High bulk tissue comprising cross-linked fibers

Patent metadata

Field	Value
Publication number	US-10458067-B2
Application number	US-201816332073-A
Country	US
Kind code	B2
Filing date	Jan 25, 2018
Priority date	Jan 31, 2017
Publication date	Oct 29, 2019
Grant date	Oct 29, 2019

Abstract

The present application relates to a cross-linked fiber and more specifically to fibers that have been subjected to cold caustic extraction (at less than 60° C.) to reduce the hemicellulose content of the fibers by at least 50% and then cross-linked with a cross-linking agent that is curable at a modest temperature, such as less than 160° C. The treated cross-linked fibers preferably have a hemicellulose content that is less than 5% by weight of the fiber. Preferable cross-linking agents are polyamide-epichlorohydrin (PAE) resins, polyamide-polyamine-epichlorohydrin (PPE) resins, and polydiallylamine-epichlorohydrin resins. The cross-linked fibers are readily dispersible in water even without fiberization and generally form webs and products having relatively few knits or knots. As such, the cross-linked fibers of the present invention are well suited for use in the manufacture of tissue webs and products, particularly wet-laid tissue webs and products.

First claim

What is claimed is:

1. A method of manufacturing a cross-linked fiber comprising the steps of: (a) providing a plurality of fibers having a first hemicellulose content, (b) treating a plurality of fibers with a caustic solution at a temperature less than about 60° C. to yield a plurality of caustic extracted fibers having a second hemicellulose content which is at least about 50 percent less than the first hemicellulose content (c) mixing the caustic extracted fibers at a consistency of less than about 15 percent with a cross-linking agent selected from the group consisting of polyamide-epichlorohydrin (PAE) resins, polyamide-polyamine-epichlorohydrin (PPE) resins, and polydiallylamine-epichlorohydrin resins to yield a plurality of treated fibers, and (d) drying the treated fibers at a drying temperature less than about 200160° C. to yield a plurality of cross-linked fibers having a water retention value (WRV) less than about 0.80 g/g.

2. The method of claim 1 wherein the plurality of fibers are eucalyptus hardwood kraft pulp fibers and the second hemicellulose content is less than about 5.0 percent by weight of the fiber.

3. The method of claim 1 further comprising the step of dispersing the fibers in water to form a fiber slurry having a fiber consistency from about 2.0 to about 25 percent prior to the step of treating the plurality of fibers and wherein the caustic solution comprises a caustic agent selected from the group consisting of sodium hydroxide, potassium hydroxide and ammonium hydroxide, and combinations thereof.

4. The method of claim 1 wherein the cross-linking agent is a polyamide-epichlorohydrin (PAE) resin.

5. The method of claim 1 wherein the mixing step (c) is carried out at a consistency less than about 10 percent.

6. The method of claim 1 wherein the step of mixing the caustic extracted fibers with a cross-linking agent is carried out at a fiber consistency of less than about 5.0 percent, a pH from 6.0 to about 8.0 and a temperature less than about 40° C.

7. The method of claim 1 wherein the cross-linking agent is a PAE resin and the amount of PAE resin mixed with the caustic extracted fiber is from about 5 to about 20 kg per metric ton of caustic extracted fiber.

8. The method of claim 1 wherein the drying step is carried out at a drying temperature from about 100 to about 160° C.

9. A fibrous sheet comprising water dispersible cellulosic cross-linked fiber comprising less than about 5.0 percent hemicellulose, a cross-linking agent selected from the group consisting of polyamide-epichlorohydrin (PAE) resins, polyamide-polyamine-epichlorohydrin (PPE) resins, and polydiallylamine-epichlorohydrin resins, wherein the water dispersible cellulosic cross-linked fiber has a water retention value (WRV) less than about 0.80 g/g, and the fibrous sheet has less than 15 percent knits per gram of sheet material.

10. The fibrous sheet of claim 9 wherein the sheet having has less than about 12 percent knits per gram of sheet material.

11. The fibrous sheet of claim 10 having a sheet bulk greater than about 5.0 cc/g.

12. A tissue web comprising at least about 10 percent, by weight of the web, the fibrous sheet of claim 9 , the web having a basis weight from about 20 to about 50 gsm and a sheet bulk of about 5.0 cc/g or greater.

13. The tissue web of claim 12 wherein the cellulosic fibers are eucalyptus hardwood kraft pulp fibers and the cross-linking agent is a PAE resin.

14. The tissue web of claim 12 wherein the web comprises from about 25 to about 45 weight percent water dispersible cellulosic cross-linked fiber.

15. A method of making a high bulk tissue product comprising the steps of: (a) dispersing cross-linked fibers comprising less than about 5.0 percent hemicellulose and a cross-linking agent selected from the group consisting of polyamide-epichlorohydrin (PAE) resins, polyamide-polyamine-epichlorohydrin (PPE) resins, and polydiallylamine-epichlorohydrin resins in water to form an aqueous suspension of cross-linked fibers having a WRV less than about 0.80 g/g; (b) depositing the aqueous suspension of cross-linked fibers on a forming fabric to form a wet tissue web (c) partially dewatering the wet tissue web and (d) drying the partially dewatered tissue web to a consistency of at least about 95 percent to form a dry tissue web; and (e) converting the tissue web to form a tissue product, wherein the tissue product has a basis weight from about 10 to about 50 gsm and a sheet bulk of about 5 cc/g or greater.

16. The method of claim 15 wherein the drying step comprises non-compressively drying the tissue web.

17. The method of claim 15 wherein the drying step comprises transferring the partially dewatered web to a Yankee dryer and further comprising the step of creping the dried web to remove the web from the Yankee dryer surface.

18. The method of claim 15 wherein the cross-linked fibers are not fiberized prior to the dispersing step (a).

19. The method of claim 15 wherein the tissue web has less than about 15 percent knits per gram of web.

20. The method of claim 15 further comprising the steps of dispersing papermaking fibers that have not been subjected to cross-linking in water to form a second aqueous fiber suspension and depositing the second aqueous suspension on a forming fabric along with an aqueous suspension of cross-linked fibers to form a wet tissue web.

Assignees

• Kimberly Clark Co

Inventors

• Zawadzki Michael Andrew
• Goulet Mike Thomas
• Waldroup Donald Eugene
• Uttecht Cathleen Mae
• Lindsay Stephen Michael

Classifications

• D21H27/005

  relating to physical or mechanical properties, e.g. tensile strength, stretch, softness · CPC title

• B31F1/126

  including making of the paper to be crêped · CPC title

• D21H11/20 Primary

  Chemically or biochemically modified fibres · CPC title

• D21F1/0027

  Screen-cloths · CPC title

• D21H27/002

  Tissue paper; Absorbent paper (D21H21/22, D21H27/02, D21H27/20 take precedence; toilet paper A47K10/00; absorbent pads for physiological fluids A61L15/16; making on paper-making machines D21F11/00) · CPC title