Treatment of calcium carbonate containing materials for increased filler load in paper

Patent metadata

Field	Value
Publication number	US-10519307-B2
Application number	US-201715682999-A
Country	US
Kind code	B2
Filing date	Aug 22, 2017
Priority date	May 11, 2012
Publication date	Dec 31, 2019
Grant date	Dec 31, 2019

Abstract

The present invention concerns a process for preparing self-binding pigment particles from an aqueous suspension of calcium carbonate containing material, wherein an anionic binder and at least one cationic polymer are mixed with the suspension.

First claim

The invention claimed is:

1. A self-binding pigment particle suspension obtained by the process comprising the following steps:
a) providing an aqueous suspension comprising at least one calcium carbonate containing material,
b) providing at least one acid or acid salt in an amount from 0.001 to 40 wt.-% based on the total weight of the dry calcium carbonate containing material, wherein the anion of the acid or acid salt is capable of forming water-insoluble calcium salts, and wherein the at least one acid or acid salt of step b) is selected from the group consisting of citric acid, oxalic acid, phosphoric acid, arsenic acid, iodic acid, acid salts thereof, and any mixture thereof,
c) providing an anionic polymeric binder in an amount from 0.001 to 20 wt.-% based on the total weight of the dry calcium carbonate containing material, wherein the binder comprises at least one modified polysaccharide,
d) providing at least one cationic polymer in an amount from 0.001 to 20 wt.-% based on the total weight of the dry calcium carbonate containing material,
e) mixing the aqueous suspension of step a) with the at least one acid or acid salt of step b) to obtain a suspension of calcium carbonate containing material that is at least partially coated with a water-insoluble calcium salt formed from the anion of the acid or the acid salt, and
f) mixing the suspension of step e), the anionic polymeric binder of step c) and the at least one cationic polymer of step d) to obtain an aqueous suspension of self-binding pigment particles, wherein the self-binding pigment particles so obtained comprise calcium carbonate containing material which is at least partially coated with a water-insoluble calcium salt formed from the anion of the acid or acid salt, the anionic binder comprising the at least one modified polysaccharide, and the at least one cationic polymer.

2. The suspension of claim 1 , wherein in step f) the suspension obtained by step e) is, in a first step, mixed with the anionic polymeric binder of step c), and then, in a second step, is mixed with the at least one cationic polymer of step d).

3. The suspension of claim 1 , wherein in step f) the suspension obtained by step e) is mixed with the anionic polymeric binder of step c) and the at least one cationic polymer of step d) in one step.

4. The suspension of claim 1 , wherein in step f) the suspension obtained by step e) is, in a first step, mixed with the at least one cationic polymer of step d), and then, in a second step, is mixed with the anionic polymeric binder of step c).

5. The suspension of claim 1 , wherein the suspension obtained by step e) is concentrated before step f).

6. The suspension of claim 1 , wherein the at least one calcium carbonate containing material is selected from the group consisting of calcium carbonate, calcium carbonate containing minerals, mixed calcium carbonate based fillers, and any mixture thereof.

7. The suspension of claim 1 , wherein the at least one calcium carbonate containing material is precipitated calcium carbonate (PCC).

8. The suspension of claim 7 , wherein the PCC is scalenohedral PCC (S-PCC), rhombohedral PCC (R-PCC), prismatic PCC (P-PCC), cubic PCC (C-PCC), or any mixture thereof.

9. The suspension of claim 1 , wherein the at least one calcium carbonate containing material of step a) is provided in form of particles having a weight median particle diameter d 50 value from 0.1 to 100 μm.

10. The suspension of claim 1 , wherein the at least one calcium carbonate containing material of step a) is provided in form of particles having a specific surface area from 0.1 to 200 m 2 /g.

11. The suspension of claim 1 , wherein the aqueous suspension of step a) has a solid content from 10 to 70 wt.-%, based on the total weight of the suspension.

