Compositions containing derivatized polyamines

Patent metadata

Field	Value
Publication number	US-10465086-B2
Application number	US-201314436408-A
Country	US
Kind code	B2
Filing date	Oct 16, 2013
Priority date	Oct 16, 2012
Publication date	Nov 5, 2019
Grant date	Nov 5, 2019

Abstract

Disclosed herein are aqueous coating compositions containing an anionically stabilized polymer, one or more derivatized polyamines, and a volatile base. Coating compositions can further include one or more additional copolymers, which may or may not be anionically stabilized, and/or additional additives, including pigments, defoamers, pigment dispersing agents, thickeners, surfactants, and combinations thereof. By incorporating a derivatized polyamine, such as an alkoxylated polyamine, the setting time of the coating compositions can be decreased. Also provided are coatings formed from the coating compositions described herein, as well as methods of forming these coatings.

First claim

What is claimed is:

1. An aqueous composition comprising:
(a) an anionically stabilized copolymer derived from greater than 65% by weight of one or more (meth)acrylate monomers and has a Tg of between −50° C. and 0° C., wherein the anionically stabilized copolymer comprises (i) 10-15% by weight methyl methacrylate; (ii) 50-70% by weight butyl acrylate; (iii) 15-30% by weight 2-ethylhexylacrylate; (iv) greater than 0 to 5% by weight carboxylic acid-containing monomers; (v) 0-5% by weight acrylamide; and (vi) 0-5% by weight acetoacetoxy monomers, wherein the anionically stabilized copolymer does not include a phosphorus-containing monomer;
(b) a derivatized polyalkylene imine or an alkoxylated polyvinylamine in an amount of from greater than 0% to 5% by weight, based on the dry weight of the anionically stabilized polymer; and
(c) a volatile base;
wherein the derivatized polyalkylene imine or alkoxylated polyvinylamine has a degree of nitrogen-derivatization of at least 40%.

2. The composition of claim 1 , wherein the derivatized polyalkylene imine or alkoxylated polyvinylamine has a degree of nitrogen-derivatization between 70% and 90%.

3. The composition of claim 1 , wherein the derivatized polyalkylene imine or alkoxylated polyvinylamine comprises alkoxylated polyethyleneimine (PEI).

4. The composition of claim 1 , wherein the composition includes alkoxylated polyvinylamine.

5. The composition of claim 1 , wherein the derivatized polyalkylene imine or alkoxylated polyvinylamine is present in the composition at between 0.1% by weight and 5% by weight, based on the dry weight of the anionically stabilized copolymer.

6. The composition of claim 1 , wherein the anionically stabilized copolymer includes an acrylic-based copolymer, wherein the acrylic-based copolymer is derived from greater than 90% by weight of one or more (meth)acrylate monomers.

7. The composition of claim 6 , wherein the one or more (meth)acrylate monomers are selected from the group consisting of methyl methacrylate, butyl acrylate, 2-ethylhexylacrylate, and combinations thereof.

8. The composition of claim 1 , wherein the anionically stabilized copolymer is derived from greater than 0% by weight to 5% by weight of one or more carboxylic acid-containing monomers.

9. The composition of claim 1 , wherein the anionically stabilized copolymer is derived from greater than 0% by weight to 35% by weight of one or more additional ethylenically-unsaturated monomers, wherein the one or more additional ethylenically-unsaturated monomers include a vinyl aromatic monomer.

10. A method of producing a coating on a surface comprising
(a) applying to the surface an aqueous coating composition defined by claim 1 ; and
(b) allowing the composition to dry to produce the coating,
wherein the surface is an architectural surface or a roof.

11. The method of claim 10 , further comprising applying a setting accelerator.

12. The composition of claim 1 , wherein the derivatized polyalkylene imine or an alkoxylated polyvinylamine is present in an amount of from 0.05% to 5% by weight, based on the dry weight of the anionically stabilized polymer.

13. The composition of claim 1 , wherein the composition has a tensile strength of greater than 200 psi and an elongation at break of greater than 100% after a drying period of 14 days at room temperature, according to ASTM D-2370.

14. An aqueous composition comprising:
(a) an anionically stabilized copolymer derived from (i) 55-75% by weight butyl acrylate; (ii) 0-25% by weight 2-ethylhexylacrylate; (iii) greater than 0% to 35% by weight of one or more additional ethylenically-unsaturated monomers; (iv) greater than 0 to 5% by weight carboxylic acid-containing monomers; (v) 0-5% by weight acrylamide; and (vi) 0-5% by weight acetoacetoxy monomers and has a Tg of between −50° C. and −10° C., wherein the anionically stabilized copolymer does not include a phosphorus-containing monomer;
(b) a derivatized polyamine in an amount of from greater than 0% to 5% by weight, based on the dry weight of the anionically stabilized polymer, wherein the derivatized polyamine is selected from a derivatized polyalkylene imine or an alkoxylated polyvinylamine; and
(c) a volatile base;
wherein the derivatized polyamine has a degree of nitrogen-derivatization of at least 40%.

15. The composition of claim 1 , wherein the anionically stabilized copolymer has a Tg of from −50° C. to less than −10° C.

16. An aqueous composition comprising:
(a) an anionically stabilized copolymer derived from greater than 65% by weight of one or more (meth)acrylate monomers and has a Tg of between −50° C. and 0° C., wherein the anionically stabilized copolymer comprises (i) 55-75% by weight butyl acrylate; (ii) 0-25% by weight 2-ethylhexylacrylate; (iii) greater than 0% to 35% by weight of one or more additional ethylenically-unsaturated monomers; (iv) greater than 0 to 5% by weight carboxylic acid-containing monomers; (v) 0-5% by weight acrylamide; and (vi) 0-5% by weight acetoacetoxy monomers, wherein the anionically stabilized copolymer and does not include a phosphorus-containing monomer;
(b) a derivatized polyalkylene imine or an alkoxylated polyvinylamine in an amount of from greater than 0% to 5% by weight, based on the dry weight of the anionically stabilized polymer; and
(c) a volatile base;
wherein the derivatized polyalkylene imine or alkoxylated polyvinylamine has a degree of nitrogen-derivatization of at least 40%.

Assignees

• Basf Se

Inventors

• Petrie Randall
• Egan Luke S
• Iyer Sridhar G
• Burghart Armin
• Funk Jeremy

Classifications

• E04B1/66

  Sealings ({damp-proof courses E04B1/644; fire-proof sealings E04B1/948;} additions of anti-leak properties to plaster C04B; bituminous sealing masses C08L95/00; sealings for hydraulic engineering work in general E02B3/16; against ground humidity or ground water E02D31/02; coverings against rain or other precipitations of the atmosphere E04D) · CPC title

• C09D143/02

  Homopolymers or copolymers of monomers containing phosphorus · CPC title

• C09D133/064

  containing anhydride, COOH or COOM groups, with M being metal or onium-cation · CPC title

• C08L33/08 Primary

  Homopolymers or copolymers of acrylic acid esters · CPC title

• C08L33/064

  containing anhydride, COOH or COOM groups, with M being metal or onium-cation · CPC title