Solution for forming layer that contains solid electrolyte for all-solid-state alkali metal secondary batteries, coated active material particles, electrode, all-solid-state alkali metal secondary battery and method for manufacturing same

Patent metadata

Field	Value
Publication number	US-10439198-B2
Application number	US-201415026817-A
Country	US
Kind code	B2
Filing date	Sep 30, 2014
Priority date	Oct 3, 2013
Publication date	Oct 8, 2019
Grant date	Oct 8, 2019

Abstract

A forming solution for forming a layer containing a solid electrolyte for an all-solid-state alkali metal secondary battery comprising a component derived from A2S and MxSy (A is selected from Li and Na; M is selected from P, Si, Ge, B, Al and Ga; and x and y are a number that gives a stoichiometric ratio in accordance with a species of M) as a starting material for manufacturing the solid electrolyte, a nonpolar organic solvent and a polar organic solvent having a polarity value higher than that of the nonpolar organic solvent by 0.3 or more.

First claim

What is claimed is:

1. A forming solution for forming a layer containing a solid electrolyte for an all-solid-state alkali metal secondary battery comprising a component derived from A 2 S and M x S y (A is selected from Li and Na; M is selected from P, Si, Ge, B, Al and Ga; and x and y are a number that gives a stoichiometric ratio in accordance with a species of M) as a starting material for manufacturing the solid electrolyte, a nonpolar organic solvent and a polar organic solvent having a polarity value higher than that of the nonpolar organic solvent by 0.3 or more,
wherein the nonpolar organic solvent has a polarity value of less than 0.5, and the polar organic solvent has a polarity value of 0.5 or more,
wherein the nonpolar organic solvent is selected from hydrocarbons having a carbon number of 5 to 10, and the polar organic solvent is selected from aliphatic alcohols having a carbon number of 1 to 4, formamide, formamide substituted with an alkyl group having a carbon number of 1 to 4, and hydrazine-based compounds, and
wherein a content of the nonpolar organic solvent and the polar organic solvent is set to be 100 to 800 parts by weight respectively relative to a sum of 100 parts by weight of A 2 S and M x S y .

2. The forming solution for forming a layer containing a solid electrolyte for an all-solid-state alkali metal secondary battery of claim 1 , comprising a component derived from Li 2 S and M x S y (M is selected from P, Si, Ge, B, Al and Ga; and x and y are a number that gives a stoichiometric ratio in accordance with a species of M) as a starting material for manufacturing the solid electrolyte, the nonpolar organic solvent and the polar organic solvent having a polarity value higher than that of the nonpolar organic solvent by 0.3 or more.

3. The forming solution for forming a layer containing a solid electrolyte for an all-solid-state alkali metal secondary battery of claim 1 , comprising a component derived from Na 2 S and M x S y (M is selected from P, Si, Ge, B, Al and Ga; and x and y are a number that gives a stoichiometric ratio in accordance with a species of M) as a starting material for manufacturing the solid electrolyte, the nonpolar organic solvent and the polar organic solvent having a polarity value higher than that of the nonpolar organic solvent by 0.3 or more.

4. The forming solution for forming a layer containing a solid electrolyte for an all-solid-state alkali metal secondary battery of claim 1 , wherein the forming solution is a solution obtained by adding a starting material into the nonpolar organic solvent to obtain a mixed liquid and subsequently adding the polar organic solvent into the mixed liquid.

5. The forming solution for forming a layer containing a solid electrolyte for an all-solid-state alkali metal secondary battery of claim 1 , wherein the nonpolar organic solvent is n-hexane, and the polar organic solvent is N-methylformamide or ethylenediamine.

6. The forming solution for forming a layer containing a solid electrolyte for an all-solid-state alkali metal secondary battery of claim 1 , wherein the solid electrolyte is Li 2 S-M x S y containing Li 2 S and M x S y at a ratio of 50:50 to 90:10 (molar ratio), and M x S y is P 2 S 5 .

7. The forming solution for forming a layer containing a solid electrolyte for an all-solid-state alkali metal secondary battery of claim 1 , wherein the solid electrolyte is Na 2 S-M x S y containing Na 2 S and M x S y at a ratio of 50:50 to 90:10 (molar ratio), and M x S y is P 2 S 5 .

