Composition and method for controlling the wettability of surfaces

Patent metadata

Field	Value
Publication number	US-10377920-B2
Application number	US-201715716686-A
Country	US
Kind code	B2
Filing date	Sep 27, 2017
Priority date	Feb 9, 2012
Publication date	Aug 13, 2019
Grant date	Aug 13, 2019

Abstract

The present invention relates to a composition comprising hedgehog shaped particles, at least one binder, and at least one hydrophobizing agent and/or at least one hydrophilizing agent, a method for controlling the wettability of substrate surfaces using these compositions, as well as a material comprising these compositions.

First claim

The invention claimed is:

1. A coating formulation comprising:
(i) a mixture of at least one binder and hydrophilized hedgehog shaped particles pre-treated and coated with at least one hydrophilizing agent but not a hydrophobizing agent, or
(ii) a mixture of at least one binder, at least one hydrophilizing agent, and hydrophobized hedgehog shaped particles pre-treated and coated with at least one hydrophobizing agent but not a hydrophilizing agent,
wherein the hedgehog shaped particles are composed of a calcium carbonate containing material, wherein the coating formulation is in a form of a solution or dispersion in a liquid medium, wherein the liquid medium is selected from the group consisting of water, alcohol ethers, alcohols, aliphatic hydrocarbons, esters, and any mixture thereof, wherein the binder is selected from the group consisting of a latex binder, a styrene-acrylic latex; a homopolymer or copolymer of acrylic acid and/or methacrylic acid, itaconic acid; an acid ester, ethylacrylate, butyl acrylate, a styrene; an unsubstituted or substituted vinyl chloride, vinyl acetate, ethylene, butadiene, and acrylonitrile; a silicone resin, a water dilutable alkyd resin, an acrylic/alkyd resin, a polyvinyl alcohol, a natural oil, linseed oil, and any mixture thereof, and wherein the at least one hydrophilizing agent in part (i) is, or the hydrophobizing agent and the least one hydrophilizing agent in part (ii) are, present in a total amount of from 0.3 to 2.4 wt %, based on the weight of the hedgehog shaped particles in part (i) and part (ii), respectively.

2. The coating formulation according to claim 1 , wherein the hedgehog shaped particles are composed of aragonitic precipitated calcium carbonate in a form of clusters of needle like crystals.

3. The coating formulation according to claim 1 , wherein the hedgehog shaped particles are clusters and/or aggregates of scalenohedral precipitated calcium carbonate.

4. The coating formulation according to claim 1 , wherein the hedgehog shaped particles have a BET specific surface area of from 1 to 50 m 2 /g, measured using nitrogen and the BET method according to ISO 9277.

5. The coating formulation according to claim 1 , wherein the hedgehog shaped particles have a BET specific surface area of from 2 to 40 m 2 /g, measured using nitrogen and the BET method according to ISO 9277.

6. The coating formulation according to claim 1 , wherein the hedgehog shaped particles have a BET specific surface area of from 11 to 35 m 2 /g, measured using nitrogen and the BET method according to ISO 9277.

7. The coating formulation according to claim 1 , wherein the hedgehog shaped particles have a BET specific surface area of from 15 to 20 m 2 /g, measured using nitrogen and the BET method according to ISO 9277.

8. The coating formulation according to claim 1 , wherein the hedgehog shaped particles have a weight median particle diameter d 50 of from 1 μm to 50 μm.

9. The coating formulation according to claim 1 , wherein the hedgehog shaped particles have a weight median particle diameter d 50 of from 2 μm to 40 μm.

10. The coating formulation according to claim 1 , wherein the hedgehog shaped particles have a weight median particle diameter d 50 of from 3 μm to 30 μm.

11. The coating formulation according to claim 1 , wherein the hydrophobizing agent is selected from the group consisting of fatty acids, stearic acid, palmitic acid, and their salts; alkylketene dimer; polyacrylamide resins; silicone resins, polysiloxanes, polysiloxane modified with a functional silicone resin, and any mixture thereof.

