Flame retarder, flame retardant resin composition and method of producing the flame retarder

Patent metadata

Field	Value
Publication number	US-10508239-B2
Application number	US-201313867601-A
Country	US
Kind code	B2
Filing date	Apr 22, 2013
Priority date	Mar 23, 2004
Publication date	Dec 17, 2019
Grant date	Dec 17, 2019

Abstract

A flame retardant resin composition in which an acrylonitrile-styrene based polymer, into which sulfonic acid groups and/or sulfonate groups have been introduced by sulfonating processing with a sulfonating agent containing less than 3 wt % of moisture, is contained in a resin to be made flame retardant, so that flame retardant properties will be conferred on the resin flame resistant.

First claim

What is claimed is:

1. A resin composition containing a flame retarder which comprises:
an acrylonitrile-styrene copolymer containing 1 mol% to 90 mol% of styrene units, the acrylonitrile-styrene copolymer having a weight average molecular weight ranging from 20,000 to 500,000;
sulfonate groups in all monomer units of the acrylonitrile-styrene copolymer in an amount ranging from 0.01 mol % to 8 mol % of the monomer units of the acrylonitrile-styrene copolymer; and
a monomer ratio of a mol% content of the styrene to a mol% content of the acrylonitrile of 90/10-1/99,
wherein,
the resin composition has a rating of V-0 or V-1 in accordance with Underwriter Laboratories flammability testing standard UL94.

2. The resin composition according to claim 1 wherein the acrylonitrile-styrene copolymer contains at least one or more of an acrylonitrile-styrene copolymer, an acrylonitrile-butadiene-styrene copolymer, an acrylonitrile-chlorinated polyethylene-styrene copolymer, an acrylonitrile-styrene-acrylate copolymer, an acrylonitrile-ethylene-propylene rubber-styrene copolymer, an acrylonitrile-ethylene-propylene-diene-styrene copolymer.

3. The resin composition according to claim 1 wherein the sulfonating agent is one or more selected from the group consisting of sulfuric anhydride, fuming sulfuric acid, chlorosulfonic acid and polyalkylbenzene sulfonic acid.

4. The resin composition according to claim 1 wherein the acrylonitrile-styrene copolymer contains monomer units having aromatic skeletons ranging between 30 mol % and 90 mol %.

5. The resin composition according to claim 1 wherein the acrylonitrile-styrene copolymer contains monomer units having aromatic skeletons ranging between 40 mol % and 90 mol %.

6. The resin composition according to claim 1 wherein the sulfonate groups include at least one of Na, K, Li, Ca, Mg, Al, Zn, Sb, or Sn salt groups of sulfonic acid.

7. The resin composition of claim 1 having no amide groups or carboxylic groups exhibiting hygroscopicity.

8. The resin composition of claim 1 , wherein the acrylonitrile-styrene copolymer contains 10 mol% to 80 mol% of acrylonitrile monomer units.

9. The flame resin composition of claim 8 , wherein the acrylonitrile-styrene copolymer contains 20 mol% to 70 mol%of acrylonitrile monomer units.

10. The resin composition of claim 1 , wherein the acrylonitrile-styrene copolymer contains 10 mol% to 90 mol% of styrene units.

11. The resin composition of claim 10 , wherein the acrylonitrile-styrene copolymer contains 20 mol% to 80 mol% of styrene units.

Assignees

• Sony Corp

Inventors

• Inagaki Yasuhito

Classifications

• C08G64/42

  Chemical after-treatment · CPC title

• C08G64/081

  containing sulfur · CPC title

• C08L101/02

  characterised by the presence of specified groups {, e.g. terminal or pendant functional groups} · CPC title

• C08L25/18

  Homopolymers or copolymers of aromatic monomers containing elements other than carbon and hydrogen · CPC title

• C08L25/12 Primary

  with unsaturated nitriles · CPC title