Laminate, food packaging material, and method for producing laminate

Patent metadata

Field	Value
Publication number	US-10434751-B2
Application number	US-201615556306-A
Country	US
Kind code	B2
Filing date	Mar 11, 2016
Priority date	Mar 11, 2015
Publication date	Oct 8, 2019
Grant date	Oct 8, 2019

Abstract

In a laminate film 1 including a substrate 2, a polyurethane layer 3 formed on the substrate 2, and a metal vapor deposition layer 4 formed on the polyurethane layer 3, a coating liquid is applied on the substrate 2 and dried to produce the polyurethane layer 3. The coating liquid contains a water dispersible polyisocyanate and a polyurethane dispersion containing polyurethane resin produced by reaction of an isocyanate group-terminated prepolymer with a chain extender. The isocyanate group-terminated prepolymer is produced by reaction of a polyisocyanate component including xylylene diisocyanate and/or hydrogenated xylylene diisocyanate and a polyol component including diol having 2 to 6 carbon atoms and an active hydrogen group-containing compound containing a hydrophilic group.

First claim

The invention claimed is:

1. A laminate including a substrate composed of a heat sealable plastic film, a polyurethane layer having gas barrier properties and formed on the substrate, and a metal vapor deposition layer formed on the polyurethane layer,
wherein the polyurethane layer is produced on the substrate by applying and drying, a coating liquid containing a water dispersible polyisocyanate and a polyurethane dispersion containing polyurethane resin produced by reaction of an isocyanate group-terminated prepolymer with a chain extender,
the isocyanate group-terminated prepolymer is produced by reaction of a polyisocyanate component including xylylene diisocyanate and/or hydrogenated xylylene diisocyanate and a polyol component including diol having 2 to 6 carbon atoms and an active hydrogen group-containing compound containing a hydrophilic group.

2. The laminate according to claim 1 , wherein the mass ratio of the resin component in the polyurethane dispersion to the resin component in the water dispersible polyisocyanate is in the range of 2/1 to 99/1.

3. The laminate according to claim 1 , wherein the substrate is a cast polyolefin film.

4. The laminate according to claim 1 , wherein the metal vapor deposition layer is an aluminum layer.

5. A food packaging material including the laminate according to claim 1 .

6. A laminate including a substrate, a polyurethane layer consisting of polyurethane resin, and a metal vapor deposition layer formed in this order,
wherein the substrate is a polyolefin film,
the polyurethane layer contains the following groups relative to 100 mass % of the polyurethane layer as a whole at the percentage below:
(A) xylylene group and/or hydrogenated xylylene group: 10 mass % or more and 45 mass % or less,
(B) alkylene group having 2 to 6 carbon atoms: 0.5 mass % or more and 25 mass % or less,
(C) polyalkylene oxide group: 0.5 mass % or more and 10 mass % or less,
(D) alkylene group containing an ionic group, and/or, arylene group containing an ionic group: 1 mass % or more and 25 mass % or less, and
(E) at least one group selected from the group consisting of an alkylene group having an amino group, an arylene group having an amino group, an alkylene group having a thiol group, and an arylene group having a thiol group: 1 mass % or more and 25 mass % or less.

7. A food packaging material including the laminate according to claim 6 .

8. A method for producing a laminate, the method including:
forming a polyurethane layer consisting of polyurethane resin on a substrate composed of a heat sealable plastic film, and forming a metal vapor deposition layer on the polyurethane layer, thereby producing a laminate,
wherein in the formation of the polyurethane layer,
a coating liquid is applied on the substrate and dried,
the coating liquid contains polyurethane dispersion and water dispersible polyisocyanate,
the polyurethane dispersion contains polyurethane resin produced by reaction of an isocyanate group-terminated prepolymer and a chain extender,
the isocyanate group-terminated prepolymer is produced by reaction of a polyisocyanate component including xylylene diisocyanate and/or hydrogenated xylylene diisocyanates and a polyol component including diol having 2 to 6 carbon atoms and an active hydrogen group-containing compound containing an ionic group.

Assignees

• Mitsui Chemicals Inc

Inventors

• Uchida Takashi
• Kouda Chikako
• Dinh Hoang Yen

Classifications

• B32B2250/03

  3 layers · CPC title

• B32B15/20

  comprising aluminium or copper {(B32B15/016 and B32B15/017 take precedence)} · CPC title

• C23C14/20

  on organic substrates · CPC title

• B05D3/144

  of polymeric substrates · CPC title

• B32B27/40

  comprising polyurethanes · CPC title