Crosslinkable vinylidene fluoride and trifluoroethylene polymers

Patent metadata

Field	Value
Publication number	US-10414844-B2
Application number	US-201214365451-A
Country	US
Kind code	B2
Filing date	Dec 6, 2012
Priority date	Dec 16, 2011
Publication date	Sep 17, 2019
Grant date	Sep 17, 2019

Abstract

The present invention pertains to semi-crystalline fluoropolymer [polymer (F)] comprising: —recurring units derived from vinylidene fluoride (VDF); —from 10% to 50% by moles [with respect to the total moles of recurring units of polymer (F)] of recurring units derived from trifluoroethylene (TrFE); and —from 0.01% to 10% by moles [with respect to the total moles of recurring units of polymer (F)] of recurring units derived from at least one monomer comprising an azide group [monomer (Az)], to a process for its manufacture, to a crosslinkable composition comprising the same, to a process for crosslinking the same and to a method for manufacturing one of electrical and electronic devices using the same.

First claim

The invention claimed is:

1. A semi-crystalline fluoropolymer (F) comprising:
recurring units derived from vinylidene fluoride (VDF);
from 10% to 50% by moles with respect to the total moles of recurring units of fluoropolymer (F) of recurring units derived from trifluoroethylene (TrFE); and
from 0.01% to 10% by moles with respect to the total moles of recurring units of fluoropolymer (F) of recurring units derived from at least one monomer (Az) comprising an azide group.

2. The fluoropolymer (F) of claim 1 , wherein monomer (Az) is selected from monomers of formula (I):
CX 1 X 2 ═CX—(O) p —R f —(CH 2 ) n —[S(O) q ] s N 3   (I)

wherein: X, X 1 and X 2 , equal to or different from each other, are independently H or F, p is 0 or 1, n is 0 to 4, s is 0 or 1, q is 1 or 2, R f is a divalent (hydro)fluorocarbon group, optionally interrupted by one or more ethereal oxygen atoms.

3. The fluoropolymer (F) of claim 2 , wherein monomer (Az) is selected from monomers of formula (II):
CX 1 X 2 ═CX—O—R f —(CH 2 ) n —[S(O) q ] s N 3   formula (II)

wherein: X, X 1 and X 2 , equal to or different from each other, are independently H or F, n is 0 to 4, s is 0 or 1, q is 1 or 2, R f is a divalent (hydro)fluorocarbon group, optionally interrupted by one or more ethereal oxygen atoms.

4. The fluoropolymer (F) of claim 2 , wherein monomer (Az) is selected from monomers of formula (IV):
CX″ 1 X″ 2 ═CX″—R″ f —(CH 2 ) n″ —[S(O) q″ ] s″ N 3   (IV)

wherein: X″, X″ 1 and X″ 2 , equal to or different from each other, are independently H or F, n″ is 0 to 4, s″ is 0 or 1, q″ is 1 or 2, R″ f is a divalent (hydro)fluorocarbon group, optionally interrupted by one or more ethereal oxygen atoms,
wherein the sp 2 hybridized carbon atom of the terminal double bond ═CX″— is bound to a sp a carbon atom of the R″ f group.

5. The fluoropolymer (F) of claim 4 , wherein monomer (Az) is selected from monomers of formula (V):
CX″ 1 X″ 2 ═CX″—R″ f —(CH 2 ) n″ —S(O) 2 N 3   (V),

wherein: X″, X″ 1 and X″ 2 , equal to or different from each other, are independently H or F, n″ is 0 to 4, R″ f is a divalent (hydro)fluorocarbon group, optionally interrupted by one or more ethereal oxygen atoms,
wherein the sp 2 hybridized carbon atom of the terminal double bond ═CX″— is bound to a sp a carbon atom of the R″ f group.

6. The fluoropolymer (F) of claim 5 , wherein monomer (Az) is selected from monomers of formula (VI):
CX″ 1 X″ 2 ═CX″—R* f —SO 2 N 3   (VI),

wherein: X″, X″ 1 and X″ 2 , equal to or different from each other, are independently H or F, R* f is a divalent perfluoroalkyl group, optionally interrupted by one or more ethereal oxygen atoms.

7. The fluoropolymer (F) of claim 5 , wherein monomer (Az) is selected from monomers of formula (VIII):
CX″ 1 X″ 2 ═CX″—R* f —(CH 2 ) n *—SO 2 N 3   (VIII),

wherein: X″, X″ 1 and X″ 2 , equal to or different from each other, are independently H or F, n* is an integer of 1 to 4, preferably 2 or 4, more preferably n* is 2; R* f is a divalent perfluoroalkyl group, optionally interrupted by one or more ethereal oxygen atoms.

