Hydrogel contact lenses with lubricious coating thereon

Patent metadata

Field	Value
Publication number	US-10449739-B2
Application number	US-201715704205-A
Country	US
Kind code	B2
Filing date	Sep 14, 2017
Priority date	Sep 20, 2016
Publication date	Oct 22, 2019
Grant date	Oct 22, 2019

Abstract

The invention is generally related to soft contact lenses which comprise a non-silicone hydrogel lens body and a hydrogel coating thereon. The non-silicone hydrogel lens body is composed of a hydrogel material which is free of silicone and comprises at least 50% by mole of repeating units of at least one hydroxyl-containing vinylic monomer. The hydrogel coating comprises a first polymeric material having first reactive functional groups and a hydrogel layer derived from a second polymeric material having second reactive functional groups, and the hydrogel layer is covalently attached onto the anchor layer through linkages each formed between one first reactive functional group and one second reactive functional group. The soft contact lens has a surface lubricity better than the lubricity of the non-silicone hydrogel lens body and has a friction rating of about 2 or lower after 7 cycles of manual rubbing, a water content of from about 10% to about 85% by weight and an elastic modulus of from about 0.2 MPa to about 1.5 MPa when being fully hydrated at room temperature.

First claim

What is claimed is:

1. A soft contact lens, comprising:
a non-silicone hydrogel lens body, wherein the non-silicone hydrogel lens body is composed of a hydrogel material which is free of silicone and comprises at least 50% by mole of repeating units of at least one hydroxyl-containing vinylic monomer; and
a hydrogel coating thereon, wherein the hydrogel coating comprises an anchoring layer of a first polymeric material having first reactive functional groups and a hydrogel layer derived from a second polymeric material having second reactive functional groups, wherein the hydrogel layer is covalently attached onto the anchor layer through linkages each formed between one first reactive functional group and one second reactive functional group,
wherein the soft contact lens has a surface lubricity better than the lubricity of the non-silicone hydrogel lens body and has a friction rating of about 2 or lower after 7 cycles of manual rubbing, a water content of from about 10% to about 85% by weight and an elastic modulus of from about 0.2 MPa to about 1.5 MPa when being fully hydrated.

2. The soft contact lens of claim 1 , wherein the hydrogel coating has a thickness of from about 0.1 μm to about 20 μm.

3. The soft contact lens of claim 2 , wherein the first and second reactive functional groups are different from each other and co-reactive with each other and are selected from the group consisting of carboxyl groups, primary amino groups, secondary amino groups, thiol groups, azetidinium groups, epoxy groups, azlactone groups, aziridine groups, isocyanate groups, vinyl sulfone groups, and combinations thereof.

4. The soft contact lens of claim 3 , wherein said at least one hydroxyl-containing vinylic monomer is selected from the group consisting of hydroxyethyl (meth)acrylate, 2-hydroxypropyl (meth)acrylate, 3-hydroxypropyl (meth)acrylate, glycerol (meth)acrylate, N-2-hydroxyethyl (meth)acrylamide, N-2-hydroxypropyl (meth)acrylamide, N-3-hydroxypropyl (meth)acrylamide, N,N-bis(hydroxyethyl) (meth)acrylamide, N-2,3-dihydroxypropyl (meth)acrylamide, N-tris(hydroxymethyl)methyl (meth)acrylamide, vinyl alcohol, allyl alcohol, and combinations thereof.

5. The soft contact lens of claim 3 , wherein the hydrogel material is a crosslinked product of a water-soluble, actinically-crosslinkable polyvinyl alcohol prepolymer which comprises:
at least 60% by mole of repeating units of vinyl alcohol;
repeating units of formula (I); and

in which:
R 3 can be hydrogen or a C 1 -C 6 alkyl group;
R 4 is a C 1 -C 6 alkylene divalent radical;
R 5 is hydrogen or C 1 -C 6 alkyl;
R 6 is an ethylenically unsaturated group of

in which q1 and q2 independently of each another are zero or one, and R 7 and R 8 independently of one another are a C 2 -C 8 alkylene divalent radical, R 9 is C 2 -C 8 alkenyl.

6. The soft contact lens of claim 1 , wherein the first reactive functional groups are carboxyl groups and the second reactive functional groups are azetidinium groups, wherein the first polymeric material is a polyanionic polymer which is a homo- or co-polymer of at least one carboxyl-containing acrylic monomer selected from the group consisting of acrylic acid, methacrylic acid, ethylacrylic acid, 2-acrylamidoglycolic acid, 2-methacrylamidoglycolic acid, and combinations thereof, wherein the hydrogel layer is covalently attached onto the anchoring layer of the polyanionic polymer through linkages each formed between one carboxyl group and one azetidinium group.

