Low-oxygen clean steel and low-oxygen clean steel product

Patent metadata

Field	Value
Publication number	US-10526686-B2
Application number	US-201414783698-A
Country	US
Kind code	B2
Filing date	Apr 24, 2014
Priority date	Apr 24, 2013
Publication date	Jan 7, 2020
Grant date	Jan 7, 2020

Abstract

Low-oxygen clean steel is provided containing C, Si, Mn, P, and S as chemical components, and further containing, by mass %, 0.005% to 0.20% of Al, greater than 0% to 0.0005% of Ca, 0.00005% to 0.0004% of REM, and greater than 0% to 0.003% of T.O, wherein the REM content, the Ca content, and the T.O content satisfy 0.15≤REM/Ca≤4.00 and Ca/T.O≤0.50, nonmetallic inclusions which have a maximum predicted diameter of 1 μm to 30 μm measured using an extreme value statistical method under the condition in which a prediction area is 30,000 mm2, and contain Al2O3 and REM oxide are dispersed in the steel, an average proportion of the Al2O3 in the nonmetallic inclusions is greater than 50%, the REM is one or two or more of rare-earth elements La, Ce, Pr, and Nd, and the steel is Al-deoxidized steel or Al—Si-deoxidized steel.

First claim

The invention claimed is:

1. A low-oxygen clean steel containing C, Si, Mn, P, and S as chemical components, and further containing, by mass %, 0.010% to 0.20% of Al, 0.0001% to 0.0003% of Ca, 0.00005% to 0.0004% of REM, and greater than 0% to 0.003% of T.O,
wherein the REM content, the Ca content, and the T.O content satisfy the following Expressions 1 and 2,
nonmetallic inclusions which have a maximum predicted diameter of 1 μm to 30 μm measured using an extreme value statistical method under the condition in which a prediction area is 30,000 mm 2 , and contain Al 2 O 3 and REM oxide are dispersed in the steel,
a proportion of the Al 2 O 3 is greater than 50% by mass based on the total amount of nonmetallic inclusions,
a proportion of CaO is 1.0% or less by mass based on the total amount of the nonmetallic inclusions,
the REM is one or two or more of rare-earth elements La, Ce, Pr, and Nd, and
the steel is Al-deoxidized steel or Al—Si-deoxidized steel,
0.15≤REM/Ca≤4.00  Expression 1,

Ca/T.O≤0.50  Expression 2.

2. The low-oxygen clean steel according to claim 1 ,
wherein the following Expression 3 is satisfied,
0.05≤REM/T.O≤0.50  Expression 3.

3. The low-oxygen clean steel according to claim 1 , containing, by mass %, 1.20% or less of C, 3.00% or less of Si, 16.0% or less of Mn, 0.05% or less of P, and 0.05% or less of S as the chemical components with the remainder Fe and impurities.

4. The low-oxygen clean steel according to claim 3 , further containing, by mass %, one or two or more of 3.50% or less of Cr, 0.85% or less of Mo, 4.50% or less of Ni, 0.20% or less of Nb, 0.45% or less of V, 0.30% or less of W, 0.006% or less of B, 0.06% or less of N, 0.25% or less of Ti, 0.50% or less of Cu, 0.45% or less of Pb, 0.20% or less of Bi, 0.01% or less of Te, 0.20% or less of Sb, and 0.01% or less of Mg as the chemical components.

5. A low-oxygen clean steel product produced by processing the low-oxygen clean steel according to claim 1 .

6. A low-oxygen clean steel product produced by processing the low-oxygen clean steel according to claim 3 .

7. A low-oxygen clean steel product produced by processing the low-oxygen clean steel according to claim 4 .

8. The low-oxygen clean steel according to claim 2 , containing, by mass %, 1.20% or less of C, 3.00% or less of Si, 16.0% or less of Mn, 0.05% or less of P, and 0.05% or less of S as the chemical components with the remainder Fe and impurities.

9. The low-oxygen clean steel according to claim 8 , further containing, by mass %, one or two or more of 3.50% or less of Cr, 0.85% or less of Mo, 4.50% or less of Ni, 0.20% or less of Nb, 0.45% or less of V, 0.30% or less of W, 0.006% or less of B, 0.06% or less of N, 0.25% or less of Ti, 0.50% or less of Cu, 0.45% or less of Pb, 0.20% or less of Bi, 0.01% or less of Te, 0.20% or less of Sb, and 0.01% or less of Mg as the chemical components.

10. A low-oxygen clean steel product produced by processing the low-oxygen clean steel according to claim 2 .

11. A low-oxygen clean steel product produced by processing the low-oxygen clean steel according to claim 8 .

12. The low-oxygen clean steel according to claim 1 , wherein a proportion of SiO 2 in the inclusions is 1.0% or less by mass based on the total amount of nonmetallic inclusions.

13. The low-oxygen clean steel according to claim 1 , wherein the proportion of the Al 2 O 3 in the inclusions is greater than 61.8% to 82.9% by mass based on the total amount of the nonmetallic inclusions.

14. The low-oxygen clean steel according to claim 1 , wherein the proportion of the Al 2 O 3 is greater than 66.0% to 82.9% by mass based on the total amount of nonmetallic inclusions.

Assignees

• Nippon Steel & Sumitomo Metal Corp
• Nippon Steel Corp

Inventors

• AONO Michimasa
• Miyamoto Kenichiro
• Suzuki Masanobu

Classifications

• C21C7/06

  Deoxidising, e.g. killing · CPC title

• C21C7/04

  Removing impurities by adding a treating agent · CPC title

• C22C38/60

  containing lead, selenium, tellurium, or antimony, or more than 0.04% by weight of sulfur · CPC title

• C22C38/08

  containing nickel {(C22C38/105 takes precedence)} · CPC title

• C22C38/00

  Ferrous alloys, e.g. steel alloys (cast-iron alloys C22C37/00) · CPC title