Biodegradable polyester composition

Patent metadata

Field	Value
Publication number	US-10400100-B2
Application number	US-201715578697-A
Country	US
Kind code	B2
Filing date	Feb 24, 2017
Priority date	Mar 7, 2016
Publication date	Sep 3, 2019
Grant date	Sep 3, 2019

Abstract

A biodegradable polyester composition based on a total weight of the biodegradable polyester composition, including a weight content of tetrahydrofuran, which is 3 ppm-200 ppm; and based on the total weight of the biodegradable polyester composition, a weight content of cyclopentanone is 0.5 ppm-85 ppm is provided. The tetrahydrofuran and cyclopentanone is added into the composition and controlling the content of tetrahydrofuran and the content of cyclopentanone in a certain range in the composition to realize printing performance. Moreover, when a velocity of film blowing is 176 Kg/h, a range of a film thickness is less than 0.2 μm and a relative deviation of the film thickness is less than 1%.

First claim

What is claimed is:

1. A biodegradable polyester composition, comprising the following components in parts by weight:
i) 60 to 100 parts of biodegradable aliphatic-aromatic polyester;
ii) 0 to 40 parts of polylactic acid;
iii) 0 to 35 parts of an organic filler and/or an inorganic filler;
iv) 0 to 1 part of a copolymer which contains epoxy group and is based on styrene, acrylate and/or methacrylate;
wherein, based on a total weight of the biodegradable polyester composition, a weight content of tetrahydrofuran is 3 ppm-200 ppm;
and based on the total weight of the biodegradable polyester composition, a weight content of cyclopentanone is 0.5 ppm-85 ppm.

2. The biodegradable polyester composition according to claim 1 , wherein based on the total weight of the biodegradable polyester composition, the weight content of tetrahydrofuran is 8 ppm-100 ppm; and the weight content of cyclopentanone is 5 ppm-50 ppm.

3. The biodegradable polyester composition according to claim 1 , comprising the following components in parts by weight:
i) 65 to 95 parts of the biodegradable aliphatic-aromatic polyester;
ii) 5 to 35 parts of the polylactic acid;
iii) 5 to 25 parts of the organic filler and/or the inorganic filler;
iv) 0.02 to 0.5 part of the copolymer which contains epoxy group and is based on styrene, acrylate and/or methacrylate.

4. The biodegradable polyester composition according to claim 1 , wherein the weight content of tetrahydrofuran is measured by following method: 1.2000 g of the biodegradable polyester composition is weighed accurately and added into a static headspace test flask; a peak area of tetrahydrofuran in the biodegradable polyester composition is measured by a static headspace method; the content of tetrahydrofuran in the biodegradable polyester composition is calculated according to the peak area of tetrahydrofuran in the biodegradable polyester composition and a standard curve of tetrahydrofuran; and the standard curve of tetrahydrofuran is calibrated by a solution of tetrahydrofuran/methanol;
the weight content of cyclopentanone is measured by following method: 1.2000 g of the biodegradable polyester composition is weighed accurately and added into a static headspace test flask; a peak area of cyclopentanone in the biodegradable polyester composition is measured by the static headspace method; the content of cyclopentanone in the biodegradable polyester composition is calculated according to the peak area of cyclopentanone in the biodegradable polyester composition and a standard curve of cyclopentanone; and the standard curve of cyclopentanone is calibrated by a solution of cyclopentanone/methanol.

5. The biodegradable polyester composition according to claim 1 , wherein the biodegradable aliphatic-aromatic polyester is one or more of poly(butyleneadipate-co-terephthalate) (PBAT), poly(butylenesuccinate-co-terephthalate) (PBST) and poly(butylenesebacate-co-terephthalate) (PBSeT).

6. The biodegradable polyester composition according to claim 1 , wherein the organic filler is selected from a group consisting of natural starch, plasticized starch, modified starch, natural fiber and wood flour, or a mixture thereof; and the inorganic filler is selected from a group consisting of talcum powder, montmorillonite, kaolin, chalk, calcium carbonate, graphite, gypsum, conductive carbon black, calcium chloride, ferric oxide, dolomite, silicon dioxide, wollastonite, titanium dioxide, silicate, mica, glass fiber and mineral fiber, or a mixture thereof.

