Method for preparing superabsorbent polymer

Patent metadata

Field	Value
Publication number	US-10450428-B2
Application number	US-201615757041-A
Country	US
Kind code	B2
Filing date	Dec 1, 2016
Priority date	Dec 9, 2015
Publication date	Oct 22, 2019
Grant date	Oct 22, 2019

Abstract

The present invention relates to a method for preparing superabsorbent polymer. According to the preparation method of the present invention, by maintaining the hydrophilicity of superabsorbent polymer and appropriately controlling the crosslinking density, superabsorbent polymer with excellent properties can be prepared though homogeneous surface crosslinking. Thus, superabsorbent polymer with improved absorption speed can be provided without decrease in absorbency under load.

First claim

What is claimed is:

1. A method for preparing superabsorbent polymer comprising the steps of:
performing thermal polymerization or photopolymerization of a monomer composition comprising water-soluble ethylenically unsaturated monomers and a polymerization initiator to form hydrogel polymer;
drying the hydrogel polymer;
grinding the dried polymer; and
mixing the ground polymer with a surface crosslinking agent comprising a compound represented by the following Chemical Formula 1 to conduct a surface crosslinking reaction:

in the Chemical Formula 1,
R is selected from the group consisting of a hydroxy group, a carboxyl group, an amino group and halogen; and
n is an integer of 1 to 5.

2. The method for preparing superabsorbent polymer according to claim 1 , wherein in the Chemical Formula 1, R is a hydroxy group.

3. The method for preparing superabsorbent polymer according to claim 1 , wherein the compound represented by the Chemical Formula 1 is included in the content of 0.02 to 0.5 parts by weight, based on 100 parts by weight of the polymer.

4. The method for preparing superabsorbent polymer according to claim 1 , wherein the surface crosslinking agent further comprises porous silica or clay.

5. The method for preparing superabsorbent polymer according to claim 1 , wherein the centrifuge retention capacity (CRC) of the superabsorbent polymer is 30 g/g to 40 g/g, and the absorbency under pressure (AUP) is 15 g/g to 27 g/g.

6. The method for preparing superabsorbent polymer according to claim 1 , wherein the absorption speed of the superabsorbent polymer measured by vortex test is 10 to 65 seconds.

7. The method for preparing superabsorbent polymer according to claim 1 , wherein the surface crosslinking reaction is conducted at a temperature of 160 to 220° C. for 20 to 120 minutes.

Assignees

• Lg Chemical Ltd

Inventors

• Yang Ye Sol
• Kim Gi Cheul
• Lee Kum Hyoung

Classifications

• C08F2/10

  Aqueous solvent · CPC title

• C08J3/12

  Powdering or granulating · CPC title

• C08J2333/02

  Homopolymers or copolymers of acids; Metal or ammonium salts thereof · CPC title

• C08J3/245

  Differential crosslinking of one polymer with one crosslinking type, e.g. surface crosslinking · CPC title

• C08F2/50

  with sensitising agents · CPC title