7. The soft contact lens of claim 6 , wherein the polyanionic polymer is poly(acrylic acid) (PAA), poly(methacrylic acid) (PMAA), poly(acrylic acid-co-methacrylic acid) (pAA-pMAA), poly(ethylacrylic acid) (PEAA), poly(acrylic acid-co-ethylacrylic acid) (pAA-pEAA), poly(methacrylic acid-co-ethylacrylic acid) (pMAA-pEAA), poly[2-acrylamidoglycolic acid], poly[2-methacrylamidoglycolic acid], or a combination thereof.

8. The soft contact lens of claim 7 , wherein the second polymeric material is a water-soluble hydrophilic polymeric material comprising
(i) from about 20% to about 95% by weight of first polymer chains derived from a polyamidoamine-epichlorohydrin or a poly(2-oxazoline-co-ethyleneimine)-epichlorohydrin,
(ii) from about 5% to about 80% by weight of hydrophilic moieties and/or second polymer chains,
wherein each of the hydrophilic moieties is derived from at least one first hydrophilicity-enhancing agent having at least one reactive functional group selected from the group consisting of primary amino group, secondary amino group, carboxyl group, thiol group, and combinations thereof, wherein the hydrophilic moieties are covalently attached to the first polymer chains through one or more covalent linkages each formed between one azetidinium group and one primary or secondary amino, carboxyl or thiol group of the first hydrophilicity-enhancing agent,
wherein each of the second polymer chains is derived from at least one second hydrophilicity-enhancing agent having at least one reactive functional group selected from the group consisting of primary amino group, secondary amino group, carboxyl group, thiol group, and combinations thereof, wherein the second polymer chains are covalently attached to the first polymer chains through one or more covalent linkages each formed between one azetidinium group and one primary amino, secondary amino, carboxyl or thiol group of the second hydrophilicity-enhancing agent, and
(iii) azetidinium groups which are parts of the first polymer chains or pendant or terminal groups covalently attached to the first polymer chains.

9. The soft contact lens of claim 8 , wherein the second hydrophilicity-enhancing agent is: a polyethylene glycol having one sole primary or secondary amino, carboxyl or thiol group; a polyethylene glycol with two terminal primary or secondary amino, carboxyl and/or thiol groups; a multi-arm polyethylene glycol with one or more primary or secondary amino, carboxyl and/or thiol groups; a polyethylene glycol dendrimer with one or more primary or secondary amino, carboxyl and/or thiol groups; or a polymerization product of a composition comprising (1) about 60% or less by weight of one or more reactive vinylic monomers and (2) one or more non-reactive hydrophilic vinylic monomers,
wherein said one or more reactive vinylic monomers are vinylic monomers having a carboxyl, primary amino, or secondary amino group,
wherein said one or more non-reactive vinylic monomers are selected from the group consisting of a phosphorylcholine-containing vinylic monomer, (meth)acrylamide, N,N-dimethyl (meth)acrylamide, N-vinylpyrrolidone (NVP), N-vinyl formamide, N-vinyl acetamide, N-vinyl isopropylamide, N-vinyl-N-methyl acetamide, N,N-dimethylaminoethyl (meth)acrylate, N,N-dimethylaminopropyl (meth)acrylamide, glycerol (meth)acrylate, N-2-hydroxyethyl (meth)acrylamide, N-2-hydroxypropyl (meth)acrylamide, N-3-hydroxypropyl (meth)acrylamide, N,N-bis(hydroxyethyl) (meth)acrylamide, N-2,3-dihydroxypropyl (meth)acrylamide, N-tris(hydroxymethyl)methyl (meth)acrylamide, N-methyl-3-methylene-2-pyrrolidone, 1-ethyl-3-methylene-2-pyrrolidone, 1-methyl-5-methylene-2-pyrrolidone, 1-ethyl-5-methylene-2-pyrrolidone, 5-methyl-3-methylene-2-pyrrolidone, 5-ethyl-3-methylene-2-pyrrolidone, 2-hydroxyethyl (meth)acrylate, hydroxypropyl (meth)acrylate, C 1 -C 4 -alkoxy polyethylene glycol (meth)acrylate having a weight average molecular weight of up to 1500 Daltons, allyl alcohol, vinyl alcohol, and combinations thereof.

10. The soft co

Assignees

• Novartis Ag

Inventors

• Qiu Yongxing
• Pruitt John Dallas
• Nelson Jared

Classifications

• B29D11/00923

  on lens surfaces for colouring or tinting (printing or marking in general B41M) · CPC title

• C08F220/58

  containing oxygen in addition to the carbonamido oxygen {, e.g. N-methylolacrylamide, N-(meth)acryloylmorpholine} · CPC title

• C08F220/20

  of polyhydric alcohols or phenols {, e.g. 2-hydroxyethyl (meth)acrylate or glycerol mono-(meth)acrylate} · CPC title

• B29D11/00067 Primary

  Hydrating contact lenses · CPC title

• G02B1/043

  Contact lenses · CPC title