Method for producing coated active materials, core, battery and method for producing batteries using the materials

Patent metadata

Field	Value
Publication number	US-10388949-B2
Application number	US-201414471178-A
Country	US
Kind code	B2
Filing date	Aug 28, 2014
Priority date	Feb 28, 2012
Publication date	Aug 20, 2019
Grant date	Aug 20, 2019

Abstract

A method for producing coated active materials includes aqueously coating surfaces of the active materials and subsequently carbonizing the coated particles. A core, a battery and a method for using the materials for batteries are also provided.

First claim

The invention claimed is:

1. A coated core, comprising:
a core material selected from the group consisting of carbon, compounds of carbon and metals, mixtures of carbon and metals, compounds of carbon and metal oxides, mixtures of carbon and metal oxides, particles of lithium salts or lithium oxides, and nanoparticles of silicon, tin, tin oxide, tin dioxide, titanium dioxide and lithium titanates; and
a coating layer of amorphous carbon having a thickness of 2 nm to 500 nm;
said coated core having characteristics of having been obtained by:
applying a polyelectrolyte multilayer alternately including anionic and cationic polyelectrolyte layers to said core material so as to obtain a core material including multiple layers of polyelectrolytes; and
carbonizing said core material including said multiple layers of polyelectrolytes.

2. The core according to claim 1 , wherein said core material is a lithium-ion battery active material.

3. The coated core according to claim 1 , wherein said coated core material is selected from the group consisting of carbon particles, carbon-silicon multilayer particles, carbon-tin multilayer particles, carbon-tin dioxide multilayer particles, carbon-copper multilayer particles, multilayer particles of carbon and metal alloys, nanoparticles of silicon, tin, tin dioxide, titanium dioxide and lithium titanates.

4. The coated core according to claim 1 , wherein said lithium salts or lithium oxides are selected from the group consisting of lithium iron phosphate or lithium oxides including lithium-manganese spinels or mixed oxide systems of lithium plus nickel, cobalt or manganese.

5. The coated core according to claim 3 , wherein at least one of:
said carbon particles are amorphous carbon and/or graphite particles,
said silicon of the carbon-silicon multilayer particles is an amorphous nano-silicon,
said metal of at least one of said carbon-metal multilayer particles or said carbon-metal oxide multilayer particles is an amorphous nanoscale metal including tin, copper, titanium or cobalt, or
said metal oxide of said carbon-metal oxide multilayer particles is an oxide of tin, iron, titanium, manganese, nickel or copper.

6. The coated core according to claim 1 , wherein said coating is an aqueous substrate coating.

7. The coated core according to claim 1 , wherein said polyelectrolytes contain at least one of aliphatic or aromatic rings, heterocycles or carbon nanomaterials.

8. The coated core according to claim 1 , wherein said particles have a median particle diameter of from 200 nm to 150 μm.

9. The coated core according to claim 1 , wherein said particles have a median particle diameter of from 100 nm to 80 μm.

10. The coated core according to claim 1 , wherein said particles have a median particle diameter of from 0.5 μm to 50 μm.

11. The coated core according to claim 1 , wherein said particles have a BET surface area of from 0.5 to 1000 m 2 /g.

12. The coated core according to claim 1 , wherein said particles have a BET surface area of from 1 to 300 m 2 /g.

13. The coated core according to claim 1 , wherein said particles have a BET surface area of from 2 to 100 m 2 /g.

14. A method of producing a coated core, the method comprising the following steps:
providing a core material selected from the group consisting of carbon, compounds of carbon and metals, mixtures of carbon and metals, compounds of carbon and metal oxides, mixtures of carbon and metal oxides, particles of lithium salts or lithium oxides, and nanoparticles of silicon, tin, tin oxide, tin dioxide, titanium dioxide and lithium titanates;
providing a coating layer of amorphous carbon having a thickness of 2 nm to 500 nm;
applying a polyelectrolyte multilayer alternately including anionic and cationic polyelectrolyte layers to the core material so as to obtain a core material including multiple layers of polyelectrolytes; and
carbonizing the core material including the multiple layers of polyelectrolytes.

Assignees

• Sgl Carbon Se

Inventors

• Schweiss Ruediger-Bernd
• Schumann Lea
• Hammer Christian

Classifications

• H01M4/587

  for inserting or intercalating light metals · CPC title

• H01M4/366 Primary

  as layered products · CPC title

• H01M4/62

  Selection of inactive substances as ingredients for active masses, e.g. binders, fillers · CPC title

• H01M2220/20

  Batteries in motive systems, e.g. vehicle, ship, plane · CPC title

• H01M2300/0094

  in the form of layered products, e.g. coatings · CPC title