Anti-corrosion and/or passivation composition for metal-containing substrates and methods for making, enhancing, and applying the same

Patent metadata

Field	Value
Publication number	US-10465292-B2
Application number	US-201615288972-A
Country	US
Kind code	B2
Filing date	Oct 7, 2016
Priority date	Oct 7, 2016
Publication date	Nov 5, 2019
Grant date	Nov 5, 2019

Abstract

A method of disposing a corrosion resistant system to a substrate may comprise applying a plating material to the substrate; forming a chemical conversion coating solution by combining a solvent, at least one corrosion inhibitive cation comprising at least one of zinc, calcium, strontium, magnesium, or aluminum, at least one corrosion inhibitive anion comprising at least one of phosphate, molybdate, or silicate, and a complexing agent; and applying the chemical conversion coating solution to the plating material on the substrate.

First claim

What is claimed is:

1. A method of disposing a corrosion resistant system to a substrate, comprising:
applying a plating material to the substrate;
forming a chemical conversion coating solution by combining a solvent, at least one corrosion inhibitive cation comprising at least one of zinc, calcium, strontium, magnesium or aluminum, at least one corrosion inhibitive anion comprising at least one of phosphate, molybdate, or silicate, and a complexing agent;
applying the chemical conversion coating solution to the plating material on the substrate;
drying the chemical conversion coating solution to form a chemical conversion coating, wherein the chemical conversion coating comprises the at least one corrosion inhibitive cation comprising at least one of zinc, calcium, strontium, magnesium or aluminum, the at least one corrosion inhibitive anion comprising at least one of phosphate, molybdate, or silicate, and the complexing agent; and
applying a corrosion resistant coating to the chemical conversion coating, wherein the corrosion resistant coating comprises a corrosion inhibition composition and an application vehicle, and
wherein the corrosion inhibition composition comprises a zinc oxide, a zinc phosphate, a calcium silicate, an aluminum phosphate, a zinc calcium strontium aluminum orthophosphate silicate hydrate, a molybdate compound, and a silicate compound.

2. The method of claim 1 , wherein each of the at least one corrosion inhibitive cation has a concentration in a range of 0.5×10 −3 molar to 0.5 molar in the chemical conversion coating solution.

3. The method of claim 1 , wherein each of the at least one corrosion inhibitive anion has a concentration in a range of 0.5×10 −3 molar to 0.5 molar in the chemical conversion coating solution.

4. The method of claim 3 , wherein the silicate has a concentration in a range of 0.005 molar to 0.02 molar in the chemical conversion coating solution.

5. The method of claim 4 , wherein the forming the chemical conversion coating further comprises adding an organic binder into the chemical conversion coating solution.

6. The method of claim 5 , wherein the organic binder comprises at least one of polyvinyl alcohol, polyvinylpyrrolidone, polyvinyl acetate, or an acrylic.

7. The method of claim 1 , wherein the complexing agent has a concentration in a range of 0.5×10 −3 molar to 0.5 molar in the chemical conversion coating solution.

8. The method of claim 1 , wherein the corrosion inhibitive cation is provided by at least one of zinc chloride, zinc sulfate, zinc nitrate, zinc molybdate, calcium molybdate, magnesium molybdate, zinc silicate, magnesium silicate, calcium silicate, zinc oxide, zinc phosphate, aluminum phosphate, magnesium phosphate, calcium phosphate, zinc calcium strontium aluminum orthophosphate silicate, calcium chloride, calcium sulfate, calcium nitrate, strontium chloride, strontium sulfate, strontium nitrate, aluminum chloride, aluminum sulfate, or aluminum nitrate.

9. The method of claim 1 , wherein the corrosion inhibitive anion is provided by at least one of sodium phosphate, sodium silicate, sodium vanadate, zinc molybdate, calcium molybdate, sodium molybdate, magnesium molybdate, zinc silicate, magnesium silicate, calcium silicate, sodium silicate, zinc phosphate, aluminum phosphate, magnesium phosphate, calcium phosphate, zinc calcium strontium aluminum orthophosphate silicate, sodium nitrite, phosphoric acid, silicic acid, vanadic acid, and/or molybdic acid.

10. The method of claim 1 , wherein the complexing agent comprises at least one of ethylenediaminetetraacetic acid (EDTA), nitrilotracetic acid (NTA), oxalic acid, formic acid, acetic acid, tartaric acid, nicotinic acid, citric acid, or malonic acid.

11. The method of claim 1 , wherein the silicate compound comprises between 10% and 90% by weight of the corrosion inhibition composition.

12. The method of claim 1 , wherein the zinc oxide, the zinc phosphate, the calcium silicate, the aluminum phosphate, and the zinc calcium strontium aluminum orthophosphate silicate hydrate, collectively, comprise between 10% and 90% by weight of the corrosion inhibition composition.

Assignees

• Goodrich Corp

Inventors

• Kryzman Michael A
• Zafiris Georgios S
• Jaworowski Mark R
• Zhang Weilong
• Panza-Giosa Roque
• Manzini Marilea

Classifications

• C09D5/084 Primary

  Inorganic compounds · CPC title

• C25D3/26

  of cadmium · CPC title

• C23F11/18

  using inorganic inhibitors · CPC title

• C23C22/73

  characterised by the process · CPC title

• C23F11/173

  Macromolecular compounds · CPC title