Cathode active material for non-aqueous electrolyte secondary battery and manufacturing method thereof

Patent metadata

Field	Value
Publication number	US-10516164-B2
Application number	US-201816034586-A
Country	US
Kind code	B2
Filing date	Jul 13, 2018
Priority date	May 22, 2013
Publication date	Dec 24, 2019
Grant date	Dec 24, 2019

Abstract

The purpose of the present invention is to easily provide at low cost, a cathode active material for non-aqueous electrolyte secondary batteries, which exhibits high particle strength and high weather resistance, while enabling achievement of excellent charge and discharge capacity and excellent output characteristics in cases where the cathode active material is used as a cathode material of a non-aqueous electrolyte secondary battery. A slurry of from 500 g/L to 2000 g/L is formed by adding water to a powder of a lithium nickel composite oxide represented by the general formula (A): Li z Ni 1-x-y Co x M y O 2 , where 0.10≤x≤0.20, 0≤y≤0.10, 0.97≤z≤1.20, and M represents at least one element selected from among Mn, V, Mg, Mo, Nb, Ti and Al); the slurry is washed with water by stirring; and after filtration, the resulting material is subjected to a heat treatment at a temperature of from 120° C. to 550° C. (inclusive) in an oxygen atmosphere having an oxygen concentration of 80% by volume or more.

First claim

What is claimed is:

1. A manufacturing method for manufacturing a cathode active material for a non-aqueous electrolyte secondary battery comprising steps of: preparing a powder of a lithium nickel composite oxide that is represented by a general formula (A): Li z Ni 1-x-y Co x M y O 2 , wherein 0.10≤x≤0.20, 0≤y≤0.10, 0.97≤z≤1.20, and M is at least one element that is selected from the group consisting of Mn, V, Mg, Mo, Nb, Ti and Al; forming a 500 g/L to 2000 g/L slurry by adding water to the powder; washing the slurry by mixing such that the particles that exist on a surface of the lithium composite oxide are peeled away and then the particles adhered again to the surface to cover the lithium composite oxide; filtering the slurry; and performing heat treatment to the powder after filtering at a temperature of no less than 120° C. and no greater than 550° C. in an oxygen atmosphere having an oxygen concentration of 80% by volume or more, to obtain a powder of a lithium nickel composite oxide that is represented by a general formula (B): Li z Ni 1-x-y Co x M y O 2 , where 0.10≤x≤0.20, 0≤y≤0.10, 0.95≤z≤1.10, and M is at least one element that is selected from the group consisting of Mn, V, Mg, Mo, Nb, Ti and Al, in which a coating layer that includes a high concentration of lithium is formed on the surface of the lithium nickel composite oxide.

2. The manufacturing method for manufacturing a cathode active material for a non-aqueous electrolyte secondary battery according to claim 1 , wherein a temperature of the water that is used during the washing process is 10° C. to 50° C.

3. The manufacturing method for manufacturing a cathode active material for a non-aqueous electrolyte secondary battery according to claim 1 , wherein the temperature during the heat treatment is 120° C. or greater but less than 400° C.

4. The manufacturing method for manufacturing a cathode active material for a non-aqueous electrolyte secondary battery according to claim 1 , wherein a rate of temperature rise during the heat treatment is 2° C./min to 10° C./min.

5. The manufacturing method for manufacturing a cathode active material for a non-aqueous electrolyte secondary battery according to claim 1 , wherein a moisture content of the cathode active material after the heat treatment is 0.2% by mass or less.

Assignees

• Sumitomo Metal Mining Co

Inventors

• Nakayama Tomoko
• Kokado Rei
• Mori Kensaku

Classifications

• H01M4/485 Primary

  of mixed oxides or hydroxides for inserting or intercalating light metals, e.g. LiTi2O4 or LiTi2OxFy (H01M4/505, H01M4/525 take precedence) · CPC title

• H01M10/052

  Li-accumulators · CPC title

• C01P2002/30

  Three-dimensional structures · CPC title

• H01M4/505

  of mixed oxides or hydroxides containing manganese for inserting or intercalating light metals, e.g. LiMn2O4 or LiMn2OxFy · CPC title

• C01G53/42 Primary

  containing alkali metals, e.g. LiNiO2 · CPC title