High strength and translucency dental zirconia ceramic materials, devices and methods

Patent metadata

Field	Value
Publication number	US-10532008-B2
Application number	US-201815900945-A
Country	US
Kind code	B2
Filing date	Feb 21, 2018
Priority date	Feb 22, 2017
Publication date	Jan 14, 2020
Grant date	Jan 14, 2020

Abstract

A zirconia ceramic material for use in dental applications is provided comprising an yttria-stabilized zirconia material comprising from 4.5 mol % to 5.1 mol % yttria. Optionally, the zirconia ceramic has a coloring agent that may comprise one or more metals selected from terbium (Tb), chromium (Cr), erbium (Er), and cobalt (Co), and further, may, optionally, comprise alumina, which if present may be in an amount from 0 wt % to 0.25 wt %. The zirconia ceramic materials exhibit both enhanced translucency and a flexural strength of at least 800 MPa when fully sintered.

First claim

We claim:

1. A shaded zirconia ceramic material for use in dental applications comprising an yttria-stabilized zirconia material comprising from 4.7 mol % to 5.1 mol % yttria, a coloring agent comprising at least one metal selected from:
a. Tb, measured as Tb 4 O 7 , in an amount from 0.005 wt % to 0.025 wt %;
b. Cr, measured as Cr 2 O 3 , in an amount from 0.0002 wt % to 0.0009 wt %;
c. Er, measured as Er 2 O 3 , in an amount from 0.022 wt % to 0.3 wt %; and
Co, measured as Co 3 O 4 , in an amount from 0 wt % to 0.0001 wt %, and

optionally, alumina in an amount from 0 wt % to 0.25 wt %,
wherein the shaded zirconia ceramic exhibits a flexural strength of at least 800 MPa when fully sintered.

2. The shaded zirconia ceramic material of claim 1 , wherein the shaded zirconia ceramic material exhibits a relative translucency difference (ΔT) from to −3 to −1 at 700 nm when fully sintered.

3. A shaded zirconia ceramic material for use in dental applications comprising
an yttria-stabilized zirconia material comprising from 4.7 mol % to 5.1 mol % yttria,
a coloring agent that comprises at least one metal selected from:
a. Tb, measured as Tb 4 O 7 , in an amount from 0.015 wt % to 0.04 wt %;
b. Cr, measured as Cr 2 O 3 , in an amount from 0.0006 wt % to 0.0017 wt %;
c. Er, measured as Er 2 O 3 , in an amount from 0.016 wt % to 0.4 wt %; and
d. Co, measured as Co 3 O 4 , in an amount from 0.00002 wt % to 0.0025 wt %, and optionally, alumina in an amount from 0 wt % to 0.25 wt %,

wherein the shaded zirconia ceramic exhibits a flexural strength of at least 800 MPa when fully sintered.

4. The shaded zirconia ceramic material of claim 3 , wherein the shaded zirconia ceramic material exhibits a ΔT from −4.5 to −3 at 700 nm when fully sintered.

5. A shaded zirconia ceramic material for use in dental applications comprising
an yttria-stabilized zirconia material comprising from 4.7 mol % to 5.1 mol % yttria,
a coloring agent that comprises at least one metal selected from:
a. Tb, measured as Tb 4 O 7 ,in an amount from 0.03 wt % to 0.06 wt %;
b. Cr, measured as Cr 2 O 3 , in an amount from 0.001 wt % to 0.0025 wt %;
c. Er, measured as Er 2 O 3 , in an amount from 0.02 wt % to 0.6 wt %; and
d. Co, measured as Co 3 O 4 , in an amount from 0.00008 wt % to 0.0045 wt %, and optionally, alumina in an amount from 0 wt % to 0.25 wt %,

wherein the shaded zirconia ceramic exhibits a flexural strength of at least 800 MPa when fully sintered.

6. The shaded zirconia ceramic material of claim 5 , wherein the shaded zirconia ceramic material exhibits a ΔT from −6 to −4 at 700 nm when fully sintered.

