Laminated glazing

Patent metadata

Field	Value
Publication number	US-10486396-B2
Application number	US-201815923404-A
Country	US
Kind code	B2
Filing date	Mar 16, 2018
Priority date	Dec 16, 2013
Publication date	Nov 26, 2019
Grant date	Nov 26, 2019

Abstract

A laminated glazing comprising a first ply of glazing material and a second ply of glazing material joined by at least one ply of adhesive interlayer material is disclosed. The first ply of glazing material comprises a sheet of glass having a first composition and the second ply of glazing material comprises a sheet of glass having a second composition different to the first composition. The laminated glazing has (i) a peripheral region extending around the periphery of the laminated glazing, the laminated glazing having a surface compression stress in the peripheral region and (ii) an edge compression, wherein the magnitude of edge compression is greater than the magnitude of the surface compression stress in the peripheral region. A method of making such a laminated is provided. A glass sheet suitable for being incorporated in such a laminated glazing is also disclosed.

First claim

The invention claimed is:

1. A laminated glazing comprising a first ply of glazing material and a second ply of glazing material joined by at least one ply of adhesive interlayer material, the first ply of glazing material comprising a sheet of glass having a first composition and the second ply of glazing material comprising a sheet of glass having a second composition different to the first composition, wherein the laminated glazing has (i) a peripheral region extending around the periphery of the laminated glazing, the laminated glazing having a surface compression stress in the peripheral region and (ii) an edge compression, wherein the magnitude of the edge compression is greater than the magnitude of the surface compression stress in the peripheral region, further wherein the second ply of glazing material is a sheet of glass that has been chemically strengthened to have a depth of layer between 10 μm and 60 μm.

2. A laminated glazing according to claim 1 , wherein the second composition is an alkali aluminosilicate glass composition.

3. A laminated glazing according to claim 1 , wherein the second composition includes at least about 6 wt % aluminium oxide.

4. A laminated glazing according to claim 1 , wherein the second composition is (i) 68 mol % SiO 2 , 2.5 mol % Al 2 O 3 , 11 mol % MgO, 3.7 mol % CaO, 14.2 mol % Na 2 O and 0.6 mol % K 2 O, or (ii) wherein the second composition comprises 67-72 mol. % SiO 2 , 1-4 mol. % Al 2 O 3 , 8-15 mol. % MgO, 1-8 mol. % CaO and 12-16 mol. % Na 2 O, or (iii) wherein the second composition comprises (by weight) 58% to 70% SiO 2 , 5% to 15% Al 2 O 3 , 12% to 18% Na 2 O, 0.1% to 5% K 2 O, 4% to 10% MgO and 0% to 1% CaO with the provisos that the sum of the Al 2 O 3 and MgO exceeds 13%, that the sum of the amounts of Al 2 O 3 plus MgO divided by the amount of K 2 O exceeds 3 and that the sum of the Na 2 O plus K 2 O plus MgO exceeds 22%.

5. A laminated glazing according to claim 1 , wherein the peripheral region extends in a band around the entire periphery of the laminated glazing.

6. A laminated glazing according to claim 5 , wherein the band extends a distance from the periphery of the laminated glazing wherein the distance is between 200 mm and 400 mm.

7. A laminated glazing according to claim 1 , wherein the surface compression stress in the peripheral region is between 5 MPa and 25 MPa.

8. A laminated glazing according to claim 1 , wherein the first ply of the laminated glazing has an edge region having a residual edge stress with a net tension and wherein the residual edge stress of the first ply in the edge region has a net tension less than 15 MPa.

9. A laminated glazing according to claim 1 , wherein the edge compression of the first ply is greater than 24 MPa.

10. A laminated glazing according to claim 1 , wherein the first ply of glazing material has a thickness between 1.5 mm and 2.5 mm.

11. A laminated glazing according to claim 1 , wherein the second ply of glazing material is a sheet of glass that has been chemically strengthened to have a surface compressive stress greater than 400 MPa.

