Plastic container having pearl-like appearance and process for producing the same

Patent metadata

Field	Value
Publication number	US-10370139-B2
Application number	US-201615222634-A
Country	US
Kind code	B2
Filing date	Jul 28, 2016
Priority date	Jul 13, 2005
Publication date	Aug 6, 2019
Grant date	Aug 6, 2019

Abstract

This invention provides a plastic container characterized in that an expanded layer comprising expanded cells having a flat shape with an average major axis of not more than 400 μm and an average aspect ratio (L/t) of not less than 6 as viewed in cross section of the container wall along the maximum stretch direction, which are oriented in the stretch direction and are distributed so as to be superimposed on top of each other in the thickness-wise direction, is formed within the container wall. In this container, expanded cells having a flat shape are distributed so as to orient in a given direction and, thus, has light shielding properties and has a pearl-like appearance, that is, has a very high commercial value. Further, since any colorant is not contained, the suitability for recycling is excellent.

First claim

The invention claimed is:

1. A process for producing a foamed preform for forming a container by preparing an unfoamed preform for forming a container of a single-layer structure using a thermoplastic resin imbibing an inert gas, and forming the unfoamed preform by selectively heating part of said unfoamed preform in a manner that a portion corresponding to the mouth of the container and the vicinity thereof are not foamed.

2. The process for producing a foamed preform according to claim 1 , wherein said thermoplastic resin is injection-formed or extrusion-formed into a preform imbibing no inert gas, and the preform imbibing no inert gas is held in an atmosphere of said inert gas of a high pressure to form said unfoamed preform.

3. The process for producing a foamed preform according to claim 2 , wherein the preform imbibing no inert gas is of a shape including a neck portion that has a thread formed on an outer surface thereof, a body portion continuous to the neck portion, and a bottom portion, the preform imbibing no inert gas is heated and cooled in a manner that the neck portion is selectively crystallized and, thereafter, the preform imbibing no inert gas is held in the atmosphere of the inert gas of a high pressure.

4. The process for producing a foamed preform according to claim 1 , wherein, by using a forming machine equipped with a melt-kneading unit, said thermoplastic resin and said inert gas are fed into said melt-kneading unit, and a melt of the thermoplastic resin imbibing said inert gas is injected or extruded from said forming machine to thereby prepare said unfoamed preform imbibing the inert gas.

5. The process for producing a foamed preform according to claim 4 , wherein the melt of said thermoplastic resin imbibing the inert gas is injection-filled in a mold from said forming machine to thereby prepare said unfoamed preform imbibing the inert gas.

6. The process for producing a foamed preform according to claim 1 , wherein the unfoamed preform imbibing no inert gas is held at atmospheric pressure as part of the inert gas is released to form a skin layer which contains no inert gas on a surface of the unfoamed preform, and thereafter, the unfoamed preform is heated and is foamed.

7. The process for producing a foamed preform according to claim 1 , wherein the unfoamed preform is heated and foamed in a manner that an average cell diameter of foamed cells formed by heating is in a range of 5 to 50 μm and that the cell density is 10 6 to 10 9 cells/cm 3 .

8. The process for producing a foamed preform according to claim 1 , wherein the unfoamed preform is heated in a manner that no foamed cell is formed in a central portion of the unfoamed preform in the direction of thickness thereof to thereby form an unfoamed core layer therein.

9. The process for producing a foamed preform according to claim 1 , wherein after the unfoamed preform has been foamed, the obtained foamed preform is cooled.

10. A process for producing a foamed plastic container by stretch-forming the foamed preform of claim 1 .

11. The process according to claim 10 , wherein the foamed preform of claim 1 is cooled and is, thereafter, heated again at a temperature at which it can be stretched so as to be stretch-formed.

12. The process for producing a foamed preform according to claim 1 , wherein the thermoplastic resin is a polyester resin.

Assignees

• Toyo Seikan Kaisha Ltd

Inventors

• Ichikawa Kentarou
• Koiso Nobuhisa

Classifications

• B29C2949/0715

  the preform having one end closed · CPC title

• B29C49/071

  Preforms or parisons characterised by their configuration, e.g. geometry, dimensions or physical properties · CPC title

• B29K2023/065

  HDPE, i.e. high density polyethylene · CPC title

• B29C44/352

  Means for giving the foam different characteristics in different directions · CPC title

• B29B2911/14333

  Operations & Transport · mapped topic