Copper-titanium alloy foil having plated layer

Patent metadata

Field	Value
Publication number	US-10495840-B2
Application number	US-201715473721-A
Country	US
Kind code	B2
Filing date	Mar 30, 2017
Priority date	Mar 31, 2016
Publication date	Dec 3, 2019
Grant date	Dec 3, 2019

Abstract

The present invention provides a titanium copper foil having improved adhesion to solder and higher resistance to discoloration due to a high temperature and high humidity environment, an acid solution or an alkaline solution, and as well as having improved etching processability. The present invention provides a titanium copper foil comprising a base metal, the base metal having a composition containing Ti of from 1.5 to 5.0% by mass, the balance being copper and inevitable impurities, and having a thickness of from 0.018 to 0.1 mm, wherein the titanium copper foil has an Sn plated layer on a surface of the base metal, and has an adhesive strength of 0.5 N or more as measured by a solder adhesive strength test according to the definition in the specification.

First claim

What is claimed is:

1. A titanium copper foil comprising a base metal, the base metal having a composition containing Ti of from 1.5% by mass to 5.0% by mass, optionally containing one or more further element(s) selected from the group consisting of Ag, B, Co, Fe, Mg, Mn, Mo, Ni, P, Si, Cr, and Zr in a total amount of from 0% by mass to 1.0% by mass, the balance being copper and inevitable impurities, and the base metal having a thickness of from 0.018 mm to 0.1 mm, wherein the titanium copper foil has an Sn plated layer on a surface of the base metal, and has an adhesive strength of 0.5 N or more as measured by a solder adhesive strength test wherein, according to the solder adhesive strength test, the titanium copper foil having the plated layer and a pure copper foil (alloy number C1100 as defined in JIS H3100-2012 with a foil thickness of 0.02 mm to 0.05 mm) are joined together via a lead-free solder (Sn-3.0% by mass Ag-0.5% by mass Cu), and the titanium copper foil is in a form of a rectangle having a width of 15 mm and a length of 200 mm, the pure copper foil is in the form of a rectangle having a width of 20 mm and a length of 200 mm, and the lead-free solder (diameter: 0.4±0.02 mm, length 120±1 mm) is arranged in an area of 30 mm×15 mm at a central portion in a lengthwise direction so as to fall within the above-mentioned area, and joined at a joining temperature of 245° C.±5° C., and then, after joining, the adhesive strength is measured by performing a 180° peeling test at a speed of 100 mm/min, and an average value of the load (N) in the section of 40 mm from 30 mm to 70 mm of peeling displacement is defined as the adhesive strength.

2. The titanium copper foil according to claim 1 , wherein the Sn plated layer has a thickness of from 0.01 μm to 2.0 μm.

3. The titanium copper foil according to claim 1 , wherein the base metal composition further contains at least one said further element selected from the group consisting of Ag, B, Co, Fe, Mg, Mn, Mo, Ni, P, Si, Cr, and Zr in a total amount of up to 1.0% by mass.

4. The titanium copper foil according to claim 1 , wherein the titanium copper foil has a tensile strength in a direction parallel to a rolling direction of 1100 MPa or more.

5. The titanium copper foil according to claim 1 , wherein the adhesive strength is 20 N or more.

6. The titanium copper foil according to claim 1 , wherein a decreasing rate of the adhesive strength after heating at a temperature of 85° C. for 100 hours relative to the adhesive strength before heating is less than 5%.

7. The titanium copper foil according to claim 1 , wherein the titanium copper foil is suitable for etching processing.

8. An electronic component comprising the titanium copper foil according to claim 1 .

9. A joined body of the titanium copper foil according to claim 1 and a solder, wherein the joined body has a joined site to the solder on a surface of the plated layer on the titanium copper foil.

10. An autofocus module comprising the titanium copper foil according to claim 1 as a spring material.

11. An autofocusing camera module comprising a lens; a spring member made of the titanium copper foil according to claim 1 for elastically biasing the lens to an initial position in an optical axis direction; and an electromagnetic driving means configured to generate electromagnetic force for withstanding the biasing force of the spring member so that the lens can be driven in the optical axis direction, wherein the electromagnetic driving means comprises a coil, and wherein the spring member is joined to the coil at a location having the plated layer by soldering.

12. A method for joining the titanium copper foil according to claim 1 to a conductive member, comprising shape processing the titanium copper foil by etching; and joining the resulting profiled product of the titanium copper foil to the conductive member at a location having the plated layer by soldering.

13. A method for producing a titanium copper foil according to claim 1 , comprising:
preparing a base metal having a composition containing Ti of from 1.5% by mass to 5.0% by mass, optionally containing one or more further element(s) selected from the group consisting of Ag, B, Co, Fe, Mg, Mn, Mo, Ni, P, Si, Cr, and Zr in a total amount of from 0% by mass to 1.0% by mass, the balance being copper and inevitable impurities, wherein the base metal has a thickness of from 0.018 mm to 0.1 mm, and has a surface glossiness of from 100 to 200; and
forming an Sn plated layer having a thickness of 0.01 μm or more on a surface of the base metal to produce a titanium copper foil, wherein the titanium copper foil has an adhesive strength of 0.5 N or more as measured by the solder adhesive strength test, wherein, in the solder adhesive strength test, the titanium copper foil having the plated layer and a pure copper foil (alloy number C1100 as defined in JIS H3100-2012; foil thickness of 0.02 mm to 0.05 mm) are joined together via a lead-free solder (Sn-3.0% by mass Ag-0.5% by mass Cu), and the titanium copper foil is in a form of a rectangle having a width of 15 mm and a length of 200 mm, and the pure copper foil is in the form of a rectangle having a width of 20 mm and a length of 200 mm, and the lead-free solder (diameter: 0.4±0.02 mm, length 120±1 mm) is arranged in an area of 30 mm×15 mm at a central portion in the lengthwise direction so as to fall within the above-mentioned area, and joined at a joining temperature of 245° C.±5° C., and then, after joining, the adhesive strength is measured by performing a 180° peeling test at a speed of 100 mm/min, and an average value of the load (N) in the section of 40 mm from 30 mm to 70 mm of peeling displacement is defined as the adhesive strength.

14. The method for producing the titanium copper foil according to claim 13 , wherein the Sn plated layer has a thickness of from 0.01 μm to 2.0 μm.

15. The method for producing the titanium copper foil according to claim 13 , wherein the base metal composition further contains at least one said further element selected from the group consisting of Ag, B, Co, Fe, Mg, Mn, Mo, Ni, P, Si, Cr, and Zr in a total amount of up to 1.0% by mass.

16. The method for producing the titanium copper foil according to claim 13 , wherein the surface of the base metal having the surface glossiness of from 100 to 200 has arithmetic average roughness (Ra) of 0.5 μm or less.

Assignees

• Jx Nippon Mining & Metals Corp

Inventors

• Tsujie Kenta

Classifications

• H04N23/57

  Mechanical or electrical details of cameras or camera modules specially adapted for being embedded in other devices · CPC title

• Y10T428/26

  Web or sheet containing structurally defined element or component, the element or component having a specified physical dimension · CPC title

• Y10T428/12993

  Surface feature [e.g., rough, mirror] · CPC title

• B23K2103/12

  Copper or alloys thereof · CPC title

• C25D7/0614 Primary

  Strips or foils · CPC title