7. The biodegradable polyester composition according to claim 1 , further comprising 0 to 4 parts of at least one of following substances: plasticizer, release agent, surfactant, wax, antistatic agent, pigment, UV absorbent, UV stabilizer or other plastic additives.

8. The biodegradable polyester composition according to claim 1 , wherein a level of printing performance of the biodegradable polyester composition reaches to level 3 or above.

9. The biodegradable polyester composition according to claim 1 , wherein when an extrusion velocity at film blowing of the biodegradable polyester composition is 176 Kg/h, a range of a film thickness is less than 0.2 μm and a relative deviation of the film thickness is less than 1%.

10. The biodegradable polyester composition according to claim 2 , comprising the following components in parts by weight:
i) 65 to 95 parts of the biodegradable aliphatic-aromatic polyester;
ii) 5 to 35 parts of the polylactic acid;
iii) 5 to 25 parts of the organic filler and/or the inorganic filler;
iv) 0.02 to 0.5 part of the copolymer which contains epoxy group and is based on styrene, acrylate and/or methacrylate.

11. The biodegradable polyester composition according to claim 2 , wherein the weight content of tetrahydrofuran is measured by following method: 1.2000 g of the biodegradable polyester composition is weighed accurately and added into a static headspace test flask; a peak area of tetrahydrofuran in the biodegradable polyester composition is measured by a static headspace method; the content of tetrahydrofuran in the biodegradable polyester composition is calculated according to the peak area of tetrahydrofuran in the biodegradable polyester composition and a standard curve of tetrahydrofuran; and the standard curve of tetrahydrofuran is calibrated by a solution of tetrahydrofuran/methanol;
the weight content of cyclopentanone is measured by following method: 1.2000 g of the biodegradable polyester composition is weighed accurately and added into a static headspace test flask; a peak area of cyclopentanone in the biodegradable polyester composition is measured by the static headspace method; the content of cyclopentanone in the biodegradable polyester composition is calculated according to the peak area of cyclopentanone in the biodegradable polyester composition and a standard curve of cyclopentanone; and the standard curve of cyclopentanone is calibrated by a solution of cyclopentanone/methanol.

12. The biodegradable polyester composition according to claim 3 , wherein the weight content of tetrahydrofuran is measured by following method: 1.2000 g of the biodegradable polyester composition is weighed accurately and added into a static headspace test flask; a peak area of tetrahydrofuran in the biodegradable polyester composition is measured by a static headspace method; the content of tetrahydrofuran in the biodegradable polyester composition is calculated according to the peak area of tetrahydrofuran in the biodegradable polyester composition and a standard curve of tetrahydrofuran; and the standard curve of tetrahydrofuran is calibrated by a solution of tetrahydrofuran/methanol;
the weight content of cyclopentanone is measured by following method: 1.2000 g of the biodegradable polyester composition is weighed accurately and added into a static headspace test flask; a peak area of cyclopentanone in the biodegradable polyester composition is measured by the static headspace method; the content of cyclopentanone in the biodegradable polyester composition is calculated according to the peak area of cyclopentanone in the biodegradable polyester composition and a standard curve of cyclopentanone; and the standard curve of cyclopentanone is calibrated by a solution of cyclopentanone/methanol.

13. The biodegradable polyester composition according to claim 10 , wherein the weight content of tetrahydrofuran is measured by following method: 1.2000 g of the biodegradable polyester composition is weighed accurately and added into a static headspace test flask; a peak area of tetrahydrofuran in the biodegradable polyester composition is measured by a static headspace method; the

Assignees

• Kingfa Science & Technology Co
• Zhuhai Wango Chem Co Ltd
• Tianjin Kingfa New Mat Co Ltd

Inventors

• Lu Changli
• Yuan Zhimin
• Cai Tongmin
• Huang Xianbo
• Zeng Xiangbin
• Jiao Jian
• Yuan Renxu
• Zhong Yuke
• Xiong Kai
• Yang Hui
• Mai Kaijin
• Dong Xueteng

Classifications

• C08L67/04

  Polyesters derived from hydroxycarboxylic acids, e.g. lactones (C08L67/06 takes precedence) · CPC title

• C08L25/14

  with unsaturated esters · CPC title

• C08L3/02

  Starch; Degradation products thereof, e.g. dextrin · CPC title

• C08K5/1535

  Five-membered rings · CPC title

• C08K5/07

  Aldehydes; Ketones · CPC title