7. A shaded zirconia ceramic material for use in dental applications comprising
an yttria-stabilized zirconia material comprising from 4.7 mol % to 5.1 mol % yttria,
a coloring agent that comprises at least one metal selected from:
a. Tb, measured as Tb 4 O 7 , in an amount from 0.04 wt % to 0.08 wt %;
b. Cr, measured as Cr 2 O 3 , in an amount from 0.0015 wt % to 0.003 wt %;
c. Er, measured as Er 2 O 3 , in an amount from 0.15 wt % to 0.6 wt %; and
d. Co, measured as Co 3 O 4 , in an amount from 0.0017 wt % to 0.0055 wt %, and optionally, alumina in an amount from 0 wt % to 0.25 wt %, and

wherein the shaded zirconia ceramic, when fully sintered, exhibits a flexural strength of at least 800 MPa and a ΔT from −6 to −5 at 700 nm.

8. A shaded zirconia ceramic material for use in dental applications comprising
an yttria-stabilized zirconia material comprising from 4.5 mol % to 5.1 mol % yttria,
a coloring agent comprising at least one metal selected from terbium (Tb), chromium (Cr), erbium (Er), and cobalt (Co),
wherein, the shaded zirconia ceramic material, when fully sintered exhibits:
a flexural strength greater 800 MPa,
a CIE color space Value (L*) between 65 and 77, and
a ΔT of (0.632(L*)−49.164)+1.5, at 700 nm.

9. The shaded zirconia ceramic material of claim 8 , wherein the yttria-stabilized zirconia exhibits a ΔT between −6 and 2 at 700 nm.

10. The shaded zirconia material according to claim 8 , wherein the coloring agent comprises at least one metal selected from:
a. Tb, measured as Tb 4 O 7 in an amount from 0 wt % to 0.066 wt %;
b. Cr, measured as Cr 2 O 3 in an amount from 0 wt % to 0.0025 wt %;
c. Er, measured as Er 2 O 3 in an amount from 0 wt % to 0.78 wt %; and
d. Co, measured as Co 3 O 4 , in an amount from 0 wt % to 0.007 wt %.

11. The shaded sintered zirconia body of claim 10 wherein L* is between 73.5 and 76. 4, and ΔT is from −4 to 0.

12. The shaded sintered zirconia body of claim 10 wherein L* is between 71 and 74, and ΔT is from −6 to −1.

13. The shaded sintered zirconia body of claim 10 wherein L* is between 68 and 72. 5, and ΔT is from −2 to −6.

14. The shaded sintered zirconia body of claim 10 wherein L* is between 66 and 71, and ΔT is from −3 to −6.

15. A zirconia ceramic material for use in dental applications comprising:
an yttria-stabilized zirconia material comprising between 4 mol % yttria and 5.1 mol % yttria,
wherein the zirconia ceramic material exhibits a flexural strength of at least 800 MPa and
a total light transmittance of at least 55% at 700 nm, when fully sintered.

16. The zirconia ceramic material of claim 15 , wherein the yttria-stabilized zirconia material comprises between 4.5 mol % yttria and 5.1 mol % yttria.

17. The zirconia ceramic material of claim 15 , wherein the yttria-stabilized zirconia material comprises between 4.7 mol % yttria and 5.1 mol % yttria and the total light transmittance is at least 56% at 700 nm.

18. The zirconia ceramic material of claim 15 , wherein the zirconia ceramic material comprises a bisqued body having a density between 57% and 62% of theoretical density and median pore diameter from 40 nm to 70 nm.

19. The zirconia ceramic material of claim 18 , wherein the bisque body comprises a particle size at D(50) that is from 100 nm to 300 nm.

20. A zirconia ceramic material for use in dental applications comprising
an yttria-stabilized zirconia material comprising between 3.9 mol % yttria and 5.0 mol % yttria,
wherein the zirconia ceramic material exhibits a flexural strength of at least 800 MPa, and
a ΔT from −2.5 to 0.5 at 700 nm, when fully sintered.

21. The zirconia ceramic material of claim 20 , wherein the yttria-stabilized zirconia material comprises between 4.6 mol % yttria and 4.9 mol % yttria.

22. The zirconia ceramic material of claim 20 , wherein the ΔT is from −1 to 0 at 700 nm when fully sintered.

Assignees

• Glidewell James R Dental Ceramics Inc

Inventors

• Balasubramanian Sreeram
• Gubb Tyler Arthur
• Akash
• Valenti Thomas C
• Yang Yan
• Recor Kevin Michael

Classifications

• C04B35/486

  Fine ceramics · CPC title

• C04B2235/3241

  Chromium oxides, chromates, or oxide-forming salts thereof · CPC title

• C04B2235/6567

  Treatment time · CPC title

• C04B2235/3277

  Co3O4 · CPC title

• C04B2235/6027

  Slip casting · CPC title