12. The suspension of claim 1 , wherein the suspension of step a) further comprises talc, kaolin, TiO 2 , bentonite or any mixture thereof.

13. The suspension of claim 1 , wherein the at least one acid or acid salt of step b) is added in an amount from 0.005 to 20 wt.-%, based on the total weight of the dry calcium carbonate containing material.

14. The suspension of claim 1 , wherein the at least one acid or acid salt of step b) is selected from the group consisting of citric acid, oxalic acid, phosphoric acid, acid salts thereof, and any mixture thereof.

15. The suspension of claim 1 , wherein the at least one acid or acid salt of step b) is an acid salt comprising at least one non-hydrogen cation that is sodium.

16. The suspension of claim 1 , wherein the at least one acid or acid salt of step b) is an acid salt selected from the group consisting of sodium dihydrogen citrate, potassium dihydrogen citrate, disodium hydrogen citrate, dipotassium hydrogen citrate, trisodium citrate, tripotassium citrate, disodium oxalate, dipotassium oxalate, magnesium oxalate sodium dihydrogen phosphate, potassium dihydrogen phosphate, disodium hydrogen phosphate, dipotassium hydrogen phosphate, trisodium phosphate and tripotassium phosphate.

17. The suspension of claim 1 , wherein the at least one acid or acid salt of step b) is trisodium citrate.

18. The suspension of claim 1 , wherein the suspension obtained by step e) has a solid content from 2 to 60 wt.-%, based on the total weight of the suspension.

19. The suspension of claim 1 , wherein the at least one modified polysaccharide is a carboxymethyl derivate, a carboxymethyl hydroxypropyl derivate, a carboxymethyl hydroxyethyl derivate of a polysaccharide, a carboxymethylcellulose, an anionic guar, an anionic starch, xanthan gum, or any mixture thereof.

20. The suspension of claim 1 , wherein the at least one modified polysaccharide has a degree of substitution of the hydroxyl groups in the range from 0.4 to 2.0.

21. The suspension of claim 1 , wherein the at least one modified polysaccharide has a degree of substitution of the hydroxyl groups in the range from 0.7 to 1.5.

22. The product of claim 1 , wherein the intrinsic viscosity of the at least one modified polysaccharide is in the range from 5 to 500 ml/g.

23. The product of claim 1 , wherein the binder of step c) is in form of an aqueous solution or dry material.

24. The suspension of claim 1 , wherein the binder of step c) is in form of an aqueous solution having a binder concentration from 1 to 70 wt.-%, based on the total weight of the solution.

25. The suspension of claim 1 , wherein the binder of step c) is added in an amount from 0.005 to 15 wt.-%, based on the total weight of the dry calcium carbonate containing material.

26. The suspension of claim 1 , wherein the at least one cationic polymer of step d) is selected from the group consisting of polyethyleneimines, polyacrylamides, cationic epichlorohydrin resins, cationic starch, cationic guar, and any mixture thereof.

27. The suspension of claim 1 , wherein the at least one cationic polymer of step d) is in form of a solution or dry material.

28. The suspension of claim 1 , wherein the at least one cationic polymer of step d) is in form of a solution having a concentration from 0.5 to 70 wt.-%, based on the total weight of the solution.

29. The suspension of claim 1 , wherein the at least one cationic polymer of step d) is added in an amount from 0.005 to 15 wt.-%, based on the total weight of the dry calcium carbonate containing material.

30. A

Assignees

• Omya Int Ag

Inventors

• Gantenbein Daniel
• Schoelkopf Joachim
• Gane Patrick A C

Classifications

• D21H19/385

  Oxides, hydroxides or carbonates · CPC title

• D21H17/69

  modified, e.g. by association with other compositions prior to incorporation in the pulp or paper · CPC title

• D21H19/54

  Starch · CPC title

• D21H19/42

  at least partly organic · CPC title

• D21H19/56

  Macromolecular organic compounds or oligomers thereof obtained by reactions only involving carbon-to-carbon unsaturated bonds · CPC title