps of feeding a parison of said thermoplastic material into a mold having an inner surface with at least a portion of SPI finish standard selected from the group consisting of A-1, A-2, A-3, B-1, B-2 and B-3 mold and a first temperature of greater than 55° C.; blowing the parison against the inner surface of the mold to form the article; and subsequently lowering the temperature of the mold to a second temperature of between 10° C. to 55° C. before release of the molded article. The cycle time of the mold (tct) is less than 250 seconds.

First claim

What is claimed is:

1. A method of blow molding a glossy article, the method comprising the steps of:
providing a parison comprising an outer layer of thermoplastic material and an inner layer of thermoplastic material, wherein the inner layer has a lower melt flow index than the outer layer;
heating a mold to a first temperature of greater about 55° C., wherein the mold has an inner surface with at least a portion of SPI finish standard selected from the group consisting of A-1, A-2, A-3, B-1, B-2 and B-3 mold, wherein the first temperature is greater than about 5° C. above a heat distortion temperature of the outer layer of the thermoplastic material and the inner layer of thermoplastic material;
feeding the parison into the heated mold;
blowing the parison against the inner surface of the heated mold to form the article;
subsequently lowering the temperature of the mold to a second temperature of between about 10° C. to about 55° C. while an outer surface of the article touches the inner surface of the mold, wherein the second temperature is less than about 5° C. below the heat distortion temperature of the outer layer and the inner layer, and
wherein the cycle time (t ct ) of the mold is less than 250 seconds.

2. The method of blow molding a glossy article as claimed in claim 1 , wherein the first temperature is less than 200° C.

3. The method of blow molding a glossy article as claimed in claim 1 , wherein the first temperature is between 70° C. and 100° C.

4. The method of blow molding a glossy article as claimed in claim 1 , wherein the thermoplastic material of the inner layer and the outer layer is selected from the group consisting of polyethylene (PE), polypropylene (PP), polyethylene terephthalate glycol (PETG), polystyrene (PS), polycarbonate (PC), polyvinyl chloride (PVC), polyvinyl dichloride (PVDC), polyethylene naphthalate (PEN), polycyclohexylenedimethylene terephthalate (PCT), glycol-modified PCT copolymer (PCTG), copolyester of cyclohexanedimethanol and terephthalic acid (PCTA), polybutylene terephthalate (PBT), acrylonitrile styrene (AS), styrene butadiene copolymer (SBC), polyhydroxyalkanoates (PHA), polycaprolactone (PLC), polycyanoacrylate (PACA), polyhydroxybutyrate (PHB), copolymer of 1,3-propanediol and p-Phthalic acid, ethylene vinyl alcohol copolymer (EVOH), polymethyl methacrylate (PMMA), extrudable PET, ethylene/vinyl acetate (EVA), ethylene/acrylic acid (EAA), ethylene/methyl acrylate (EMA), ethylene/ethyl acrylate (EEA), ethylene acrylic acid ionomers, cyclic olefin copolymers (COC), polyethylene terephthalate (PET), amorphous PET, polyamides and a combination thereof.

5. The method of blow molding a glossy article as claimed in claim 1 , comprising mixing an additive with the thermoplastic material of at least one of the inner layer and the outer layer prior to forming the parison, wherein the additive is selected from the group consisting of an alcohol, oil, siloxane fluid, water, a slip agent, and a combination thereof.

6. The method of blow molding a glossy article as claimed in claim 1 , comprising mixing an adjunct ingredient with the thermoplastic material of at least one of the inner layer and the outer layer prior to forming the parison, wherein at least some of the adjunct ingredient is a pearlescent agent having a particle size of up to 300 μm.

7. The method of blow molding a glossy article as claimed in claim 1 , wherein the step of heating the mold to the first temperature comprises using heat induction of electromagnetic response or coils embedded within the mold surface.

8. The method of blow molding a glossy article as claimed in claim 1 , further comprising heating the mold to the first temperature, wherein a heating bar is temporarily located within the mold prior to introduction of the parison, and the method further comprises heating the bar via electromagnetic induction.

9. The method of blow molding a glossy article as claimed in claim 1 , wherein the step of cooling the mold to the second temperature by circulating cooling water within the mold.

10. The method of blow molding a glossy article as claimed in claim 1 , wherein the time taken to cool the mold (t c ) is less than 175 seconds.

11. The method of blow molding a glossy article as claimed in claim 1 , wherein at least 50% of the inner surface of the mold has a SPI finish standard of A-1.

12. The method of blow molding a glossy article as claimed in claim 1 , wherein the thermoplastic material of at least one of the inner layer and the outer layer is PE and the method of blow molding is extrusion blow molding.

Assignees

• Procter & Gamble

Inventors

• Culeron Guy Hubert Stephane Sylvain
• Song Shuo
• Wang Ping
• Yang Liang
• Liang Chun-Chuan

Classifications

• B29K2995/0022

  Bright, glossy or shiny surface · CPC title

• B29C2049/4838

  for heating moulds or mould parts · CPC title

• B29B7/002

  Methods (chemical aspects C08J3/00) · CPC title

• B29B7/94

  Liquid charges · CPC title

• B29C49/786

  Temperature · CPC title