Shaded zirconia ceramic material and machinable sintered ceramic bodies made therefrom

Patent metadata

Field	Value
Publication number	US-10479729-B2
Application number	US-201815895516-A
Country	US
Kind code	B2
Filing date	Feb 13, 2018
Priority date	Feb 22, 2017
Publication date	Nov 19, 2019
Grant date	Nov 19, 2019

Abstract

Shaded, zirconia ceramic materials are disclosed that are suitable for use in dental applications. Ceramic bodies are made from a zirconia-containing ceramic material and a coloring composition comprising a terbium (Tb)-containing component and a chromium (Cr)-containing component as a coloring agent. The pre-shaded ceramic body is machinable into a dental restoration either as a bisque body or sintered body. A pre-shaded machinable sintered ceramic body may obviate the need for further processing steps, such as shading or sintering, and may be suitable for use in chair-side machining applications, such as in a dentist's office, significantly reducing the time to create a custom finished product.

First claim

We claim:

1. A sintered ceramic body suitable for use in dental restoration applications comprising:
a. a ceramic material that comprises zirconia and
b. a coloring agent comprising 0.002 mass % to 0.65 mass % of terbium (Tb) and chromium (Cr) combined, measured as metal ions,
wherein the mass ratio of Tb to Cr, measured as metal ions, is in the range of approximately 93:7 Tb:Cr to approximately 99.5:0.5 Tb:Cr.

2. The sintered ceramic body of claim 1 , wherein the mass ratio of Tb to Cr, measured as metal ions, is in the range of approximately 94:6 Tb:Cr to approximately 99:1 Tb:Cr.

3. The sintered ceramic body of claim 1 , wherein the coloring agent further comprises at least one element selected from Er, Co, Mn, Pr, V, Ti, Ni, Cu and Zn.

4. The sintered ceramic body of claim 1 , wherein at least one coloring agent further comprises at least one element selected from Er, Co, Mn, and Pr.

5. The sintered ceramic body of claim 1 , comprising between 0.01 mass % and 0.1 mass % Fe.

6. The sintered ceramic body of claim 1 , comprising between 0 mass % and 0.002 mass % Fe ions.

7. The sintered body of claim 1 , having a center cross-sectional geometry that is at least 6 mm.

8. The sintered body of claim 7 , having a CIE L*a*b* ΔE of less than 5 between a cross-sectional center and a perimeter of the sintered ceramic body.

9. The sintered body of claim 7 , having a CIE L*a*b* ΔE of less than 3 between a cross-sectional center and a perimeter of the sintered ceramic body.

10. The sintered ceramic body of claim 1 , wherein the coloring agent comprises
a. 0.002 mass % to 0.3 mass % Tb, measured as Tb ions,
b. 0.000006 mass % to 0.01 mass % Cr, measured as Cr ions,
c. 0.02 mass % to 1.5 mass % Er, measured as Er ions, and
d. 0 mass % to 0.009 mass % Co, measured as Co ions.

11. The sintered ceramic body of claim 1 wherein zirconia comprises between 85 wt % to approximately 100 wt % of the ceramic material.

12. The sintered ceramic body of claim 1 , wherein the ceramic material comprises yttria-stabilized zirconia comprising from 2 mol % to 7 mol % yttria, and 0 mol % to 1 mol % alumina.

13. A ceramic powder suitable for use in dental restoration applications that comprises
a. a ceramic material comprising an yttria-stabilized zirconia that comprises from 2 mol % to 7 mol % yttria, and
b. a coloring agent comprising 0.002 mass % to 0.65 mass % Tb and Cr combined, measured as metal ions,
wherein a mass ratio of Tb ions to Cr ions is in a range of approximately 93:7 Tb:Cr to 99.5:0.5 Tb:Cr, and
c. optionally, a binder.

14. The ceramic powder of claim 13 , comprising 0.002 mass % to 0.3 mass % Tb and Cr combined, measured as metal ions.

15. The ceramic powder of claim 13 , wherein the mass ratio of Tb to Cr, measured as metal ions, is in the range of approximately 94:6 Tb:Cr to approximately 99:1 Tb:Cr.

16. The ceramic powder of claim 13 , wherein the coloring agent further comprises at least one element selected from Er, Co, Mn, Pr, V, Ti, Ni, Cu and Zn.

17. A millable, pre-sintered ceramic body for use in making dental restorations comprising:
a. a ceramic material comprising an yttria-stabilized zirconia having from 2 mol % to 7 mol % yttria,
b. optionally comprising alumina, which if present comprises between 0 mol % and 1 mol %, and
c. a coloring agent comprising 0.03 mass % to 2 mass % of metal-containing components measured as metal ions,

wherein the coloring agent comprises terbium (Tb) and chromium (Cr) which are present in a mass ratio in a range of 93:7 Tb:Cr to 99.5:0.5 Tb:Cr, and
wherein Tb comprises 0.002 mass % to 0.65 mass %.

18. The millable, pre-sintered ceramic body of claim 17 , wherein the coloring agent further comprises at least one metal-containing component having an element selected from Er, Co, Mn, Pr, V, Ti, Ni, Cu and Zn.

19. The millable, pre-sintered ceramic body of claim 17 , wherein the coloring agent comprises terbium (Tb) and chromium (Cr) which are present in a mass ratio in a range of 94:6 Tb:Cr to 99:1 Tb:Cr.

20. The millable, pre-sintered ceramic body of claim 17 , wherein Tb comprises 0.002 mass % to 0.3 mass %.

Assignees

• Glidewell James R Dental Ceramics Inc

Inventors

• Valenti Thomas C
• Recor Kevin Michael

Classifications

• A61K6/818 Primary

  comprising zirconium oxide · CPC title

• A61C13/0022

  Blanks or green, unfinished dental restoration parts · CPC title

• C01P2006/62

  L* (lightness axis) · CPC title

• C01G25/02

  Oxides · CPC title

• C04B2235/3241

  Chromium oxides, chromates, or oxide-forming salts thereof · CPC title