Photoluminescent pigment; cosmetic, paint composition, and resin composition containing same; and bright pigment production method

Patent metadata

Field	Value
Publication number	US-10544309-B2
Application number	US-201214363695-A
Country	US
Kind code	B2
Filing date	Dec 7, 2012
Priority date	Dec 9, 2011
Publication date	Jan 28, 2020
Grant date	Jan 28, 2020

Abstract

A bright pigment of the present invention is a bright pigment including flaky particles and a metal oxide layer covering each surface of the flaky particles. The metal oxide layer has a thickness variation coefficient (standard deviation of thickness of the metal oxide layer/average thickness of the metal oxide layer) of 20% or less. The bright pigment preferably contains a sodium component, and the sodium component is Na 2 O. The content of Na 2 O in the flaky particles is 3% by mass or more and less than 9.5% by mass. The bright pigment preferably has a specific surface area of 5.0 m 2 /g or less.

First claim

The invention claimed is:

1. A bright pigment comprising a flaky glass particle and a metal oxide layer covering a surface of the flaky glass particle,
wherein the flaky glass particle contains Na 2 O in an amount of 7% by mass or more and less than 9% by mass,
the metal oxide layer consists essentially of at least one selected from the group consisting of titanium dioxide (TiO 2 ) and reduced titanium dioxide (TiO 2-x ) obtained by reducing titanium dioxide,
a crystal phase of the metal oxide layer contains sodium ions, and
the metal oxide layer has a thickness variation coefficient of 20% or less, wherein the thickness variation coefficient is a standard deviation of thickness of the metal oxide layer divided by an average thickness of the metal oxide layer.

2. The bright pigment according to claim 1 , wherein the bright pigment has a specific surface area of 5.0 m 2 /g or less.

3. The bright pigment according to claim 1 , wherein the bright pigment has a particle diameter of 10 to 300 μm, which is a 50% volume-cumulative particle diameter from a small particle diameter side in a particle size distribution.

4. The bright pigment according to claim 1 , wherein the metal oxide layer comprises titanium dioxide and the sodium ions.

5. Cosmetics comprising the bright pigment according to claim 1 .

6. A paint composition comprising the bright pigment according to claim 1 .

7. A resin composition comprising the bright pigment according to claim 1 .

8. A method for producing a bright pigment according to claim 1 , the method comprising:
adding an aqueous solution of a metal compound to a slurry for forming a metal oxide layer containing the flaky glass particle and acid to deposit a hydrate of an oxide of a metal derived from the metal compound on the surface of the flaky glass particle, thereby covering the flaky glass particle with a metal oxide hydrate layer containing the hydrate of the oxide of the metal; and
of washing and drying the flaky glass particle covered with the metal oxide hydrate layer, and baking the resultant flaky glass particle covered with the metal oxide hydrate layer to form the metal oxide hydrate layer into a metal oxide layer,
wherein the flaky glass particle to be used for preparing the slurry for forming a metal oxide layer has a zeta potential of −25 mV to −10 mV in hydrochloric acid aqueous solution of pH 2,
the flaky glass particle covered with the metal oxide layer contains Na 2 O in an amount of 7% by mass or more and less than 9% by mass,
the metal oxide layer consists essentially of at least one selected from the group consisting of titanium dioxide (TiO 2 ) and reduced titanium dioxide (TiO 2-x ) obtained by reducing titanium dioxide,
a crystal phase of the metal oxide layer contains sodium ions, and
the metal oxide layer has a thickness variation coefficient of 20% or less, wherein the thickness variation coefficient is a standard deviation of thickness of the metal oxide layer divided by an average thickness of the metal oxide layer.

9. The method for producing a bright pigment according to claim 8 , wherein the aqueous solution of the metal compound is a titanium-containing aqueous solution, and
the titanium-containing solution is an aqueous solution containing at least one kind selected from the group consisting of titanium tetrachloride, titanium trichloride, titanium dichloride, titanium sulfate, titanyl sulfate, titanium nitrate, and titanyl nitrate.

10. The method for producing a bright pigment according to claim 8 , wherein a baking temperature is 600° C. or less in the baking the resultant flaky glass particle.

Assignees

• Nippon Sheet Glass Co Ltd

Inventors

• Kitamura Takeaki

Classifications

• C09C1/0021

  comprising a core coated with only one layer having a high or low refractive index · CPC title

• C01P2004/61

  Micrometer sized, i.e. from 1-100 micrometer · CPC title

• C01P2004/20

  extending in two dimensions, e.g. plate-like · CPC title

• C09C1/407

  Aluminium oxides or hydroxides · CPC title

• Y10T428/258

  Alkali metal or alkaline earth metal or compound thereof · CPC title