Abstract

The invention provides an exhaust gas cleaning oxidation catalyst and in particular to an oxidation catalyst for cleaning the exhaust gas discharged from internal combustion engines of compression ignition type (particularly diesel engines). The invention further relates to a catalyzed substrate monolith comprising an oxidizing catalyst on a substrate monolith for use in treating exhaust gas emitted from a lean-burn internal combustion engine. In particular, the invention relates to a catalyzed substrate monolith comprising a first washcoat coating and a second washcoat coating, wherein the second washcoat coating is disposed in a layer above the first washcoat coating.

First claim

The invention claimed is:

1. An oxidation catalyst for the oxidative treatment of a hydrocarbon (HC) and carbon monoxide (CO) in an exhaust gas, the oxidation catalyst comprising a supporting substrate and a plurality of catalyst layers supported on the supporting substrate, wherein each catalyst layer in the plurality of catalyst layers comprises an active metal, a washcoat material for supporting the active metal and a zeolite hydrocarbon adsorbent, and wherein one catalyst layer lies on a catalyst surface layer side and one or more other catalyst layers lie on a side between the said one catalyst layer and the supporting substrate; and wherein:
(a) the amount of zeolite hydrocarbon adsorbent in the said one catalyst layer is greater than the amount of zeolite hydrocarbon adsorbent in the said one or more other catalyst layers, and the concentration of active metal in the said one catalyst layer is the same as or less than the concentration of active metal in the said one or more other catalyst layers; or
(b) the amount of zeolite hydrocarbon adsorbent in the said one catalyst layer is the same as the amount of zeolite hydrocarbon adsorbent in the said one or more other catalyst layers, and the concentration of active metal in the said one catalyst layer is less than the concentration of active metal in the said one or more other catalyst layers;

and wherein:
each washcoat material is selected from the group consisting of optionally stabilised alumina, amorphous silica-alumina, optionally stabilised zirconia, ceria, titania, optionally stabilised ceria-zirconia mixed oxide, a zeolite molecular sieve or a mixture of any two or more thereof; and
each active metal is a base metal or a platinum group metal, wherein the base metal is copper, manganese, cobalt or zinc, and the platinum group metal is platinum, palladium or a mixture thereof;
wherein the supporting substrate is a substrate monolith, the said one catalyst layer is a first washcoat coating and one of the said other catalyst layers is a second washcoat coating; and wherein the first washcoat coating comprises a catalyst composition comprising platinum and at least one support material for the platinum, and the second washcoat coating comprises a catalyst composition comprising both platinum and palladium and at least one support material for the platinum and the palladium and wherein a weight ratio of platinum to palladium in the second washcoat coating is ≤2.

2. An oxidation catalyst according to claim 1 , wherein the one catalyst layer has a concentration of hydrocarbon adsorbent of 0.05 to 3.00 gin −3 .

3. An oxidation catalyst according to claim 1 , wherein the catalyst has a ratio by amount of hydrocarbon adsorbent in the said one catalyst layer to the said one or more other catalyst layers of 10:1 to 1.1:1.

4. An oxidation catalyst according to claim 1 , wherein said one catalyst layer is a first washcoat coating and one of the said other catalyst layers is a second washcoat coating and wherein said first or second washcoat coating has a concentration of hydrocarbon adsorbent of 10 to 50% by weight of the layer.

5. An oxidation catalyst according to claim 1 , wherein the one or more other catalyst layers have a concentration of active metal of 0.05 to 3.5 gin −3 .

6. An oxidation catalyst according to claim 1 , wherein the ratio by concentration of active metal in the said one catalyst layer to the said one or more other catalyst layers is 1:50 to 1:1.1.

7. An oxidation catalyst according to claim 1 , wherein the washcoat material comprises a zeolite and the active metal is supported on the zeolite.

8. An oxidation catalyst according to claim 7 , wherein the washcoat material further comprises optionally stabilised alumina, amorphous silica-alumina, optionally stabilised zirconia, ceria, titania, optionally stabilised ceria-zirconia mixed oxide, or a mixture of any two or more thereof.

9. A catalysed substrate monolith comprising an oxidising catalyst on a substrate monolith for use in treating exhaust gas emitted from a lean-burn internal combustion engine, which catalysed substrate monolith comprising a first washcoat coating and a second washcoat coating, wherein the second washcoat coating is disposed in a layer above the first washcoat coating, wherein the first washcoat coating comprises a catalyst composition comprising platinum and at least one support material for the platinum, wherein the second washcoat coating comprises a catalyst composition comprising both platinum and palladium and at least one support material for the platinum and the palladium and wherein a weight ratio of platinum to palladium in the second washcoat coating is ≤2.

10. The catalysed substrate monolith according to claim 9 , wherein the substrate monolith is a flow-through substrate monolith.

11. The catalysed substrate monolith according to claim 9 , wherein the second washcoat coating comprises both platinum and palladium and wherein the first washcoat coating comprises both platinum and palladium at a higher Pt:Pd weight ratio than in the second washcoat coating.

12. The catalysed substrate monolith according to claim 9 , wherein a Pt:Pd weight ratio of both the first washcoat coating and the second washcoat coating combined is ≥1:1.

13. The catalysed substrate monolith according to claim 12 , wherein a Pt:Pd weight ratio of both the first washcoat coating and the second washcoat coating combined is ≥2:1.

14. The catalysed substrate monolith according to claim 9 , wherein a Pt:Pd weight ratio of both the first washcoat coating and the second washcoat coating combined is ≤10:1.

15. An exhaust system for a lean-burn internal combustion engine, which system comprises a first catalysed substrate monolith according to claim 9 .

16. The exhaust system according to claim 15 , comprising a second catalysed substrate monolith comprising a selective catalytic reduction (SCR) catalyst, which second catalysed substrate monolith being disposed downstream from the first catalysed substrate monolith.

17. A lean-burn internal combustion engine, particularly for a vehicle, comprising an exhaust system according to claim 9 .

18. A method of reducing or preventing a selective catalytic reduction (SCR) catalyst in an exhaust system of a lean-burn internal combustion engine from becoming poisoned with platinum which may volatilise from a first washcoat coating comprising a catalyst composition comprising platinum and at least one support material for the platinum disposed on a substrate monolith upstream of the SCR catalyst when the catalyst composition comprising platinum is exposed to relatively extreme conditions including relatively high temperatures, which method comprising trapping volatilised platinum in a second washcoat coating disposed in a layer above the first washcoat coating, which second washcoat coating comprising a catalyst composition comprising both platinum and palladium and at least one support material for the platinum and the palladium and wherein a weight ratio of platinum to palladium in the second washcoat coating is ≤2.

Assignees

• Johnson Matthey Plc

Inventors

• Blakeman Philip Gerald
• Brown Gavin Michael
• Chatterjee Sougato
• Chiffey Andrew Francis
• Gast Jane
• Phillips Paul Richard
• Oyamada Hanako
• Rajaram Raj Rao
• Sumiya Satoshi
• Walker Andrew Peter
• Wang Lifeng

Classifications

• B01D2255/2065

  Cerium · CPC title

• B01D2255/1023

  Palladium · CPC title

• B01J2229/186

  not in framework positions · CPC title

• B01D2258/012

  Diesel engines and lean burn gasoline engines · CPC title

• B01J37/038

  to form slurries or suspensions, e.g. a washcoat · CPC title