Matrices and sealants which are based on sulfur-containing polymers and which comprise a photoinitiator, curing and coating methods, and use of said matrices and sealants

Patent metadata

Field	Value
Publication number	US-10370562-B2
Application number	US-201314391590-A
Country	US
Kind code	B2
Filing date	Apr 9, 2013
Priority date	Apr 12, 2012
Publication date	Aug 6, 2019
Grant date	Aug 6, 2019

Abstract

A method for curing a mixture of a matrix and a curing agent based on sulfur-containing polymers on command and so rapidly that a tack-free surface results. A method for coating a substrate with the composition and of curing a sealant is also provided. The matrix and curing agent containing sulfur-containing polymers. The mixture is an uncured mixture with an isocyanate content, and the matrix is uncured and contains a mercaptan-terminated base polymer based on at least one polyether, polythioether, polysulfide or copolymers thereof. The uncured matrix, the curing agent, or both contain at least one photoinitiator based on sterically-inhibited tertiary amines. The mixture cures in the temperature range of −10 to +70° C. after the high-energy actinic radiation is applied. Corresponding matrices A, mixtures B, curing agents, sealant systems, and substrates, e.g., aircraft are contemplated.

First claim

The invention claimed is:

1. A method for coating a substrate with a mixture B or with a curing sealant produced therefrom, wherein the mixture B and the sealant contain sulfur-based polymers,
wherein the mixture B comprises an uncured mixture of
a matrix A which is uncured and contains a mercapto-terminated polymer based on polythioether, polysulfide, copolymers thereof, and/or mixtures thereof, wherein the mercapto-terminated polymer has a mercaptan content, based on the reactive SH groups to the total weight of the polymer, in the range of 0.8 to 8 wt %, and
a curing agent that contains isocyanate having an average functionality in the range of from 1.5 to 3.2;
wherein the uncured matrix A, the curing agent or both further comprise at least one photoinitiator, which includes an α-aminoketone;
wherein the at least one photoinitiator splits off at least one free radical per molecule based on tertiary amine on exposure to high-energy actinic radiation, and an active catalyst is formed from the amine by uptake of hydrogen and acts as a catalyst for curing the sealant; and
wherein the matrix A and the sealant are free of (meth)acrylate-based compounds and polymers;
the method comprising
exposing mixture B to high-energy actinic radiation at a temperature in the range from −10 to +70° C.,
where mixture B becomes a sealant when curing starts.

2. The method according to claim 1 , wherein the curing takes place on demand, that the mixture B begins to cure more rapidly due to high-energy actinic radiation only on demand, and that curing proceeds to form a tack-free surface of the sealant in a tack-free time of 0.05 to 5 minutes, measured from when curing starts.

3. The method according to claim 1 , wherein the photoinitiator releases and/or forms an amine on exposure to high-energy actinic radiation, and that the amine thereby released and/or formed catalyzes a reaction between mercapto-terminated based polymer and isocyanate-based curing agent.

4. The method according to claim 1 , wherein the photoinitiator triggers and/or accelerates a reaction of isocyanate groups with mercapto groups when mixture B is exposed to a high-energy actinic radiation.

5. The method according to claim 1 , wherein the matrix A, the curing agent, the mixture B and/or the sealant further comprises at least one additive selected from the group consisting of photosensitizers, fillers, lightweight fillers, thixotropy agents, plasticizers, adhesion promoters, antiaging agents, water scavengers, flame retardants, crosslinking agents and organic solvents.

6. The method according to claim 1 , wherein when including fillers and/or additional additives to matrix A and/or mixture B, the fillers and/or additional additives are permeable to the selected radiation.

7. The method according to claim 1 , wherein the curing agent contains sulfur-based prepolymers with a polymer backbone based on polythioether, polysulfide, copolymers containing an amount of polythioether and/or polysulfide and/or mixtures thereof, wherein the prepolymers are isocyanate-terminated.

8. The method according to claim 1 , wherein a processing time according to DIN 65262-1 is in the range of 0.5 to 5 minutes after initiating the high-energy actinic radiation.

9. The method of claim 1 , wherein the substrate is an aircraft component.

10. The method of claim 1 , wherein the substrate is selected from the group consisting of a construction element, an aircraft, a space vehicle, an automobile, a rail vehicles, a ship, equipment, a machine, a building, furniture, and an electronic device.

11. A method as in claim 1 , which method also comprises joining elements, or sealing and/or filling hollow spaces and/or intermediate spaces of elements.

12. The method of claim 1 wherein the isocyanate is
a monomer, oligomer and/or prepolymer based on hexamethylene diisocyanate, isophorone diisocyanate, diphenylmethane diisocyanate and/or toluene diisocyanate, or
a polyisocyanate which is at least one hexamethylene polyisocyanate, at least one isophorone polyisocyanate, at least one toluene polyisocyanate and/or at least one diphenylmethane polyisocyanate.

Assignees

• Chemetall Gmbh

Inventors

• Kralev Miroslav
• Sievers Björn
• Bons Peter
• Diez Francisco

Classifications

• C09D181/00

  Coating compositions based on macromolecular compounds obtained by reactions forming in the main chain of the macromolecule a linkage containing sulfur, with or without nitrogen, oxygen, or carbon only; Coating compositions based on polysulfones; Coating compositions based on derivatives of such polymers · CPC title

• C08L81/04

  Polysulfides · CPC title

• C09D181/04 Primary

  Polysulfides · CPC title

• C08L81/00

  Compositions of macromolecular compounds obtained by reactions forming in the main chain of the macromolecule a linkage containing sulfur with or without nitrogen, oxygen or carbon only; Compositions of polysulfones; Compositions of derivatives of such polymers · CPC title

• B05D7/24

  for applying particular liquids or other fluent materials · CPC title