8. The fluoropolymer (F) of claim 5 , wherein monomer (Az) is selected from monomers of formula (X):
CX a 1 X a 2 ═CX a —CF 2 —O—R a f —(CH 2 ) na —SO 2 N 3   (X),

wherein: X″, X″ i and X″ 2 , equal to or different from each other, are independently H or F, na is 0 to 4 and —R a f — is a divalent perfluoroalkyl group having 1 to 6 carbon atoms.

9. The fluoropolymer (F) of claim 4 , wherein monomer (Az) is selected from monomers of formula (XII):
CX″ 1 X″ 2 ═CX″—R″ f —(CH 2 ) n″ —N 3   (XII),

wherein: X″, X″ 1 and X″ 2 , equal to or different from each other, are independently H or F, n″ is 0 to 4, R″ f is a divalent (hydro)fluorocarbon group, optionally interrupted by one or more ethereal oxygen atoms,
wherein the sp 2 hybridized carbon atom of the terminal double bond ═CX″— is bound to a sp a carbon atom of the R″ f group.

10. A process for the manufacture of the fluoropolymer (F) according to claim 1 , said process comprising polymerizing a monomer mixture comprising vinylidene fluoride, trifluoroethylene and at least one monomer (Az).

11. A crosslinkable composition (CC) comprising fluoropolymer (F) according to claim 1 and at least one curing agent in an amount of between 0.5% and 10% by weight relative to fluoropolymer (F).

12. The crosslinkable composition (CC) of claim 11 , further comprising at least one curing agent selected from the group consisting of:
polyallyl derivatives comprising more than one ethylenically unsaturated allylic double bond;
polyvinyl derivatives comprising more than one ethylenically unsaturated vinyl double bond;
bis-olefin (OF) having general formula:

 wherein R 1 , R 2 , R 3 , R 4 , R 5 and R 6 , equal or different from each other, are H or C 1 -C 5 alkyl; Z is a group of formula —(O) e1 -E-(O) e2 —, wherein e1 and e2, equal to or different from each other are independently 1 or 0, and E is a divalent C 1 -C 18 group, optionally containing oxygen atoms, optionally at least partially fluorinated;
triazines substituted with ethylenically unsaturated groups; and
polyazide compounds comprising more than one azide group.

13. A method of forming a cured article, the method comprising crosslinking the fluoropolymer (F) according to claim 1 such that a cured article is formed.

14. A method for manufacturing an electrical or electronic device, the method comprising processing the fluoropolymer (F) of claim 1 , and crosslinking the processed fluoropolymer (F).

15. The method of claim 14 , wherein processing is effected by a solution processing technique selected from the group consisting of ink printing, casting, lithographic process.

16. A method of forming a cured article, the method comprising crosslinking the crosslinkable composition (CC) according to claim 11 , such that a cured article is formed.

17. A method for manufacturing an electrical or electronic device, the method comprising processing the crosslinkable composition (CC) according to claim 11 , and crosslinking the processed crosslinkable composition (CC).

18. The crosslinkable composition (CC) of claim 12 , wherein the polyallyl derivative comprising more than one ethylenically unsaturated allylic double bond is selected from triallyl cyanurate, triallyl isocyanurate (TAIC), tris(diallylamine)-s-triazine, triallyl phosphite, N,N-diallylacrylamide, N,N,N′,N′-tetraallylmalonamide and mixtures thereof.

19. The crosslinkable composition (CC) of claim 12 , wherein the polyvinyl derivative comprising more than one ethylenically unsaturated vinyl double bond is selected from trivinyl isocyanurate, 2,4,6-trivinyl methyltrisiloxane and mixtures thereof.

20. The crosslinkable composition (CC) of claim 12 , wherein the polyazide compound comprising more than one azide group is at least one diazide selected from diazides of formula:
{N 3 —[S(O) qd ] sd } j -J d -{[S(O) qd′ ] sd′ —N 3 } j′

wherein each of j and j′, equal to or different from each other, is 0 or an integer of 1 to 3, provided that j+j′ is of at least 2, each of sd and sd′, equal to or different from each other is independently 0 or 1, each of qd and qd′, equal to or different from each other is independently 1 or 2, and J d is a (hydro)(fluoro)carbon group, optionally containing oxygen atoms, optionally at least partially fluorinated.

Assignees

• Solvay Specialty Polymers It

Inventors

• Marrani Alessio
• Wlassics Ivan
• Tortelli Vito
• Falco Ivan

Classifications

• C08L9/06

  Copolymers with styrene · CPC title

• C08F214/18

  Monomers containing fluorine · CPC title

• B05D1/00

  Processes for applying liquids or other fluent materials (B05D5/00, B05D7/00 take precedence) · CPC title

• C08F214/22 Primary

  Vinylidene fluoride · CPC title

• B05D2506/10

  Fluorinated polymers · CPC title