Masterbatches for preparing a composite material based on semi-crystalline polymer with enhanced conductivity properties, process and composite materials produced therefrom

Patent metadata

Field	Value
Publication number	US-10550231-B2
Application number	US-201615557497-A
Country	US
Kind code	B2
Filing date	Mar 11, 2016
Priority date	Mar 12, 2015
Publication date	Feb 4, 2020
Grant date	Feb 4, 2020

Abstract

The present invention relates to a masterbatch for use in a process of preparing a composite material comprising a blend of a first semi-crystalline polymer with at least 5 wt % carbon nanotubes. Good dispersion of the carbon nanotube is obtained within the masterbatch and evidenced by the blending of the masterbatch with a second semi-crystalline polymer miscible with the first one in respective proportions to obtain a composite material containing about 1 wt % of carbon nanotubes wherein said composite material yields an agglomerate area fraction U % lower than 2 and a surface resistivity lower than 105 ohm/sq.

First claim

What is claimed:

1. A composite material, the composite material comprising a blend of:
a masterbatch comprising a blend of a first semi-crystalline polymer having a melting temperature Tm1 as measured according to ISO11357-3, with carbon nanotubes, wherein the carbon nanotubes content being of at least 5 wt % of carbon nanotubes based on the total weight of the masterbatch as determined according to ISO11358, the masterbatch having a high load melt index HLMI ranging from 100 g/10 min to 1000 g/10 min as determined according to ISO1133 under a load of 21.6 kg;
characterised in that the first semi-crystalline polymer is selected from syndiotactic polypropylene and isotactic polypropylene; and
a second semi-crystalline polymer, wherein the carbon nanotubes are from 0.9 wt % to 1.1 wt, of the total weight of the composite material as determined according to ISO11358, wherein the second semi-crystalline polymer is selected to be miscible with the first semicrystalline polymer, to have a melting temperature Tm2 ranging from Tm1−5° C. to Tm1+5° C. and to have a melt flow index of not more than 20 g/10 min as determined under a load of 2.16 kg according to ISO1133, and the composite material has:
an agglomerate area fraction U % lower than 2%, as determined in accordance with ASTM D-2663-14,
a surface resistivity lower than 10 5 ohm/sq, as determined according to CEI60167.

2. A a composite material, composite material comprising a blend of:
a masterbatch comprising a blend of a first semi-crystalline polymer having a melting temperature Tm1 as measured according to ISO11357-3, with carbon nanotubes, wherein the carbon nanotubes content being of at least 5 wt % of carbon nanotubes based on the total weight of the masterbatch as determined according to ISO11358, the masterbatch having a high load melt index HLMI ranging from 2 g/10 min to 1000 g/10 min as determined according to ISO1133 under a load of 21.6 kg;
characterised in that the first semi-crystalline polymer is polyethylene; and
a second semi-crystalline polymer wherein the carbon nanotubes are from 0.9 wt. % to 1.1 wt % with respect to the total weight of the composite material as determined according to ISO11358, wherein the second semi-crystalline polymer is selected to be miscible with the first semicrystalline polymer, to have a melting temperature Tm2 ranging from Tm1−5° C. to Tm1+5° C. and to have a melt flow index of not more than 20 g/10 min as determined under a load of 2.16 kg according to ISO1133 and the composite material has:
an agglomerate area fraction U % lower than 2%, as determined in accordance with ASTM D-2663-14,
a surface resistivity lower than 10 5 ohm/sq, as determined according to CEI60167.

3. The masterbatch according to claim 2 characterized in that the HLMI of the masterbatch ranges from 10 to 100 g/10 min as determined according to ISO1133 under a load of 21.6 kg at a temperature of 190° C.

4. The masterbatch according to claim 2 , characterised in that the first semi-crystalline polymer has a melt flow index ranging from 5 to 250 g/10 min as measured according to ISO 1133 under a load of 2.16 kg.

5. The masterbatch according to claim 2 , characterised in that the masterbatch comprises from 0.01 to 4.0 wt % of one or more additives based on the total weight of the masterbatch, the one or more additives being selected from waxes, tristearin, zinc stearate, calcium stearate, magnesium stearate, erucyl amide, oleic acid amide, ethylene-acrylic acid copolymer, ethylene vinyl acetate copolymer and cetyl trimethyl ammonium bromide.

Assignees

• Total Res & Technology Feluy

Inventors

• Rousseaux Dimitri
• Lhost Olivier
• Lodefier Philippe
• Scandino Eddi

Classifications

• C08K7/24

  inorganic · CPC title

• C08J2423/10

  Homopolymers or copolymers of propene · CPC title

• C08J3/203

  Solid polymers with solid and/or liquid additives · CPC title

• C08J2323/10

  Homopolymers or copolymers of propene · CPC title

• C08J2323/04

  Homopolymers or copolymers of ethene · CPC title