Composition for the production of polyimide film for flexible board of photoelectronic device

Patent metadata

Field	Value
Publication number	US-10544266-B2
Application number	US-201615126416-A
Country	US
Kind code	B2
Filing date	Mar 7, 2016
Priority date	Mar 5, 2015
Publication date	Jan 28, 2020
Grant date	Jan 28, 2020

Abstract

Disclosed is a polyimide precursor composition for the production of a flexible board of a photoelectronic device. The polyimide precursor composition includes a polyimide precursor derived from a diamine or acid dianhydride including a structure of Formula 1:

wherein R 1 to R 8 , m1, m2, and m3 are as defined in the specification. Also disclosed is a polyimide film produced from the polyimide precursor composition. The polyimide film is obtained by applying the precursor composition to a substrate and curing the composition. The polyimide film has high transparency and good heat resistance. In addition, the polyimide film exhibits good dimensional stability because the substrate does not undergo an increase in stress even during high-temperature heat treatment.

First claim

What is claimed is:

1. A polyimide film for a flexible board of a photoelectronic device comprising: a cured product of a polyimide precursor composition comprising:
a polyimide precursor derived from a diamine or acid dianhydride comprising a structure of Formula 1:

wherein R 1 and R 2 are each independently a single bond, a C 1 -C 5 alkylene group or a divalent aromatic group comprising six or more carbon atoms, R 3 and R 4 are each independently a C 1 -C 5 alkyl group, R 5 and R 6 are each independently a C 4 -C 10 aryl group, R 7 and R 8 are a C 1 -C 5 alkyl group or a C 2 -C 10 alkenyl group provided that at least one of R 7 and R 8 is a C 2 -C 10 alkenyl group, and m1, m2, and m3 are each independently an integer equal to or greater than 1; and
a solvent having a positive partition coefficient and comprising a first solvent and a second solvent, wherein the first solvent is an amine based solvent and the second solvent is a non-amine-based solvent, and
wherein the film has a modulus of 4 GPa or less, a tensile stress of 150 MPa or less, and a coefficient of thermal expansion (CTE) of 30 ppm to 200 ppm at 100 to 250° C., and
wherein the film has an average transmittance of at least 80% to light at a wavelength of 350 nm to 760 nm.

2. The polyimide film according to claim 1 , wherein the polyimide precursor composition comprises 50% by weight or less of the diamine- or acid dianhydride-derived polyimide precursor, based on the total weight of the composition.

3. The polyimide film according to claim 1 , wherein the diamine- or acid dianhydride-derived polyimide precursor has a molecular weight of 600 to 7,000.

4. The polyimide film according to claim 1 , wherein m1, m2, and m3 in Formula 1 are each independently an integer from 1 to 10.

5. The polyimide film according to claim 1 , wherein the amine-based solvent and the non-amine-based solvent are present in a volume ratio of 50-90:10-50.

6. The polyimide film according to claim 1 , wherein the amine-based solvent is a tertiary amine substituted with an alkyl group comprising two or more carbon atoms.

7. The polyimide film according to claim 1 , wherein the non-amine-based solvent is toluene or tetrahydrofuran.

8. The polyimide film according to claim 1 , further comprising silica-based particles.

9. The polyimide film for a flexible board of a photoelectronic device according to claim 1 , wherein the film is disposed on a glass substrate.

10. A photoelectronic device comprising the polyimide film according to claim 9 as a flexible board.

11. A flexible display comprising the polyimide film according to claim 9 as a flexible board.

12. A laminate comprising a glass substrate and a polyimide film formed on the glass substrate wherein the laminate is obtained by applying the film according to claim 1 to the glass substrate.

13. The laminate according to claim 12 , wherein the substrate of the laminate is stressed at 60 MPa or less after heat treatment at 100 to 350° C.

14. The polyimide film according to claim 1 , wherein the amine-based solvent has a positive partition coefficient.

15. The polyimide film according to claim 1 , wherein the amine-based solvent is selected from N,N-diethylacetamide, N,N-diethylformamide, N-ethylpyrrolidone, and mixtures thereof.

Assignees

• Lg Chemical Ltd

Inventors

• Yun Cheolmin
• Jeong Hye Won
• Shin Bora
• Kim Kyungjun

Classifications

• H10W70/695

  Organic materials · CPC title

• C08J2379/08

  Polyimides; Polyester-imides; Polyamide-imides; Polyamide acids or similar polyimide precursors · CPC title

• C09D179/08

  Polyimides; Polyester-imides; Polyamide-imides; Polyamide acids or similar polyimide precursors · CPC title

• B32B27/34

  comprising polyamides · CPC title

• B32B2457/20

  Displays, e.g. liquid crystal displays, plasma displays · CPC title