Antifouling composition

Patent metadata

Field	Value
Publication number	US-10494524-B2
Application number	US-201615742326-A
Country	US
Kind code	B2
Filing date	Jul 7, 2016
Priority date	Jul 7, 2015
Publication date	Dec 3, 2019
Grant date	Dec 3, 2019

Abstract

An antifouling thermoplastic polyurethane (TPU) composition has a surface energy of from about 18 to about 26 mJ/m2. The antifouling TPU composition comprises the reaction product of: (A) a polyetherol; (B) a silicone polyol; (C) a chain extender different than said polyetherol and said silicone polyol; and (D) an isocyanate. An article comprising the antifouling TPU composition and having a surface with a 3-dimensional surface topography resistant to adhesion of organisms.

First claim

The invention claimed is:

1. An antifouling thermoplastic polyurethane (TPU) composition having a surface energy of from about 18 to about 26 mJ/m 2 , said antifouling TPU composition comprising the reaction product of:
(A) a polyetherol comprising polytetramethylene ether glycol;
(B) a silicone polyol;
(C) a chain extender different than said polyetherol and said silicone polyol; and
(D) an isocyanate,
wherein reactants (A) through (D) are reacted in the following amounts to form the reaction product:
from about 25 to about 75 weight percent of said polyetherol,
from about 2 to about 25 weight percent of said silicone polyol,
from about 1 to about 15 weight percent of said chain extender, and
from about 10 to about 60 weight percent of said isocyanate, based on the total weight of said reactants (A) through (D) reacted to form said reaction product.

2. An antifouling TPU composition as set forth in claim 1 wherein said silicone polyol comprises siloxane units.

3. An antifouling TPU composition as set forth in claim 2 wherein said silicone polyol has a hydroxyl functionality of 2.

4. An antifouling TPU composition as set forth in claim 1 wherein said silicone polyol has a viscosity at 25° C. of from about 20 to about 200 cSt.

5. An antifouling TPU composition as set forth in claim 1 wherein said polytetramethylene ether glycol has a hydroxyl number of from about 30 to about 1000 mgKOH/g.

6. An antifouling TPU composition as set forth in claim 1 wherein said chain extender is selected from the group of ethylene glycol, propylene glycol, butylene glycol, 1,4-butanediol, butenediol, butynediol, xylylene glycol, amylene glycol, 1,4-phenylene-bis-beta-hydroxy ethyl ether, 1,3-phenylene-bis-beta-hydroxy ethyl ether, bis-(hydroxy-methyl-cyclohexane), hexanediol, thiodiglycol, and combinations thereof.

7. An antifouling TPU composition as set forth in claim 1 wherein said chain extender comprises 1,4-butanediol.

8. An antifouling TPU composition as set forth in claim 1 wherein said isocyanate comprises diphenylmethane diisocyanate (MDI) and/or polymeric diphenylmethane diisocyanate (pMDI).

9. An antifouling TPU composition as set forth in claim 1 wherein said reaction product further comprises a fluorinated polyol reacted into said reaction product.

10. An antifouling TPU composition as set forth in claim 1 further comprising an organometallic antifouling additive.

11. An antifouling TPU composition as set forth in claim 1 further comprising zinc pyrithione.

12. An article which is resistant to adhesion of organisms, said article including an antifouling thermoplastic polyurethane (TPU) composition comprising the reaction product of:
(A) a polyetherol comprising polytetramethylene ether glycol;
(B) a silicone polyol;
(C) a chain extender different than said polyetherol and said silicone polyol; and
(D) an isocyanate,
wherein reactants (A) through (D) are reacted in the following amounts to form the reaction product:
from about 25 to about 75 weight percent of said polyetherol,
from about 2 to about 25 weight percent of said silicone polyol,
from about 1 to about 15 weight percent of said chain extender, and
from about 10 to about 60 weight percent of said isocyanate, based on the total weight of said reactants (A) through (D) reacted to form said reaction product, and
wherein said article has a surface with a 3-dimensional surface topography and a surface energy of from about 18 to about 26 mJ/m 2 .

13. An article as set forth in claim 12 wherein said 3-dimensional surface topography defines a plurality of parallel ridges, with each ridge having a height of from about 0.3 to about 150μπι and spaced about 0.3 to about 150μπι from one another to define valleys between adjacent ridges.

14. An article as set forth in claim 13 wherein a cross-sectional profile of each of said ridges defines a semi-elliptical or a polygonal configuration.

15. An article as set forth in claim 13 wherein said plurality of parallel ridges comprises discontinuous ridges.

16. An article as set forth in claim 13 wherein said plurality of parallel ridges comprises continuous ridges.

17. An article as set forth in claim 12 wherein said 3-dimensional surface topography defines a plurality of peaks, with each peak having a height of from about 0.3 to about 150μπι and spaced about 0.3 to about 150μπι from one another to define valleys.

18. An article as set forth in claim 12 wherein said surface has a surface energy which is from about 1 to about 70% less than the surface energy of a flat surface formed from said antifouling TPU composition.

Assignees

• Basf Se

Inventors

• Kurtoglu Yunus Emre
• Bandyopadhyay Diya

Classifications

• C08G18/4854

  Polyethers containing oxyalkylene groups having four carbon atoms in the alkylene group · CPC title

• C08K5/0091

  Complexes with metal-heteroatom-bonds · CPC title

• C08G18/4804

  Two or more polyethers of different physical or chemical nature · CPC title

• C08G18/6674

  with compounds of group C08G18/3203 · CPC title

• C08G18/61

  Polysiloxanes · CPC title