Method for achieving a stress profile in a glass

Patent metadata

Field	Value
Publication number	US-10442730-B2
Application number	US-201414540328-A
Country	US
Kind code	B2
Filing date	Nov 13, 2014
Priority date	Nov 25, 2013
Publication date	Oct 15, 2019
Grant date	Oct 15, 2019

Abstract

A method for generating various stress profiles for chemically strengthened glass. An alkali aluminosilicate glass is brought into contact with an ion exchange media such as, for example, a molten salt bath containing an alkali metal cation that is larger than an alkali metal cation in the glass. The ion exchange is carried out at temperatures greater than about 420° C. and at least about 30° C. below the anneal point of the glass.

First claim

The invention claimed is:

1. A method of strengthening an alkali aluminosilicate glass comprising first metal cations and having an anneal point, the method comprising:
a. immersing the alkali aluminosilicate glass in a molten salt bath, the molten salt bath comprising at least one salt of a second metal, wherein cations of the second metal are larger than the first metal cations;
b. ion exchanging the cations of the second metal from the molten salt bath for the first metal cations in the alkali aluminosilicate glass at a temperature of greater than about 420° C. and at least about 30° C. less than the anneal point, wherein ion exchanging forms a region of compressive stress, the region extending from a surface of the glass to a depth of layer of at least 40 μm into the glass, and wherein a compressive stress at a first depth is at least about 70% of a compressive stress at the surface, the first depth being between about 30% and about 70% of the depth of layer, and the compressive stress at the first depth is less than the compressive stress at the surface and is a buried peak.

2. The method of claim 1 , wherein the first metal cations are sodium cations and the second cations are at least one of potassium cations, rubidium cations, or silver cations.

3. The method of claim 2 , wherein the molten salt bath comprises at least one of potassium sulfate and potassium nitrate.

4. The method of claim 3 , wherein the molten salt bath further comprises up to about 10 wt % of at least one sodium salt.

5. The method of claim 1 , wherein the compressive stress at the surface is at least about 100 MPa.

6. The method of claim 1 , wherein the first depth is about 25 μm.

7. The method of claim 6 , wherein the compressive stress at the first depth is at least about 350 MPa.

8. The method of claim 6 , wherein the alkali aluminosilicate glass has a retained strength of at least about 200 MPa.

9. The method of claim 6 , wherein ion exchanging the alkali aluminosilicate glass comprises ion exchanging the alkali aluminosilicate glass for a period ranging from about 0.5 hours to about 8 hours.

10. The method of claim 1 , wherein the alkali aluminosilicate glass comprises at least about 50 mol % SiO 2 and at least about 11 mol % Na 2 O, and wherein the compressive stress at the surface is at least about 900 MPa.

11. The method of claim 10 , wherein the alkali aluminosilicate glass further comprises Al 2 O 3 and at least one of B 2 O 3 , K 2 O, MgO and ZnO, and wherein −340+27.1·Al 2 O 3 −28.7·B 2 O 3 +15.6·Na 2 O−61.4·K 2 O+8.1·(MgO+ZnO)≥0 mol %.

12. The method of claim 1 , wherein the alkali aluminosilicate glass comprises at least about 50 mol % SiO 2 ; from about 9 mol % to about 22 mol % Al 2 O 3 ; from about 3 mol % to about 10 mol % B 2 O 3 ; from about 9 mol % to about 20 mol % Na 2 O; from 0 mol % to about 5 mol % K 2 O; and at least about 0.1 mol % MgO, ZnO, or combinations thereof, wherein 0≤MgO≤6 and 0≤ZnO≤6 mol %; and, optionally, at least one of CaO, BaO, and SrO, wherein 0 mol %≤CaO+SrO+BaO≤2 mol %.

13. The method of claim 1 , wherein the alkali aluminosilicate glass comprises: at least about 50 mol % SiO 2 ; at least about 10 mol % R 2 O, wherein R 2 O comprises Na 2 O; Al 2 O 3 , wherein −0.5 mol %≤Al 2 O 3 (mol %)−R 2 O(mol %)≤2 mol %; and B 2 O 3 , and wherein B 2 O 3 (mol %)−(R 2 O(mol %)−Al 2 O 3 (mol %))≥4.5 mol %.

14. The method of claim 13 , wherein the alkali aluminosilicate glass has a zircon breakdown temperature that is equal to the temperature at which the glass has a viscosity of greater than about 40 kPoise and comprises: at least about 50 mol % SiO 2 ; at least about 10 mol % R 2 O, wherein R 2 O comprises Na 2 O; Al 2 O 3 ; and B 2 O 3 , wherein B 2 O 3 (mol %)−(R 2 O(mol %)−Al 2 O 3 (mol %))≥4.5 mol %.

15. The method of claim 1 , wherein the alkali aluminosilicate glass comprises at least about 4 mol % P 2 O 5 , wherein (M 2 O 3 (mol %)/R x O(mol %))<1, wherein M 2 O 3 =Al 2 O 3 +B 2 O 3 , and wherein R x O is the sum of monovalent and divalent cation oxides present in the alkali aluminosilicate glass.

16. The method of claim 1 , wherein the glass has a thickness of up to about 1.5 mm.

17. The method of claim 1 , further comprising:
a. immersing the alkali aluminosilicate glass in a second molten salt bath, the second molten salt bath comprising at least one salt of a third metal, wherein cations of the third metal are larger than the first metal cations and the cations of the second metal; and
b. ion exchanging the cations of the third metal from the second molten salt bath for at least one of the first metal cations and the cations of the second metal in the alkali aluminosilicate glass at a temperature of greater than about 420° C. and at least about 30° C. less than the anneal point, wherein ion exchanging in the second molten salt bath forms a surface region comprising the cations of the third metal.

18. The method of claim 17 , wherein the second molten salt bath is substantially free of the first metal cations.

19. The method of claim 17 , wherein the third metal is cesium or rubidium.

20. The method of claim 1 , further comprising:
a. immersing the alkali aluminosilicate glass in a second molten salt bath, the second molten salt bath comprising at least one salt of the second metal; and
b. ion exchanging the cations of the second metal from the second molten salt bath for the first metal cations in the alkali aluminosilicate glass at a temperature of less than or equal to about 420° C., wherein the surface compressive stress is formed by ion exchanging in the second molten salt bath that creates a maximum compressive stress at the surface.

21. The method of claim 20 , wherein the second molten salt bath is substantially free of the first metal cations.

22. The method of claim 21 , wherein the first metal cations are sodium cations.

23. The Method of claim 1 , wherein the compressive stress at the first depth is at least about 90% of the compressive stress at the surface.

24. The Method of claim 1 , wherein the first depth is between about 40% and about 70% of the depth of layer.

25. The Method of claim 1 , wherein the first depth is between about 40% and about 60% of the depth of layer.

26. The Method of claim 1 , wherein the first depth is between about 30% and about 35% of the depth of layer.

Assignees

• Corning Inc

Inventors

• Allan Douglas Clippinger
• Guo Xiaoju
• Hu Guangli
• Peng Gaozhu

Classifications

• C03C21/002 Primary

  to perform ion-exchange between alkali ions (C03C21/005 takes precedence) · CPC title

• C03C21/005

  to introduce in the glass such metals or metallic ions as Ag, Cu · CPC title

• C03C4/18

  for ion-sensitive glass · CPC title

• Y02P40/50

  Glass production, e.g. reusing waste heat during processing or shaping · CPC title

• C03C3/093

  containing zinc or zirconium · CPC title