Optical fiber for silicon photonics

Patent metadata

Field	Value
Publication number	US-10429589-B2
Application number	US-201815888666-A
Country	US
Kind code	B2
Filing date	Feb 5, 2018
Priority date	Feb 7, 2017
Publication date	Oct 1, 2019
Grant date	Oct 1, 2019

Abstract

An optical fiber for efficient coupling of optical signals to photonic devices. The optical fiber includes a Cl doped tapered core region with a changing outer diameter and changing maximum core refractive index to provide improved coupling at wavelength of interest to photonic devices. The photonic devices may be, for example, silicon photonic devices with an operating wavelength at or near 1310 nm, or at or near 1550 nm.

First claim

What is claimed is:

1. An optical fiber comprising: a length L, a first end face and a second end face, and a MFD at the first end face of the fiber that is different from MFD at another region of the fiber, the fiber further comprising:
(I) a Cl doped silica based core comprising:
(a) a first Cl doped core region having a maximum refractive index Δ 0 such that 0.05%≤Δ 0 ≤0.6% (relative to undoped silica), and an outer core diameter D 0 , wherein 5 microns≤D 0 ≤12 microns, said first Cl doped core region having maximum Cl concentration [Cl], where 0.5 wt. %≤[Cl]≤5 wt. %; and
(b) a Cl doped tapered core region situated adjacent to the first Cl doped core region and to the first fiber end face, the Cl doped tapered core region having a length L 2 where 0.05 mm≤L 2 ≤10 mm, and a maximum core refractive index Δc that decreases along the length of the tapered core region, the tapered region having an outer diameter that changes along the length L 2 and a maximum diameter D max , such that
(i) D max ≥D 0 +3 microns;
(ii) 8 microns≤D max ≤70 microns; and

(II) a silica based cladding surrounding the Cl doped silica based core.

2. A fiber coupler comprising: (i) a housing; (ii) a ferrule situated inside said housing, and an optical fiber of claim 1 situated within said ferrule, said ferrule being structured to receive and support at least a portion of another optical fiber therein.

3. The fiber coupler of claim 2 , further comprising said another fiber such that said optical fiber with Cl doped silica based core and said another optical fiber are situated adjacent to one another within the ferrule, and are optically coupled to one another.

4. The optical fiber having of claim 1 , wherein:
(a) the first Cl doped core region has a length L 1 , and the maximum refractive index Δ 0 of the first Cl doped core region is constant along the length L 1 , and the outer core diameter D 0 of the first Cl doped core region is constant along the length L 1 , wherein L 1 >12 cm, and
(b) said cladding has a constant outer diameter throughout the length L of the optical fiber.

5. The fiber of claim 4 , wherein said optical fiber has MFD at the first end face of the fiber that is different from the MFD at the second end face of the optical fiber.

6. The fiber of claim 4 , wherein the cladding includes fluorine, and the fiber length L is <100 m.

7. The fiber of claim 4 , wherein said core contains at least one region with Cl concentration between 1.1 wt. % and 5 wt. %.

8. The fiber of claim 4 , wherein said core contains at least one region with Cl concentration between 1.4 wt. % and 5 wt. %.

9. The fiber of claim 4 , wherein said tapered core region has a substantially adiabatic taper and satisfies the following condition:

dD
dz

≤

2
⁢

D
λ

⁢

(

n
eff

-

n
cl

)

where D is the core diameter at a position z within the tapered core region, λ is the operating wavelength, n eff is the effective index of the fundamental mode, and n cl is the refractive index of the cladding.

10. The fiber of claim 1 wherein said tapered core region has a taper profile, said taper profile being one of: linear, parabolic, exponential, or gaussian taper.

11. The fiber of claim 4 , wherein L 2 is 0.05 mm≤L 2 ≤1 mm.

12. The fiber of claim 4 , wherein L 2 is 0.2 mm≤L 2 ≤5 mm.

13. The fiber of claim 4 , wherein 10 microns/mm≤(D max −D 0 )/L 2 ≤100 microns/mm.

14. The fiber of claim 4 , wherein 14 microns/mm≤(D max −D 0 )/L 2 ≤86 microns/mm.

15. The fiber of claim 4 , wherein 14 microns/mm≤(D max −D 0 )/L 2 ≤35 microns/mm.

16. The fiber of claim 4 , wherein said tapered core region has a taper profile, said taper profile being one of: linear, parabolic, exponential, or gaussian taper.

