Incombustible decorative sheet, metal decorative member and method for fabricating a metal decorative member

Patent metadata

Field	Value
Publication number	US-10399301-B2
Application number	US-201715639779-A
Country	US
Kind code	B2
Filing date	Jun 30, 2017
Priority date	Jan 27, 2015
Publication date	Sep 3, 2019
Grant date	Sep 3, 2019

Abstract

A decorative sheet which ensures good incombustibility, processability and weatherability along with weatherability, contamination resistance and solvent resistance. An incombustible decorative sheet having incombustibility includes a weather-resistant resin layer and a fluorine resin layer laminated on a substrate layer in this order, wherein the weather-resistant resin layer is made of a mixture of an acrylic resin and an acrylic resin-based rubber having a ratio by mass between the acrylic resin-based rubber and the acrylic resin within a range of 30:70 to 60:40. The ratio between the fluorine resin layer and the weather-resistant resin layer is within a range of 10:90 to 40:60.

First claim

What is claimed is:

1. An incombustible decorative sheet, comprising:
two or more thermoplastic resin layers laminated on a substrate layer,
an outermost layer of the thermoplastic resin layers being a fluorine resin layer made of a fluorine resin,
an inside layer other than the outermost layer of the thermoplastic resin layers serving as a weather-resistant resin layer made of a mixture of an acrylic resin and an acrylic resin-based rubber having a ratio by mass between the acrylic resin-based rubber and the acrylic resin set within a range of 30:70 to 60:40, and
a design pattern layer with a design pattern thereon and an adhesion layer being provided between the substrate layer and the two or more thermoplastic resin layers,
wherein the two or more thermoplastic resin layers serve as a transparent thermoplastic resin layer having a transparency sufficient to enable the design pattern of the design pattern layer to be visible,
wherein the adhesion layer has two layers including an adhesive layer made of a urethane adhesive that contains an isocyanate compound as a curing agent and has a polyester resin as a main chain, and an anchor layer made of a urethane anchoring agent that contains an isocyanate compound as a curing agent and has an acrylic resin as a main chain, the adhesive layer being disposed at a side of the substrate layer, and
wherein a ratio in thickness between the fluorine resin layer and the weather-resistant resin layer is within a range of 10:90 to 40:60 whereby incombustibility is imparted to the sheet.

2. The incombustible decorative sheet of claim 1 ,
wherein the substrate layer is made of a polyolefin resin with its thickness being from 30 μm to 70 μm, inclusive, and a total thickness of the decorative sheet is from 80 μm to 130 μm, inclusive.

3. The incombustible decorative sheet of claim 1 ,
wherein an ultraviolet absorber is further added to the urethane anchoring agent.

4. The incombustible decorative sheet of claim 1 ,
wherein the adhesion layer is made of a thermal activation type heat-sensitive adhesive.

5. The incombustible decorative sheet of claim 1 ,
wherein the weather-resistant resin layer contains at least one ultraviolet absorber selected from benzotriazole ultraviolet absorbers and triazine ultraviolet absorbers,
wherein a total thickness of the decorative sheet is set at not larger than 200 μm, and,
wherein a total thickness of the two or more thermoplastic resin layers is set at not less than 20 μm to not larger than 80 μm.

6. The incombustible decorative sheet of claim 1 ,
wherein the weather-resistant resin layer constitutes a matte sheet layer to which a matting agent is added,
wherein a thickness of the substrate layer is set at not less than 50 μm to not large than 75 μm,
wherein the thickness of the matte sheet layer is set at not less than 20 μm to not larger than 55 μm, and
wherein the matting agent is made of acrylic-based crosslinked particles having a thermal deformation temperature (JIS K 7207) higher than an acrylic resin constituting the matte sheet layer.

7. The incombustible decorative sheet of claim 6 ,
wherein the acrylic-based crosslinked particles are polymethyl methacrylate-based crosslinked particles containing as a copolymerizing component a hydroxyalkyl acrylate and/or a hydroxyalkyl methacrylate.

