Electrode mixture layer composition for nonaqueous electrolyte secondary battery, manufacturing method thereof and use therefor

Patent metadata

Field	Value
Publication number	US-10541423-B2
Application number	US-201615561391-A
Country	US
Kind code	B2
Filing date	Mar 29, 2016
Priority date	Mar 30, 2015
Publication date	Jan 21, 2020
Grant date	Jan 21, 2020

Abstract

An electrode mixture layer composition for a nonaqueous electrolyte secondary battery contains an active material, water and a binder. The binder contains a crosslinked polymer of a monomer component including an ethylenically unsaturated carboxylic acid monomer, and a salt thereof. The crosslinked polymer is a polymer that is crosslinked with allyl methacrylate, and an amount of the allyl methacrylate used is 0.1 to 2.0 parts by weight relative to total 100 parts by weight of non-crosslinking monomers, and a content of the crosslinked polymer and salt thereof is 0.5% to 5.0% by weight of the active material.

First claim

The invention claimed is:

1. An electrode mixture layer composition for a nonaqueous electrolyte secondary battery, containing an active material, water and a binder, wherein
the binder contains a crosslinked polymer of a monomer component including an ethylenically unsaturated carboxylic acid monomer, or a salt of the crosslinked polymer,
the crosslinked polymer is a polymer that is crosslinked with allyl methacrylate, and an amount of the allyl methacrylate used is 0.1 to 2.0 parts by weight relative to total 100 parts by weight of non-crosslinking monomers,
a content of the crosslinked polymer or the salt thereof is 0.5% to 5.0% by weight of the active material, and
a ratio of the ethylenically unsaturated carboxylic acid monomer of a total amount of the non-crosslinking monomers is in a range of 50% to 100% by weight.

2. The electrode mixture layer composition for a nonaqueous electrolyte secondary battery according to claim 1 , wherein the crosslinked polymer is a polymer that is crosslinked with allyl methacrylate and a polyfunctional allyl compound, and an amount of the allyl methacrylate and polyfunctional allyl compound is 0.1 to 3.0 parts by weight relative to total 100 parts by weight of the non-crosslinking monomers.

3. The electrode mixture layer composition for a nonaqueous electrolyte secondary battery according to claim 1 , wherein a degree of neutralization of the crosslinked polymer is 20 to 100 mol %.

4. A method of manufacturing an electrode mixture layer composition for a nonaqueous electrolyte secondary battery, the method comprising:
precipitation-polymerizing a monomer component including an ethylenically unsaturated carboxylic acid monomer and allyl methacrylate in an aqueous medium to obtain a crosslinked polymer; and
mixing an active material, the crosslinked polymer or a salt of the crosslinked polymer in an amount of 0.5% to 5.0% by weight relative to the active material and water to thereby manufacture an electrode mixture layer composition for a nonaqueous electrolyte secondary battery,
wherein the monomer component contains the ethylenically unsaturated carboxylic acid monomer in a range of 50% to 100% by weight of non-crosslinking monomers which are included in the monomer component and the allyl methacrylate in an amount of 0.1 to 2.0 parts by weight relative to total 100 parts by weight of the non-crosslinking monomers.

5. A nonaqueous electrolyte secondary battery electrode comprising a mixture layer constituted of the electrode mixture layer composition for a nonaqueous electrolyte secondary battery according to claim 1 on a surface of a collector.

6. A nonaqueous electrolyte secondary battery comprising: the nonaqueous electrolyte secondary battery electrode according to claim 5 ; a separator; and a nonaqueous electrolyte solution.

7. The electrode mixture layer composition for a nonaqueous electrolyte secondary battery according to claim 2 , wherein a degree of neutralization of the crosslinked polymer is 20 to 100 mol %.

8. A nonaqueous electrolyte secondary battery electrode comprising a mixture layer constituted of the electrode mixture layer composition for a nonaqueous electrolyte secondary battery according to claim 2 on a surface of a collector.

9. A nonaqueous electrolyte secondary battery electrode comprising a mixture layer constituted of the electrode mixture layer composition for a nonaqueous electrolyte secondary battery according to claim 3 on a surface of a collector.

10. A nonaqueous electrolyte secondary battery electrode comprising a mixture layer constituted of the electrode mixture layer composition for a nonaqueous electrolyte secondary battery according to claim 7 on a surface of a collector.

11. A nonaqueous electrolyte secondary battery comprising: the nonaqueous electrolyte secondary battery electrode according to claim 8 ; a separator; and a nonaqueous electrolyte solution.

12. A nonaqueous electrolyte secondary battery comprising: the nonaqueous electrolyte secondary battery electrode according to claim 9 ; a separator; and a nonaqueous electrolyte solution.

13. A nonaqueous electrolyte secondary battery comprising: the nonaqueous electrolyte secondary battery electrode according to claim 10 ; a separator; and a nonaqueous electrolyte solution.

14. A binder for a nonaqueous electrolyte secondary battery comprising:
a crosslinked polymer of a monomer component including an ethylenically unsaturated carboxylic acid monomer or a salt of the crosslinked polymer, the crosslinked polymer being a polymer that is crosslinked with allyl methacrylate in an amount of 0.1 to 2.0 parts by weight relative to total 100 parts by weight of non-crosslinking monomers which are included in the monomer component, and a ratio of the ethylenically unsaturated carboxylic acid monomer to the total amount of non-crosslinking monomers being in a range of 50% to 100% by weight.

15. The binder according to claim 14 , wherein the range is 70% to 100% by weight.

Assignees

• Toagosei Co Ltd

Inventors

• Matsuzaki Hideo
• Saito Naohiko
• Matsunaga Morikatsu
• Kumagai Shinya

Classifications

• C08F2/14

  Organic medium · CPC title

• H01M4/622

  being polymers · CPC title

• H01M4/0404

  by coating on electrode collectors · CPC title

• C08F220/06 Primary

  Acrylic acid; Methacrylic acid; Metal salts or ammonium salts thereof · CPC title

• H01M4/139

  Processes of manufacture · CPC title