Tire comprising a layer of circumferential reinforcement elements

Patent metadata

Field	Value
Publication number	US-10399386-B2
Application number	US-201515319303-A
Country	US
Kind code	B2
Filing date	May 27, 2015
Priority date	Jun 26, 2014
Publication date	Sep 3, 2019
Grant date	Sep 3, 2019

Abstract

Tire comprising a crown reinforcement comprising two working crown layers having unequal axial widths. Layer C of rubber compound is placed between ends of the working crown layers. Second layer S of polymer compound is in contact with at least one working crown layer and the carcass reinforcement, which comprises a layer of circumferential reinforcing elements arranged radially between two working crown layers. Distance d between the end of the axially narrowest working layer and the working layer separated from it by layer C is 1.1ø<d<2.2ø, ø being the diameter of the reinforcing elements, in a meridian plane. Second layer S is made up of a filled elastomer blend having a macro dispersion coefficient Z≥65 and a maximum tan(δ) value less than 0.100. Its complex dynamic shear modulus G*, measured at 10% and 60° C. on the return cycle is greater than 1.35 MPa.

First claim

The invention claimed is:

1. Tire with a radial carcass reinforcement comprising a crown reinforcement formed of at least two working crown layers of reinforcing elements, crossed from one layer to the other making with the circumferential direction angles comprised between 10° and 45° , said at least two working crown layers having unequal axial widths, a layer of rubber compound being placed between at least the ends of said at least two working crown layers, a second layer of polymer compound being in contact with at least one working crown layer and in contact with the carcass reinforcement, said second layer of polymer compound extending axially as far as at least the axial end of the tread, said tread radially capping the crown reinforcement and being connected to two beads by two side walls, the crown reinforcement comprising at least one layer of circumferential reinforcing elements which is arranged radially between two working crown layers, wherein the distance d between the end of the axially narrowest working layer and the working layer separated from the axially narrowest working layer by the layer of rubber compound is such that 1.1ø<d<2.2ø, ø being the diameter of the reinforcing elements of said at least one layer of circumferential reinforcing elements, wherein, in a meridian plane, the thickness of the layer of rubber compound is substantially constant over the axial width comprised between the axially interior end of the layer of rubber compound and the end of the axially narrowest working layer, wherein said second layer of polymer compound is made up of a filled elastomeric compound having a macro dispersion coefficient greater than or equal to 65 and a maximum tan (δ) value, denoted tan(δ)max, less than 0.100 and wherein the complex dynamic shear modulus, measured at 10% and 60° C. on the return cycle, of said second layer of polymer compound is greater than 1.35 MPa and less than 2 MPa.

2. The tire according to claim 1 , wherein the elastomer compound of the second layer of polymer compound comprises, by way of reinforcing filler, at least carbon black used at a content comprised between 10 and 50 phr, and wherein the carbon black has a BET specific surface area greater than 90 m 2 /g.

3. The tire according to claim 1 , wherein the elastomer compound of the second layer of polymer compound comprises a blend of carbon black, of BET specific surface area greater than 90 m 2 /g, and of a white filler, wherein the reinforcing filler is used at a content comprised between 10 and 60 phr, and wherein the ratio of carbon black to white filler is greater than 2.7.

4. The tire according to claim 1 , said tire comprising a third layer of polymer compound axially in contact with the second layer of polymer compound radially between the carcass reinforcement and the radially innermost layer of reinforcing elements of the crown reinforcement, wherein said third layer of polymer compound is made up of a filled elastomer compound having a macro dispersion coefficient greater than or equal to 65 and a maximum tan (δ) value, denoted tan(δ)max, less than 0.100 and wherein the complex dynamic shear modulus, measured at 10% and 60° C. on the return cycle, of said third layer of polymer compound is greater than 1.35 MPa.

5. The tire according to claim 4 , wherein the complex shear modulus, measured at 10% and 60° C. on the return cycle, of the third layer of polymer compound is less than 2 MPa.

6. The tire according to claim 4 , wherein the elastomer compound of the third layer of polymer compound comprises, by way of reinforcing filler, at least carbon black used at a content comprised between 10 and 50 phr, and wherein the carbon black has a BET specific surface area greater than 90 m 2 /g.

