Rubber compound for tires, pneumatic tire, and an airless tire

Patent metadata

Field	Value
Publication number	US-10507692-B2
Application number	US-201515517130-A
Country	US
Kind code	B2
Filing date	Sep 30, 2015
Priority date	Oct 6, 2014
Publication date	Dec 17, 2019
Grant date	Dec 17, 2019

Abstract

To provide a rubber compound for tires, a pneumatic tire and an airless tire capable of improving the steering stability of the tire while exerting excellent low fuel consumption performance. A rubber compound for tires characterized in that, of vulcanized rubber's physical properties, a complex elastic modulus E* 70 (unit: MPa) and a loss tangent tan δ 70 under initial strain of 10%, dynamic strain of 2% and temperature of 70 degrees C., satisfy 90<E* 70 <250, and E* 70 /tan δ 70 >800. A pneumatic tire provided with a rubber member made of the above-mentioned rubber compound. An airless tire provided with a rubber member made of the above-mentioned rubber compound. An airless tire provided in a tread ring with a shear rubber layer made of the above-mentioned rubber compound.

First claim

The invention claimed is:

1. An airless tire comprising a rubber member made of a rubber composition having a complex elastic modulus E * 70 (unit: MPa) and a loss tangent tan δ 70 under the initial strain of 10%, the dynamic strain of 2%, and the temperature of 70 degrees C., satisfy the following expressions (1) and (2):
90< E* 70 <250  (1)

E* 70 /tan δ 70 >800  (2).

2. The airless tire as set forth in claim 1 , wherein
the rubber composition comprising a rubber component, a filler and a cross-linking agent,
the rubber component is one or more kinds of polymers selected from the group consisting of natural rubber (NR), isoprene rubber (IR), butadiene rubber (BR), styrene-butadiene rubber (SBR), styrene-isoprene-butadiene rubber (SIBR), chioroprene rubber (CR), acrylonitrile-butadiene rubber (NBR), ethylene-propylene-diene rubber (EPDM), isobutylene-isoprene rubber (IIR), and halogenated butyl rubber (X-IIR),
the filler is carbon black and/or silica for reinforcing the rubber composition, and
the cross-linking agent is one selected from the group consisting of sulfur, organic cross-linking agents, and organic-inorganic hybrid cross-linking agents.

3. An airless tire comprising
a cylindrical tread ring provided with a ground contacting surface,
a hub disposed radially inside the tread ring and fixed to a vehicle axle, and
a spoke connecting the tread ring and the hub,
wherein,
the tread ring comprises
a tread rubber forming the ground contacting surface,
an outer reinforcing cord layer disposed closest to the tread rubber,
an inner reinforcing cord layer disposed radially inside the outer reinforcing cord layer, and
a shearing rubber layer disposed between the outer reinforcing cord layer and the inner reinforcing cord layer,
the shearing rubber layer has a complex elastic modulus E * 70 (unit: MPa) and a loss tangent tan δ 70 under the initial strain of 10%, the dynamic strain of 2%, and the temperature of 70 degrees C. which satisfy following expressions (1) and (2):
90< E* 70 <250  (1)

E* 70 /tan δ 70 >800  (2).

4. The airless tire as set forth in claim 3 , wherein the shearing rubber layer has
a complex elastic modulus E * 30 (unit: MPa) under the initial strain of 10%, the dynamic strain of 2%, and the temperature of 30 degrees C., and
a complex elastic modulus E* 100 (unit: MPa) under the initial strain of 10%, the dynamic strain of 2%, and the temperature of 100 degrees C.
which satisfy a following expression (3):
E* 100 /E* 30 >0.8  (3).

5. The airless tire as set forth in claim 3 , wherein the shearing rubber layer has
a breaking elongation EB X in the tire circumferential direction and a breaking elongation EB Y in the tire axial direction which satisfy a following expression (4), and
a breaking strength TB X in the tire circumferential direction and a breaking strength TB Y in the tire axial direction which satisfy a following expression (5):
0.85< EB X /EB Y <1.2  (4)

0.85< TB X /TB Y <1.2  (5).

6. The airless tire as set forth in claim 3 , wherein
the shearing rubber layer has a volume resistivity less than 1×10 8 ohm cm.

7. The airless tire as set forth in claim 3 , wherein
reinforcing cords of the outer reinforcing cord layer and
reinforcing cords of the inner reinforcing cord layer are steel cords.