8. The incombustible decorative sheet of claim 1 ,
wherein an uneven pattern is formed on the weather-resistant resin layer.

9. The incombustible decorative sheet of claim 1 ,
wherein a constituent fluorine resin of the fluorine resin layer is a polyvinylidene resin.

10. The incombustible decorative sheet of claim 1 ,
wherein the substrate layer is made of a colored polypropylene resin colored by mixing of at least one of an organic pigment and an inorganic pigment.

11. The incombustible decorative sheet of claim 1 ,
wherein the substrate layer is made of a polypropylene resin and has a weight of organic solids of not less than 44 g/m 2 to not larger than 67 g/m 2 .

12. A metal decorative member having incombustibility, comprising the incombustible decorative sheet of claim 1 laminated to a substrate of a metal selected from aluminum, Galvalume, iron, stainless steel and copper.

13. A metal decorative member having incombustibility, comprising an aluminum substrate laminated on the substrate layer side of the incombustible decorative sheet defined in claim 1 through a second adhesive layer, and wherein the second adhesive layer is formed of a reaction-type hot melt adhesive or a two-part curing urethane resin using an isocyanate as a curing agent.

14. The metal decorative member having incombustibility of claim 13 ,
wherein the weight of the reaction-type hot melt adhesive in the second adhesive layer is from 37 g/m 2 to 46 g/m 2 , inclusive.

15. A metal decorative member having incombustibility, comprising:
an anodized film and a coating film layer formed on a metal substrate by baking and finishing in this order and laminating to a substrate layer side of the incombustible decorative sheet of claim 1 through a urethane resin-based adhesive layer.

16. The metal decorative member having incombustibility of claim 15 ,
wherein the coating film resin is an acrylic resin, a melamine resin, a fluorine resin or a mixed resin of two or more thereof.

17. The metal decorative member having incombustibility of claim 15 ,
wherein the solids weight of the urethane resin-based adhesive layer is from 15.0 g/m 2 to 26.4 g/m 2 , inclusive.

18. A metal decorative member having incombustibility, comprising
a composite panel, with a mixed resin layer containing a polyethylene resin and aluminum hydroxide and sandwiched between metal plates laminated to a substrate layer side of the incombustible decorative sheet of claim 1 .

19. A metal decorative member, comprising
an aluminum plate used as a substrate and laminated to a substrate layer side of the incombustible decorative sheet of claim 1 ,
wherein the fluorine resin constituting the fluorine resin layer is a polyvinylidene fluoride resin,
wherein the acrylic resin constituting the weather-resistant resin layer is a polymethyl methacrylate resin and the acrylic resin-based rubber is a polymethyl methacrylate resin-based rubber,
wherein a total thickness of the two or more thermoplastic resins is from 20 μm to 80 μm, inclusive, and,
wherein a thickness of the aluminum plate is from 0.5 mm to 0.8 mm, inclusive.

20. A metal decorative member having incombustibility, comprising
a metal decorative member obtained by laminating, to an aluminum plate, the incombustible decorative sheet of claim 1 , with the metal decorative member being formed after bending.

21. A method for making a metal decorative sheet, comprising
heating at least a portion of the metal decorative member of claim 20 being heated to be bent and subsequently subjecting to bending.

Assignees

• Toppan Printing Co Ltd

Inventors

• Shinmyo Katsuyuki
• Tominaga Takashi

Classifications

• E04F13/002

  made of webs, e.g. of fabrics, or wallpaper, used as coverings or linings (of a number of similar elements carried by a common web E04F13/0862; paperhanging, tapestry work B44C7/00) · CPC title

• B32B2307/712

  Weather resistant · CPC title

• B32B2307/408

  Matt, dull surface · CPC title

• B32B2307/406

  Bright, glossy, shiny surface · CPC title

• B32B2307/3065

  Flame resistant or retardant, fire resistant or retardant · CPC title