17. The fiber of claim 9 , wherein λ=1310 nm.

18. The fiber of claim 9 , wherein λ=1550 nm.

19. The fiber of claim 9 , wherein λ=980 nm.

20. The optical fiber of claim 4 having a maximum core refractive index Δc, wherein 0.0%≤|Δc (at D max )|≤0.3%, relative to undoped silica.

21. The optical fiber of claim 4 having a maximum core refractive index Δc, wherein 0.0%≤|Δc x (at D max )|≤0.2%, relative to undoped silica.

22. The optical fiber of claim 4 having a maximum core refractive index Δc, wherein 0.15%≤[Δ 0 −Δc (at D max )]≤0.37%.

23. The optical fiber of claim 4 , wherein the tapered core region has a taper induced loss of
≤0.2 dB at 1550 nm.

24. The optical fiber of claim 4 , wherein the tapered core region has a taper induced loss of
≤0.2 dB at 1310 nm.

25. The optical fiber of claim 4 , wherein the tapered core region has a taper induced loss of ≤0.1 dB at 1310 nm.

26. A method of forming a low loss taper in a glass optical fiber comprising greater than 0.5 wt % chlorine in a core, the core having an initial mode field diameter MFD (at 1550 nm) and is being surrounded by a cladding, said method comprising the steps of:
expanding the initial core MFD at 1550 nm by at least 3 microns by applying heat to said optical fiber for less than 60 seconds in cumulative duration, thereby diffusing chlorine from the core of the optical fiber into the cladding of the optical fiber;
cleaving said optical fiber at a location where the MFD was expanded by at least 3 microns.

27. The method of claim 26 wherein the step of applying heat is not greater than 45 seconds in cumulative duration.

28. The method of claim 26 wherein the step of applying heat is not greater than 30 seconds in cumulative duration.

29. The method of claim 26 , where the maximum amount of chlorine in the fiber core before the step of applying heat is between 0.5 wt. % and 5 wt. %.

30. The method of claim 26 , where the maximum amount of chlorine in the fiber core before the step of applying heat is between 1.4 wt. % and 5 wt. %.

31. The method of claim 26 wherein the step of applying heat is performed at a temperature Td, and 1500° C.≤Td≤2100° C.

32. The method of claim 26 wherein the step of applying heat is performed at a temperature Td, and 1700° C.≤Td≤2000° C.

33. A system comprising:
a silicon photonic device optically coupled to an optical fiber, said optical fiber comprising:
a Cl doped silica based tapered core region, the tapered core region having an outer diameter Dc that changes along the length L 2 of the tapered core region and a maximum outer diameter D max such that 8 microns≤D max ≤70 microns; the tapered core region further comprising a maximum core refractive index Δc that decreases along the length L 2 of the tapered core region;
and a silica based cladding surrounding the core region.

34. The system of claim 33 , wherein: (i) said silica based clad

Assignees

• Corning Inc

Inventors

• Bookbinder Dana Craig
• Li Ming-Jun
• Powers Dale Robert
• Tandon Pushkar

Classifications

• G02B6/421 Primary

  the intermediate optical component consisting of a short length of fibre, e.g. fibre stub · CPC title

• C03B37/01

  Manufacture of glass fibres or filaments · CPC title

• G02B6/262

  Optical details of coupling light into, or out of, or between fibre ends, e.g. special fibre end shapes or associated optical elements · CPC title

• G02B6/305 Primary

  and having an integrated mode-size expanding section, e.g. tapered waveguide · CPC title

• C03B32/00

  Thermal after-treatment of glass products not provided for in groups {C03B19/00} , C03B25/00 - C03B31/00 {or C03B37/00}, e.g. crystallisation, eliminating gas inclusions or other impurities; {Hot-pressing vitrified, non-porous, shaped glass products} · CPC title