8. The airless tire as set forth in claim 3 , wherein, the outer reinforcing cord layer comprise
a first cord ply including first reinforcing cords arranged to incline with respect to the tire circumferential direction, and
a second cord ply disposed radially outside the first cord ply and including second reinforcing cords arranged to incline with respect to the tire circumferential direction at the same angle as and to the opposite direction to the first reinforcing cords, and

the inner reinforcing cord layer comprises
a third cord ply including third reinforcing cords arranged in parallel with the tire circumferential direction or the tire axial direction.

9. The airless tire as set forth in claim 8 , wherein
the outer reinforcing cord layer further comprises a fourth cord ply disposed radially outside the second cord ply and including fourth reinforcing cords.

10. The airless tire as set forth in claim 9 , wherein
the fourth reinforcing cords are arranged in parallel with the tire circumferential direction, and an elastic modulus of the fourth reinforcing cords is not greater than elastic moduli of the first reinforcing cords and the second reinforcing cords.

11. The airless tire as set forth in claim 8 , wherein
the outer reinforcing cord layer further comprises a fifth cord ply disposed radially inside the first cord ply and including fifth reinforcing cords.

12. The airless tire as set forth in claim 11 , wherein
the fifth reinforcing cords are arranged in parallel with the tire circumferential direction.

13. The airless tire as set forth in claim 8 , wherein
the third reinforcing cords are arranged in parallel with the tire circumferential direction.

14. The airless tire as set forth in claim 8 , wherein
an angle θ of the first reinforcing cords with respect to the tire circumferential direction is 5 to 85 degrees.

15. The airless tire as set forth in claim 8 , wherein
a radial distance between
the reinforcing cord disposed radially innermost among the reinforcing cords of the outer reinforcing cord layer and
the reinforcing cord disposed radially outermost among the reinforcing cords of the inner reinforcing cord layer is not less than 3 mm.

16. The airless tire as set forth in claim 3 , wherein
the shearing rubber layer is made of a rubber composition comprising a rubber component, a filler and a cross-linking agent.

17. The airless tire as set forth in claim 16 , wherein
the rubber component is one or more kinds of polymers selected from the group consisting of natural rubber (NR), isoprene rubber (IR), butadiene rubber (BR), styrene-butadiene rubber (SBR), styrene-isoprene-butadiene rubber (SIBR), chloroprene rubber (CR), acrylonitrile-butadiene rubber (NBR), ethylene-propylene-diene rubber (EPDM), isobutylene-isoprene rubber (IIR), and halogenated butyl rubber (X-IIR).

18. The airless tire as set forth in claim 17 , wherein the filler is carbon black and/or silica for reinforcing the rubber composition.

19. The airless tire as set forth in claim 16 , wherein
the cross-linking agent is one selected from the group consisting of sulfur, organic cross-linking agents, and organic-inorganic hybrid cross-linking agents.

20. The airless tire as set forth in claim 3 , wherein
the shearing rubber layer is made of a rubber composition comprising a rubber component, a filler and a cross-linking agent,
the rubber component is one or more kinds of polymers selected from the group consisting of natural rubber (NR), isoprene rubber (IR), butadiene rubber (BR), styrene-butadiene rubber (SBR), styrene-isoprene-butadiene rubber (SIBR), chloroprene rubber (CR), acrylonitrile-butadiene rubber (NBR), ethylene-propylene-diene rubber (EPDM), isobutylene-isoprene rubber (IIR), and halogenated butyl rubber (X-IIR),
the filler is carbon black and/or silica for reinforcing the rubber composition, and
the cross-linking agent is one selected from the group consisting of sulfur, organic cross-linking agents, and organic-inorganic hybrid cross-linking agents.

Assignees

• Sumitomo Rubber Ind

Inventors

• YOKOYAMA Yuka
• Sugimoto Mutsuki
• Iwamura Wako
• Sugiya Makoto

Classifications

• B60B9/26

  comprising resilient spokes · CPC title

• B60C7/00

  Non-inflatable or solid tyres (B60C1/00 takes precedence) · CPC title

• B60C1/0008

  Compositions of the inner liner · CPC title

• B60C1/00 Primary

  Tyres characterised by the chemical composition or the physical arrangement or mixture of the composition · CPC title

• B60C1/0025

  Compositions of the sidewalls · CPC title