8. The forming solution for forming a layer containing a solid electrolyte for an all-solid-state alkali metal secondary battery of claim 1 , wherein the layer containing a solid electrolyte is a solid electrolyte layer, a positive electrode, and/or a negative electrode.

9. An all-solid-state alkali metal secondary battery comprising a positive electrode, a negative electrode and a solid electrolyte layer positioned between the positive electrode and the negative electrode, wherein one of the solid electrolyte layer, the positive electrode and the negative electrode is formed by applying of the forming solution of claim 1 and drying.

10. A method for manufacturing an all-solid-state alkali metal secondary battery comprising a positive electrode, a negative electrode and a solid electrolyte layer positioned between the positive electrode and the negative electrode, wherein one of the solid electrolyte layer, the positive electrode and the negative electrode is formed by applying of the forming solution of claim 1 and drying.

11. A coated active material particle for a positive electrode and/or a negative electrode of an all-solid-state alkali metal secondary battery, wherein the coated active material particle includes an active material particle and a layer containing a solid electrolyte that coats a surface along an outer shape thereof, wherein the solid electrolyte contains A 2 S and P 2 S 5 (A is selected from Li and Na), and wherein the solid electrolyte has a peak deriving from PS 4 3− in a Raman spectra of a N-methylformamide (NMF) solution.

12. The coated active material particle of claim 11 , wherein the layer containing the solid electrolyte is layer formed by applying the forming solution for forming a layer containing a solid electrolyte for an all-solid-state alkali metal secondary battery of claim 1 to the surface of the active material particle and drying.

13. An electrode for an all-solid-state alkali metal secondary battery comprising an assembly of a plurality of active material particles and a layer containing a solid electrolyte that coats a surface along an outer shape of individual active material particles and fills a gap between the active material particles, wherein the solid electrolyte contains A 2 S and P 2 S 5 (A is selected from Li and Na), the electrode is a positive electrode and/or a negative electrode, and the solid electrolyte has a peak deriving from PS 4 3− in a Raman spectra of a N-methylformamide (NMF) solution.

14. The electrode of claim 13 , wherein the layer containing the solid electrolyte that fills the gap between the active materials has a thickness of 10 to 1000 nm.

15. The electrode of claim 13 , wherein the electrode is obtained by pressing the coated active material particles.

16. The forming solution for forming a layer containing a solid electrolyte for an all-solid-state alkali metal secondary battery of claim 1 , wherein a content of the nonpolar organic solvent is 100 to 800 parts by weight relative to a sum of 100 parts by weight of Li 2 S-or-Na 2 S and M x S y .

17. The forming solution for forming a layer containing a solid electrolyte for an all-solid-state alkali metal secondary battery of claim 1 , wherein a content of the polar organic solvent is 100 to 800 parts by weight relative to a sum of 100 parts by weight of Li 2 S-or-Na 2 S and M x S y .

18. The forming solution for forming a layer containing a solid electrolyte for an all-solid-state alkali metal secondary battery of claim 4 , wherein the forming solution is manufactured at room temperature.

19. A solid electrolyte for an all-solid-state alkali metal secondary battery, obtained by drying the forming solution for forming a layer containing a solid electrolyte for an all-solid-state alkali metal secondary battery of claim 6 , wherein the solid electrolyte has a X-ray diffraction pattern indicating a presence of more Li 3 PS 4 than Li 2 S.

20. A solid electrolyte for an all-solid-state alkali metal secondary battery, obtained by drying

Assignees

• Japan Science & Tech Agency

Inventors

• Hayashi Akitoshi
• Tatsumisago Masahiro
• Tadanaga Kiyoharu

Classifications

• H01M4/13

  Electrodes for accumulators with non-aqueous electrolyte, e.g. for lithium-accumulators; Processes of manufacture thereof · CPC title

• H01M4/62

  Selection of inactive substances as ingredients for active masses, e.g. binders, fillers · CPC title

• H01M2300/0068

  inorganic · CPC title

• H01M10/052

  Li-accumulators · CPC title

• H01M10/0562 Primary

  Solid materials · CPC title