Shear cutter with improved wear resistance of WC—Co substrate

Patent metadata

Field	Value
Publication number	US-10456889-B2
Application number	US-201614992706-A
Country	US
Kind code	B2
Filing date	Jan 11, 2016
Priority date	Nov 29, 2011
Publication date	Oct 29, 2019
Grant date	Oct 29, 2019

Abstract

A cutting element may be formed by sintering together a plurality of metal carbide grains and a metal binder to form a substrate, forming at least one binder gradient in the substrate, and mounting an abrasive layer to the substrate at an interface. The concentration of metal binder material may decrease along at least one direction to form the at least one binder gradient.

First claim

What is claimed is:

1. A method of forming a cutting element comprising:
sintering together a plurality of metal carbide grains and a metal binder to form a substrate;
forming at least two binder gradients in the substrate; and
mounting an abrasive layer to the substrate at an interface,
wherein forming the at least two binder gradients comprises forming a binder gradient in a first region extending from the interface to a depth of the substrate wherein the amount of binder material decreases along at least one direction of the longitudinal axis of the substrate to form a first binder gradient, and
wherein forming the at least two binder gradients further comprises forming a binder gradient in a second region from the first region toward the opposite end of the substrate, wherein the second region comprises a radial binder gradient and a constant binder concentration along the longitudinal axis of the substrate to form a second binder gradient.

2. The method of claim 1 , wherein the metal binder material comprises 12% to 14% by weight of the substrate.

3. The method of claim 1 , wherein the metal binder material comprises less than 12% by weight of the substrate.

4. The method of claim 1 , wherein the substrate has a magnetic saturation ranging between 85% and 95%.

5. The method of claim 1 , wherein the substrate has a magnetic saturation ranging between 80% and 95%.

6. The method of claim 1 , wherein the step of forming at least two binder gradients comprises forming a substrate from metal carbide grain layers having decreasing metal carbide grain sizes.

7. The method of claim 1 , wherein the step of forming at least two binder gradients comprises forming a substrate from metal carbide grain layers having decreasing binder content.

8. The method of claim 1 , wherein the step of mounting comprises brazing the abrasive layer to the substrate.

9. The method of claim 6 , wherein the average metal carbide grain size in each layer decreases with increasing distance of the layer from a longitudinal axis of the cutting element.

10. The method of claim 6 , wherein the average metal carbide grain size in each layer increases with increasing distance of the layer from the interface.

11. A method for forming a cutting element comprising:
forming a first layer of metal carbide grains and a metal binder;
forming a second layer of metal carbide grains and a metal binder, the second layer having a higher concentration of carbon than the first layer;
sintering together the first layer and second layer to form a substrate;
forming at least two binder gradients in the substrate; and
mounting an abrasive layer to the substrate at an interface,
wherein forming the at least two binder gradients comprises forming a binder gradient in a first region extending from the interface to a depth of the substrate wherein the amount of binder material decreases along at least one direction of the longitudinal axis of the substrate to form a first binder gradient, and
wherein forming the at least two binder gradients further comprises forming a binder gradient in a second region from the first region toward the opposite end of the substrate, wherein the second region comprises a radial binder gradient and a constant binder concentration along the longitudinal axis of the substrate to form a second binder gradient.

12. The method of claim 11 , wherein the first layer defines a cylindrical core having an axis, and wherein the second layer encloses the outer circumference of the first layer.

13. The method of claim 11 , wherein the second layer is located adjacent to the abrasive layer.

14. A method for forming a cutting element comprising:
forming a first layer of a metal binder and metal carbide grains having a first average grain size;
forming a second layer of a metal binder and metal carbide grains having a second average grain size, wherein the first average grain size is smaller than the second average grain size;
sintering together the first layer and second layer to form a substrate;
forming at least two binder gradients in the substrate; and
mounting an abrasive layer to the substrate at an interface,
wherein forming the at least two binder gradients comprises forming a binder gradient in a first region extending from the interface to a depth of the substrate wherein the amount of binder material decreased along at least one direction of the longitudinal axis of the substrate to form a first binder gradient, and
wherein forming the at least two binder gradients further comprises forming a binder gradient in a second region from the first region toward the opposite end of the substrate, wherein the second region comprises a radial binder gradient and a constant binder concentration along the longitudinal axis of the substrate to form a second binder gradient.

15. The method of claim 14 , wherein the second layer is located adjacent to the abrasive layer.

16. A method of forming a cutting element comprising:
sintering together a plurality of metal carbide grains and a metal binder to form a substrate;
forming at least two binder gradients in the substrate, wherein the concentration of metal binder material decreases along at least one axial direction and at least one radial direction to form the at least two binder gradients, wherein a region of the substrate that comprises a radial binder gradient has a constant binder concentration along the longitudinal axis of the substrate; and
mounting an abrasive layer to the substrate at an interface.

17. The method of claim 16 , wherein the substrate comprises an upper region having an axial binder gradient and a lower region having a radial binder gradient.

Assignees

• Smith International

Inventors

• Belnap John Daniel
• Voronin Georgiy
• Cariveau Peter T

Classifications

• E21B10/46

  characterised by wear resisting parts, e.g. diamond inserts · CPC title

• B24D99/005

  Segments of abrasive wheels · CPC title

• B24D3/06 Primary

  metallic {or mixture of metals with ceramic materials, e.g. hard metals, "cermets", cements} · CPC title

• E21B10/573

  characterised by support details, e.g. the substrate construction or the interface between the substrate and the cutting element · CPC title

• B24D18/0009

  using moulds or presses · CPC title