12. A laminated glazing according to claim 1 , wherein the second ply of glazing material is a sheet of glass that has been chemically strengthened to have a surface compressive stress between 450 MPa and 675 MPa.

13. A laminated glazing according to claim 1 , wherein the first ply of glazing material has a concave surface and an opposing convex surface, wherein the concave surface faces the ply of adhesive interlayer material.

14. A laminated glazing according to claim 1 , wherein the adhesive interlayer material comprises polyvinyl butyral (PVB), EVA, PVC, EMA, polyurethane, acoustic modified PVB or Uvekol (a liquid curable resin) and/or wherein the adhesive interlayer material has a thickness between 0.3 mm and 2.3 mm.

15. A laminated glazing according to claim 1 , wherein the first composition is a soda-lime-silicate glass composition having a composition by weight of SiO 2 69-74%; Al 2 O 3 0-3%; Na 2 O 10-16%; K 2 O 0-5%; MgO 0-6%; CaO 5-14%; SO3 0-2% and Fe 2 O 3 0.005-2%.

16. A vehicle glazing comprising a laminated glazing according to claim 1 , wherein the vehicle glazing is a windscreen, backlight, side window, or sunroof.

17. A laminated glazing comprising a first ply of glazing material and a second ply of glazing material, the first ply of glazing material having a thickness between 1.5 mm and 2.5 mm and being annealed soda-lime-silica glass, the second ply having a thickness between 0.4 mm and 1.2 mm and being chemically toughened glass, the first ply of glazing material being joined to the second ply of glazing material by at least one ply of adhesive interlayer material, the first ply of glazing material prior to being incorporated in the laminated glazing having a peripheral region having a first residual surface compression stress, wherein when incorporated in the laminated glazing the first ply of glazing material has a second residual surface compression stress in the peripheral region, further wherein the second ply of glazing material is a sheet of glass that has been chemically strengthened to have a depth of layer between 10 μm and 60 μm.

18. A laminated glazing according to claim 17 , wherein the first ply of glazing material after being incorporated in the laminated glazing has a residual surface compression stress in the peripheral region between 10 MPa and 20 MPa.

19. A laminated glazing according to claim 17 , wherein the second ply of glazing material is a sheet of glass that has been chemically strengthened to have a surface compressive stress greater than 400 MPa.

20. A laminated glazing according to claim 17 , wherein the second ply of glazing material has a composition comprising (i) 67-72 mol. % SiO 2 , 1-4 mol. % Al 2 O 3 , 8-15 mol. % MgO, 1-8 mol. % CaO, and 12-16 mol. % Na 2 O; or (ii) wherein the second ply of glazing material has a composition comprising (by weight) 58% to 70% SiO2, 5% to 15% Al 2 O 3 , 12% to 18% Na 2 O, 0.1% to 5% K 2 O, 4% to 10% MgO and 0% to 1% CaO with the provisos that the sum of the A1 2 O 3 and MgO exceeds 13%, that the sum of the amounts of Al 2 O 3 plus MgO divided by the amount of K 2 O exceeds 3 and that the sum of the Na 2 O plus K 2 O plus MgO exceeds 22%; or (iii) wherein the second ply of glazing material has the composition 68 mol % SiO 2 , 2.5 mol % Al 2 O 3 , 11 mol % MgO, 3.7 mol % CaO, 14.2 mol % Na 2 O and 0.6 mol % K 2 O; or (iv) wherein the second ply of glazing material is an alkali aluminosilicate glass composition.

Assignees

• Pilkington Group Ltd

Inventors

• Michetti Massimo
• Pilz Joachim

Classifications

• B32B17/10091

  thermally hardened · CPC title

• B60J1/18

  arranged at the vehicle rear {(optical viewing arrangements integrated in rear windows, e.g. Fresnel lenses B60R1/001)} · CPC title

• C03C3/087

  containing calcium oxide, e.g. common sheet or container glass · CPC title

• B32B17/10889

  shaping the sheets, e.g. by using a mould (B32B17/10816 takes precedence) · CPC title

• B32B17/10036

  comprising two outer glass sheets · CPC title