High-toughness seamless steel tube for automobile safety airbag and manufacturing method therefor

Patent metadata

Field	Value
Publication number	US-10494690-B2
Application number	US-201515321189-A
Country	US
Kind code	B2
Filing date	Jan 14, 2015
Priority date	Jun 25, 2014
Publication date	Dec 3, 2019
Grant date	Dec 3, 2019

Abstract

A high strength and toughness seamless steel tube for an automobile airbag, comprising the following elements, by wt %: C: 0.05-0.15%; Si: 0.1-0.45%; Mn: 1.0-1.9%; Ni: 0.1-0.6%; Cr: 0.05-1.0%; Mo: 0.05-0.2%; Cu: 0.05-0.50%; Al: 0.015-0.060%; Nb: 0.02-0.1%; V: 0.02-0.15%; and the balance being Fe and other inevitable impurities. A method for manufacturing the seamless steel tube comprises the steps: (1) heating a tube blank and then soaking; (2) hot piercing, reducing the diameter and the wall thickness of the tube blank with a stretch reducer and then cooling naturally; (3) annealing, pickling, phosphating and saponifying; (4) cold working to obtain a finished product size; and (5) carrying out stress relief annealing treatment.

First claim

What is claimed is:

1. A high strength and high toughness seamless steel tube for an automobile air bag, comprising the following elements, by weight:
C: 0.05-0.15%; Si: 0.1-0.45%; Mn: 1.0-1.9%; Ni: 0.1-0.6%; Cr: 0.05-1.0%; Mo: 0.05-0.2%; Cu: 0.05-0.50%; Al: 0.015-0.060%; Nb: 0.02-0.1%; V: 0.02-0.15%; the balance of Fe and inevitable impurities, wherein the steel tube has a tensile strength of ≥850 MPa, a low-temperature impact absorption power at −60° C. of ≥15 J, and an elongation of ≥8%, and wherein the steel tube is manufactured without quenching and tempering.

2. The high strength and high toughness seamless steel tube for the automobile air bag of claim 1 , further comprising ≤0.005 wt % of B element.

3. The high strength and high toughness seamless steel tube for the automobile air bag of claim 1 , wherein it has a wall thickness of ≥1.5 mm.

4. The high strength and high toughness seamless steel tube for the automobile air bag of claim 1 , wherein it has an outer diameter of 15-50 mm.

5. The high strength and high toughness seamless steel tube for the automobile air bag of claim 1 , wherein it has a microstructure of ferrite+lower bainite.

6. A method of producing the high strength and toughness seamless steel tube for an automobile air bag of claim 1 , comprising the following steps:
(1) heating a tube blank and then soaking;
(2) hot piercing, reducing the diameter and the wall thickness of the tube blank with a stretch reducer and then cooling naturally;
(3) annealing, pickling, phosphating and saponifying;
(4) cold working to obtain a finished product size; and
(5) carrying out stress relief annealing treatment.

7. The method of producing the high strength and toughness seamless steel tube for an automobile air bag of claim 6 , wherein, in the above step (1), the tube blank is heated to 1220-1260° C. and is soaked for 10-20 minutes.

8. The method of producing the high strength and toughness seamless steel tube for an automobile air bag of claim 6 , wherein, in the above step (4), the cold working is carried out by cold drawing or cold rolling.

9. The method of producing the high strength and toughness seamless steel tube for an automobile air bag of claim 6 , wherein, in the above step (4), an extension coefficient of each run of the cold working is less than or equal to 1.5.

10. The method of producing the high strength and toughness seamless steel tube for an automobile air bag of claim 9 , wherein, in the above step (4), an extension coefficient of last run of the cold working is larger than or equal to 1.4.

11. The method of producing the high strength and toughness seamless steel tube for an automobile air bag of claim 6 , wherein, in the above step (5), a temperature of the stress relief annealing treatment is 680-780° C. and is held for 10-20 min.

Assignees

• Baoshan Iron & Steel
• Boashan Iron & Steel Co Ltd

Inventors

• Zhai Guoli
• Tian Qingchao
• Wang Qijiang
• Liu Cailing

Classifications

• C21D8/10 Primary

  during manufacturing of tubular bodies · CPC title

• C22C38/46

  with vanadium · CPC title

• C22C38/42

  with copper · CPC title

• C22C38/02

  containing silicon · CPC title

• C22C38/58

  with more than 1.5% by weight of manganese · CPC title