Catalytic composition and process for the dehydrogenation of butenes or mixtures of butanes and butenes to give 1,3-butadiene

Patent metadata

Field	Value
Publication number	US-10486140-B2
Application number	US-201715783097-A
Country	US
Kind code	B2
Filing date	Oct 13, 2017
Priority date	Dec 28, 2011
Publication date	Nov 26, 2019
Grant date	Nov 26, 2019

Abstract

The present invention relates to a dehydrogenation process starting from reagents selected from single butenes, or mixtures thereof, or mixtures of butenes with butanes, to give 1-3 butadiene using catalytic composition of microspheroidal alumina and an active component containing a mixture comprising Gallium and/or Gallium oxides, Tin and/or Tin oxides, a quantity ranging from 1 ppm to 500 ppm with respect to the total weight of the catalytic composition of platinum and/or platinum oxides, and oxides of alkaline and/or alkaline earth metals.

First claim

The invention claimed is:

1. A process of producing 1-3 butadiene, the process comprising:
diluting a reagent selected from the group consisting of butane, a mixture of butenes, and a mixture of butenes and butanes with an inert product before feeding the diluted reagents to a dehydrogenation section;
dehydrogenating said reagent in said dehydrogenation section in the presence of a catalytic composition which comprises microspheroidal alumina and an active component containing a mixture comprising
at least one of gallium and Gallium oxides,
at least one of tin and tin oxide,
at least one of platinum and a platinum oxide in a quantity ranging from 1 ppm to 500 ppm with respect to the total weight of the catalytic composition, and
at least one oxide of alkaline metal and an alkaline earth metals,
thus producing a gaseous effluent comprising 1-3 butadiene and an exhausted catalytic composition;
sending at least a part of the exhausted catalytic composition to a regenerator;
at least partially regenerating said exhausted catalytic composition in the regenerator by feeding a stream comprising an oxidant selected from air, air poor in oxygen and rich in oxygen;
sending the regenerated catalytic composition back to the dehydrogenation section, and
wherein the dehydrogenation section comprises at least one Fast Riser reactor into whose base the reagents to be dehydrogenated is charged, the reagents are mixed with the at least partially regenerated catalytic composition, and the residence time of the gas phase in the Fast Riser ranges from 0.2 sec. to 5 sec.

2. The process according to claim 1 , wherein in said catalytic composition the alumina is modified with silica.

3. The process according to claim 1 , wherein said catalytic composition comprises gallium oxide, which is selected from the group consisting of Ga 2 O 3 , Ga 2 O and a mixture thereof.

4. The process according to claim 1 , wherein said catalytic composition comprises tin oxide, which is selected from the group consisting of SnO, SnO, and a mixture thereof.

5. The process according to claim 1 , wherein said catalytic composition comprises platinum oxide, which is selected from the group consisting of PtO, PtO 2 and a mixture thereof.

6. The process according to claim 1 , wherein said catalytic composition comprises an oxide of an alkaline metal, which is K 2 O.

7. The process according to claim 1 , wherein the active component is a mixture comprising gallium oxide, an oxide of alkaline metal and/or an alkaline earth metal, tin and platinum in an amount less than 250 ppm, supported on microspheroidal alumina or on microspheroidal alumina modified with silica.

8. The process according to claim 1 , wherein said catalytic composition comprises gallium, gallium oxide, or both in an amount of from 0.05% by weight to 34% by weight with respect to the total weight of the catalytic composition.

9. The process according to claim 1 , wherein said catalytic composition comprises an oxide of an alkaline metal, an oxide of an alkaline earth metal or both in an amount of from 0.1% by weight to 5% by weight with respect to the total weight of the catalytic composition.

10. The process according to claim 8 , wherein said catalytic composition comprises gallium, gallium oxide, or both in an amount of from 0.2% by weight to 3.8% by weight with respect to the total weight of the catalytic composition.

11. The process according to claim 9 , wherein said catalytic composition comprises an oxide of an alkaline metal, an oxide of an alkaline earth metal, or both in an amount of from 0.1% by weight to 3% by weight with respect to the total weight of the catalytic composition.

12. The process according to claim 1 , wherein said catalytic composition comprises tin, tin oxide, or both in an amount of from 0.001% by weight to 1% by weight with respect to the total weight of the catalytic composition.

13. The process according to claim 12 , wherein said catalytic composition comprises tin, tin oxide, or both in an amount of from 0.05% by weight to 0.4% by weight with respect to the total weight of the catalytic composition.

14. The process according to claim 1 , wherein said catalytic composition comprises platinum, platinum oxide, or both in an amount of from 1 to 99 ppm by weight with respect to the total weight of the catalytic composition.

15. The process according to claim 14 , wherein said catalytic composition comprises platinum, platinum oxide, or both in an amount of from 1 to 50 ppm by weight with respect to the total weight of the catalytic composition.

16. The process according to claim 1 , wherein the microspheroidal alumina has a surface area less than or equal to 150 m 2 /g.

17. The process according claim 1 , wherein said catalytic composition comprises silica in an amount of from 0.05% by weight to 5% by weight.

18. The process according to claim 1 , wherein a remaining part of the catalytic composition, which is not sent to the regenerator, is recycled directly to the dehydrogenation section.

19. The process according to claim 1 , wherein the dehydrogenating is conducted at a temperature of from 450° C. to 700° C.

20. The process according to claim 1 , wherein the inert product and the reagents are in a volumetric ratio of from 1 to 9.

21. The process according to claim 1 , wherein the dehydrogenating is conducted at a pressure of from 0.2 atm absolute to 2 atm.

22. The process according claim 1 , wherein the inert product is selected from the group consisting of nitrogen, nitrogen mixed with methane, methane, and methane in the presence of hydrogen.

Assignees

• Versalis Spa

Inventors

• Iezzi Rodolfo
• Manzini Giulio
• Pollesel Paolo
• Del Seppia Alessandro

Classifications

• C07C2523/14

  of germanium, tin or lead · CPC title

• B01J37/0045

  Drying a slurry, e.g. spray drying · CPC title

• C07C2523/63

  with rare earths or actinides · CPC title

• C07C2523/04

  Alkali metals · CPC title

• B01J21/04

  Alumina · CPC title