System and method for the production of gypsum board using starch pellets

Patent metadata

Field	Value
Publication number	US-10532955-B2
Application number	US-201715858622-A
Country	US
Kind code	B2
Filing date	Dec 29, 2017
Priority date	Sep 14, 2011
Publication date	Jan 14, 2020
Grant date	Jan 14, 2020

Abstract

The present invention relates to a system and method for the production of gypsum board using starch pellets. In accordance with the present disclosure, the starch necessary for board formation is provided in the form of starch pellets. These pellets are mixed with a gypsum slurry in a mixer. The pellets are initially insoluble and do not dissolve. However, during subsequent drying stages, the pellets become soluble and dissolve into the gypsum phase. This both provides the desired starch component and also results in the formation of voids within the set gypsum.

First claim

What is claimed is:

1. A method of producing lightweight gypsum board, the method utilizing a board production line including a mixer, a forming table, and dryers, the method comprising:
providing a plurality of starch pellets, the pellets being of a uniform size and being only slightly soluble at temperatures below approximately 140° F., the pellets being more soluble at elevated temperatures;
adding the pellets to a gypsum slurry in a pellet to gypsum ratio of between approximately 5/100 to 50/100 by volume;
blending the gypsum slurry and pellets within the mixer whereby the pellets become fully encapsulated within the slurry;
supplying a first facing sheet to the forming table prior to the mixer;
discharging the blended gypsum and pellets from the mixer and onto the first facing sheet;
supplying a top facing sheet over the blended gypsum and pellets to form a composite panel;
drying the composite panel within the dryers to a temperature in excess of approximately 140° F., the drying causing the pellets to dissolve and the residual moisture to be removed from the board, whereby the dissolved pellets provide starch to the gypsum slurry and create voids within the set gypsum.

2. The method as described in claim 1 comprising the further step of combining air and starch to form the starch pellets.

3. A method of producing building board, the method utilizing starch, stucco, and water, the method comprising:
combining the starch with air to form starch pellets, the pellets being slightly soluble at temperatures below approximately 140° F.;
mixing the starch pellets with the stucco and the water to form a slurry, with the mixing serving to fully encapsulate the pellets within the slurry;
dispensing the slurry between opposing sheets to form a composite panel;
drying the composite panel, the drying causing the pellets to dissolve and the slurry to set, whereby the dissolved pellets provide starch to the slurry and create voids within the set slurry.

4. The method as described in claim 3 wherein the pellet to stucco ratio is between 5/100 to 50/100 by volume.

5. The method as described in claim 3 wherein the pellets are formed via an extrusion or other foaming procedure.

6. The method as described in claim 3 wherein the pellets are hydrophobic at temperatures below approximately 140° F.

7. The method as described in claim 3 wherein the pellets are formed from an ethylated starch.

8. The method as described in claim 3 wherein the starch pellets are formed via a prilling process.

9. A method of producing a gypsum board having opposing sheets and a core with voids, the method comprising:
providing a volume of gypsum slurry;
providing an amount of starch;
mixing the starch with air and water;
drying the mixture to form a number of dry starch pellets;
adding the starch pellets to the gypsum slurry;
mixing the starch pellets with the slurry to fully encapsulate the pellets;
depositing the starch pellet and slurry mixture between the opposing sheets;
drying the slurry to dissolve the starch pellets and create the voids within the core, the dissolved starch pellets providing a concentration of starch within the gypsum board.

10. The method as described in claim 9 wherein the voids include a lining and wherein the concentration of the dissolved starch is higher at the void lining than in the core body, whereby the void lining is strengthened and the resulting board is likewise strengthened.

11. The method as described in claim 9 wherein the pellets have an approximate particle size that is greater than 800 microns.

12. The method as described in claim 9 wherein the pellets have an approximate particle size that is less than 400 microns.

13. The method as described in claim 9 wherein the dissolved starch pellets yield a uniform bubble structure within core, thereby strengthening the core.

14. The method as described in claim 9 wherein the pellets and stucco are combined at a ratio of between 5/100 to 50/100 by volume.

15. The method as described in claim 9 including the additional step of forming the pellets via an extrusion process.

16. The method as described in claim 9 wherein the pellets are hydrophobic at temperatures below approximately 140° F.

17. The method as described in claim 9 comprising the further step of forming the pellets from an ethylated starch.

18. The method as described in claim 3 wherein the voids include a lining and wherein the concentration of the dissolved starch is higher at the void lining than in the core body, whereby the void lining is strengthened and the resulting board is likewise strengthened.

Assignees

• Certainteed Gypsum Inc

Inventors

• College John W
• Libunao Shane
• Harris Mark

Classifications

• Y10T156/1712

  Indefinite or running length work · CPC title

• C04B2111/40

  Porous or lightweight materials · CPC title

• C04B2111/0062

  Gypsum-paper board like materials · CPC title

• B32B2317/12

  Paper, e.g. cardboard · CPC title

• C04B28/14

  containing calcium sulfate cements {(gypsum-paper plates E04C)} · CPC title