Method for making a catalyst comprising a phosphorous modified zeolite and use of said zeolite

Patent metadata

Field	Value
Publication number	US-10464053-B2
Application number	US-201214236750-A
Country	US
Kind code	B2
Filing date	Jul 25, 2012
Priority date	Aug 3, 2011
Publication date	Nov 5, 2019
Grant date	Nov 5, 2019

Abstract

A method to make a phosphorus modified zeolite can include providing a zeolite having at least one ten member ring, making an ion-exchange, steaming the zeolite, and introducing phosphorus on the zeolite. The zeolite can be mixed with one or more binders and shaping additives, and then shaped. A metal can be introduced, and the catalyst can be washed, calcined, and steamed in an equilibration step. The steaming can be at performed at a steam severity (X) of at least about 2. The steaming can be performed at a temperature above 625° C. The catalyst can be used in alcohol dehydration, olefin cracking, MTO processes, and alkylation of aromatics by alcohols with olefins and/or alcohols.

First claim

The invention claimed is:

1. A method to make a phosphorus modified zeolite comprising, in this order:
a) providing a zeolite comprising at least one ten member ring in the structure thereof, and optionally making an ion-exchange;
b) steaming said zeolite;
c) introducing phosphorus on the zeolite to introduce at least 0.1 wt % of the phosphorus, wherein said introduction is performed by incipient wetness impregnation (IWI) whereby the zeolite is contacted with a volume of a solution comprising a phosphorus-containing compound, wherein the volume of the solution is substantially the same as a pore volume of the zeolite;
d) mixing said zeolite of step c) with at least a component selected among one or more binders and shaping additives;
e) shaping said mixture to form a catalyst;
f) introducing an alkaline earth or rare earth metal M to the catalyst in a soluble form, optionally simultaneously with step d);
g) optionally washing the catalyst;
h) optionally calcinating the catalyst;
i) steaming the catalyst made from steps (d) through (h) at a temperature ranging from 420-to 870° C., wherein the catalyst has a volume of pores between 30 Å and 1000 Å of at least 0.25 cc/g.

2. The method of claim 1 , wherein the zeolite of step b) contains less than 100 wppm of sodium.

3. The method of claim 1 , wherein the zeolite of step b) contains less than 100 wppm of sodium, less than 100 wppm of potassium and less than 500 wppm of iron.

4. The method of claim 1 , wherein the zeolite of step b) contains less than 1000 wppm of sodium.

5. The method of claim 1 , wherein the zeolite of step b) contains less than 1000 wppm of sodium, less than 1000 wppm of potassium and less than 1000 wppm of iron.

6. The method of claim 1 , wherein the zeolite s MFI, MTT, FER, MEL, TON, MWW, EUO, or MFS.

7. The method of claim 1 , wherein the zeolite Is ZSM-5 with Si/Al atomic ratio ranging from 11 to 30, and wherein the zeolite has been made without direct addition of organic template.

8. The method of claim 1 , wherein the zeolite is MFI with Si/Al atomic ratio ranging from 30 to 200.

9. The method of claim 1 , wherein the amount of phosphorus on the catalyst is from 0.5 to 30 wt %.

10. The method of claim 1 , wherein the amount of phosphorus on the catalyst is from 0.5 to 9 w %.

11. The method of claim 1 , wherein the alkaline earth or rare earth metal M is Mg, Ca, Sr, Ba, La, Ce, or combinations thereof.

12. A method to make a phosphorus modified zeolite comprising, in this order:
a) providing a zeolite comprising at least one ten member ring in the structure thereof, and optionally making an ion-exchange;
b) optionally steaming said zeolite;
c) introducing phosphorus on the zeolite to introduce at least 0.1 wt % of the phosphorus using incipient wetness impregnation whereby the zeolite is contacted with a volume of a solution comprising a phosphorus-containing compound, wherein the volume of the solution is substantially the same as a pore volume of the zeolite;
d) mixing said zeolite of step c) with at least a component selected among one or more binders and shaping additives;
e) shaping said mixture to form a catalyst;
f) introducing an alkaline earth or rare earth metal M to the catalyst in a soluble form, optionally simultaneously with step d);
g) optionally washing the catalyst;
h) optionally calcinating the catalyst; and
i) steaming the catalyst at a steaming severity (X) of at least about 2, wherein the catalyst has a volume of pores between 30 Å and 1000 Å of at least 0.25 cc/g.

13. The method of claim 12 , wherein the steaming of step i) is performed at a temperature ranging from 700 to 800° C.

14. The method of claim 12 , wherein the steaming of step i) is performed at a temperature ranging from 720 to 800° C.

15. The method of claim 12 , wherein the zeolite of step b) contains less than 100 wppm of sodium.

16. The method of claim 12 , wherein the zeolite of step b) contains less than 100 wppm of sodium, less than 100 wppm of potassium and less than 500 wppm of iron.

17. The method of claim 12 , wherein the zeolite of step b) contains less than 1000 wppm of sodium.

18. The method of claim 12 , wherein the zeolite of step b) contains less than 1000 wppm of sodium, less than 1000 wppm of potassium and less than 1000 wppm of iron.

19. The method of claim 12 , wherein the zeolite is MFI, MTT, FER, MEL, TON, MWW, EUO, or MFS.

20. The method of claim 12 , wherein the zeolite is ZSM-5 with Si/A atomic ratio ranging from 11 to 30, and wherein the zeolite has been made without direct addition of organic template.

21. The method of claim 12 , wherein the zeolite is MFI with Si/Al atomic ratio ranging from 30 to 200.

22. The method of claim 12 , wherein the amount of phosphorus on the catalyst is from 0.5 to 30 wt %.

23. The method of claim 12 , wherein the amount of phosphorus on the catalyst is from 0.5 to 9 w %.

24. The method of claim 12 , wherein the alkaline earth or rare earth metal M is Mg, Ca, Sr, Ba, La, Ce, or combinations thereof.

Assignees

• Nesterenko Nikolai
• Minoux Delphine
• Adam Cindy
• Dath Jean Pierre
• Total Res & Technology Feluy

Inventors

• Nesterenko Nikolai
• Minoux Delphine
• Adam Cindy
• Dath Jean-Pierre

Classifications

• C10G29/22

  containing oxygen as the only hetero atom · CPC title

• C10G3/49

  containing crystalline aluminosilicates, e.g. molecular sieves · CPC title

• B01J2229/36

  Steaming · CPC title

• B01J29/7096

  MTT-type, e.g. ZSM-23, KZ-1, ISI-4 or EU-13 · CPC title

• C07C2527/14

  Phosphorus; Compounds thereof · CPC title