7. The tire according to claim 4 , wherein the elastomer compound of the third layer comprises a blend of carbon black, of BET specific surface area greater than 90 m 2 /g, and of a white filler, wherein the reinforcing filler is used at a content comprised between 10 and 60 phr, and wherein the ratio of carbon black to white filler is greater than 2.7.

8. The tire according to claim 4 , wherein the elastomer compound of the third layer of polymer compound comprises, by way of reinforcing filler, at least carbon black used at a content comprised between 10 and 50 phr, and wherein the carbon black has a BET specific surface area greater than or equal to 120 m 2 /g.

9. The tire according to claim 4 , wherein the elastomer compound of the fourth layer comprises a blend of carbon black, of BET specific surface area greater than or equal to 120 m 2 /g, and of a white filler, wherein the reinforcing filler is used at a content comprised between 10 and 60 phr, and wherein the ratio of carbon black to white filler is greater than 2.7.

10. The tire according to claim 1 , wherein the elastic modulus under tension at 10% elongation of the first layer of rubber compound is less than 8 MPa and wherein the maximum value for tan(δ), denoted tan(δ) max , of the first layer of rubber compound is less than 0.100.

11. The tire according to claim 10 , wherein the first layer of rubber compound is an elastomeric compound based on natural rubber or synthetic polyisoprene with a majority of cis-1,4 chains, and possibly at least one other diene elastomer, the natural rubber or the synthetic polyisoprene in case of blending being present in a majority proportion relative to the proportion of the other diene elastomer or elastomers used, and a reinforcing filler composed of:
a) either carbon black with a BET specific surface area greater than 60 m 2 /g,
i. used at a content of between 20 and 40 phr when the carbon black oil absorption number (COAN) is greater than 85,
ii. used at a content comprised between 20 and 60 phr when the carbon black oil absorption number (COAN) is less than 85,

b) or carbon black of BET specific surface area less than 60 m 2 /g, whatever its oil absorption number, used at a content of between 20 and 80 phr,
c) or a white filler of the silica and/or alumina type comprising SiOH and/or AlOH surface functional groups selected from the group formed of precipitated or pyrogenated silicas, aluminas or aluminosilicates or alternatively carbon blacks modified during or after synthesis with BET specific surface area of between 30 and 260 m 2 /g used at a content of between 20 and 80 phr,
d) or a blend of carbon black described at (a) and/or of carbon black described at (b) and/or a white filler described at (c), in which the overall filler content is comprised between 20 and 80 phr.

12. The tire according to claim 1 , said at least two working crown layers each being formed of reinforcing elements inserted between two skim layers of rubber compound, wherein the elastic modulus under tension at 10% elongation of at least one skim layer of at least one working crown layer is less than 8.5 MPa and wherein the maximum value of tan(δ), denoted tan(δ)max, of said at least one skim layer of at least one working crown layer is less than 0.100.

13. The tire according to claim 12 , wherein said at least one skim layer of at least one working crown layer is an elastomer compound based on natural rubber or based on synthetic polyisoprene with a predominance of cis-1,4 chains and possibly at least one other diene elastomer, natural rubber or synthetic polyisoprene in the case of a blend being present at a content that predominates over the content of the other diene elastomer or elastomers used and of a reinforcing filler made up of:
a) either carbon black of BET specific surface area greater than 60 m 2 /g,
i. used at a content of between 20 and 40 phr when the oil absorption number (COAN) of the carbo

Assignees

• Michelin & Cie
• Michelin Rech Tech
• Cie Generale Des Etablissemetns Michelin

Inventors

• Rehab Hichem
• Salgues Nathalie
• Besson Jacques

Classifications

• B60C9/1835 Primary

  Rubber strips or cushions at the belt edges · CPC title

• B60C2001/0075

  Compositions of belt cushioning layers · CPC title

• B60C2001/0066

  Compositions of the belt layers · CPC title

• B60C9/2006

  consisting of steel cord plies only · CPC title

• B60C2009/1878

  with flat cushions or shear layers between the carcass and the belt · CPC title