12. The coating formulation according to claim 1 , wherein the hydrophilizing agent is selected from the group consisting of polyacrylic acids, salts of 1-hydroxyethane-1,1-diphosphonic acid, alkali metal salts thereof, potassium salts thereof; chelates of 1-hydroxyethane-1,1-diphosphonic acid, aluminium hydroxide chelates thereof, aluminium hydroxide/1-hydroxyethane-1,1-diphosphonic acid chelates having a weight ratio of 1:5, and any mixture thereof.

13. The coating formulation according to claim 1 , wherein the at least one hydrophilizing agent in part (i) is, or the hydrophobizing agent and the least one hydrophilizing agent in part (ii) are, present in a total amount of from 0.4 to 1.9 wt %, based on the weight of the hedgehog shaped particles in part (i) and part (ii), respectively.

14. The coating formulation according to claim 1 , wherein the at least one hydrophilizing agent in part (i) is, or the hydrophobizing agent and the least one hydrophilizing agent in part (ii) are, present in a total amount of from 0.5 to 1.5 wt %, based on the weight of the hedgehog shaped particles in part (i) and part (ii), respectively.

15. The coating formulation according to claim 1 , wherein the binder is a styrene-acrylic latex, an acrylonitrile, a polyvinyl alcohol or linseed oil.

16. The coating formulation according to claim 1 , wherein the binder is present in an amount of up to 250 wt %, based on the weight of the hedgehog shaped particles.

17. The coating formulation according to claim 1 , wherein the binder is present in an amount of up to 200 wt %, based on the weight of the hedgehog shaped particles.

18. The coating formulation according to claim 1 , wherein the binder is present in an amount of up to 150 wt %, based on the weight of the hedgehog shaped particles.

19. The coating formulation according to claim 1 , wherein the binder is present in an amount of up to 120 wt %, based on the weight of the hedgehog shaped particles.

20. The coating formulation according to claim 1 , wherein the binder is present in an amount of 1 to 50 wt %, based on the weight of the hedgehog shaped particles.

21. The coating formulation according to claim 1 , wherein the binder is present in an amount of 3 to 25 wt %, based on the weight of the hedgehog shaped particles.

22. The coating formulation according to claim 1 , wherein the binder is present in an amount of 5 to 20 wt %, based on the weight of the hedgehog shaped particles.

23. The coating formulation according to claim 1 , wherein the binder is present in an amount of 10 to 15 wt %, based on the weight of the hedgehog shaped particles.

24. The coating formulation according to claim 1 , further comprising additives selected from the group consisting of dispersing agents, siliconizing agents, thickeners, rheology modifiers anti-settling agents defoamers, antioxidants, bluing agents, surfactants, crosslinkers, flame retardants, catalysts, pH buffers, fillers, dyes, pigments, optical brightners, waxes, coalescence agents, biocides and any mixture thereof.

25. The coating formulation according to claim 1 , which is thixotropic.

26. A material coated with the coating formulation according to claim 1 , wherein the material is selected from the group consisting of paper, board, wall-paper, wood, wood composites, lake board, plastics, foil, concrete, coated or uncoated rendering, plaster, metals, ceramics, stone, brickstone and glass.

Assignees

• Omya Int Ag

Inventors

• Schoelkopf Joachim
• Weitzel Hans-Joachim

Classifications

• D21H17/17

  Ketenes, e.g. ketene dimers · CPC title

• D21H19/385

  Oxides, hydroxides or carbonates · CPC title

• D21H17/00

  Non-fibrous material added to the pulp, characterised by its constitution; Paper-impregnating material characterised by its constitution · CPC title

• C01P2006/22

  Rheological behaviour as dispersion, e.g. viscosity, sedimentation stability · CPC title

• C01P2004/03

  obtained by SEM · CPC title