Method and alloys for low pressure permanent mold without a coating

Patent metadata

Field	Value
Publication number	US-10364484-B2
Application number	US-201715471668-A
Country	US
Kind code	B2
Filing date	Mar 28, 2017
Priority date	Mar 28, 2017
Publication date	Jul 30, 2019
Grant date	Jul 30, 2019

Abstract

A method and alloys for low pressure permanent mold casting without a coating are disclosed. The method includes preparing a permanent mold casting die that is devoid of die coating or lubrication along the die surface, preparing a permanent mold casting alloy, pushing the alloy into the die under low pressure, cooling the permanent mold casting, and removing the casting from the die. One alloy has 4.5-11.5% by weight silicon; 0.45% by weight maximum iron; 0.20-0.40% by weight manganese; 0.045-0.110% by weight strontium; 0.05-5.0% by weight copper; 0.01-0.70% by weight magnesium; and the balance aluminum. Another alloy has 4.2-5.0% by weight copper; 0.005-0.45% by weight iron; 0.20-0.50% by weight manganese; 0.15-0.35% by weight magnesium; 0.045-0.110% by weight strontium; 0.50% by weight maximum nickel; 0.10% by weight maximum silicon; 0.15-0.30% by weight titanium; 0.05% by weight maximum tin; 0.10% by weight maximum zinc; and the balance aluminum.

First claim

What is claimed is:

1. A method for low pressure permanent mold casting of metallic objects, the method comprising:
preparing a permanent mold casting die, said die devoid of die coating or lubrication along a die casting surface;
preparing a permanent mold casting alloy having 4.5-11.5% by weight silicon, 0.45% by weight maximum iron, 0.20-0.40% by weight manganese, 0.045-0.110% by weight strontium, 0.05-5% by weight copper, 0.10-0.7% by weight magnesium, and balance aluminum and wherein the alloy has a die soldering factor equivalent to or greater than 1.1, the die soldering factor defined as (10[Sr]+Mn+Fe);
pushing the alloy into the permanent mold casting die under pressure of 3-15 psi to create a permanent mold casting;
cooling the permanent mold casting; and
removing the permanent mold casting from the die without force;
wherein the permanent mold casting does not solder to the permanent mold die; and
wherein the surface roughness of the casting is ±500 microinches R a or less.

2. The method of claim 1 , wherein the alloy includes 0.50% by weight maximum nickel.

3. The method of claim 1 , wherein a step of heat treating the casting is added after the step of removing the casting from the die.

4. The method of claim 1 , wherein the step of cooling the permanent mold casting further comprises solidifying the alloy without formation of primary intermetallics.

5. The method of claim 4 , wherein the primary intermetallics are Al 5 FeSi or Al 15 (MnFe) 3 Si 2 .

6. The method of claim 1 , wherein the permanent mold casting is an L-bracket.

7. The method of claim 1 , wherein the permanent mold casting is a gear case housing with an integral splash plate.

8. The method of claim 1 , wherein the step of preparing a permanent mold casting die includes preparing a permanent mold casting die having at least one thin walled section.

9. The method of claim 8 , wherein the step of pushing the alloy into the permanent mold casting die includes pushing the alloy into at least one thin walled section before the alloy solidifies.

10. The method of claim 1 , wherein the method is fully automated.

11. A method for low pressure permanent mold casting of metallic objects, the method comprising:
preparing a permanent mold casting die, said die devoid of die coating or lubrication along a die casting surface;
preparing a permanent mold casting alloy having 4.2-5.0% by weight copper; 0.005-0.45% by weight iron; 0.20-0.50% by weight manganese; 0.15-0.35% by weight magnesium; 0.045-0.110% by weight strontium; 0.05% by weight maximum nickel; 0.10% by weight maximum silicon; 0.15-0.30% by weight titanium; 0.05% by weight maximum tin; 0.10% by weight maximum zinc; and balance aluminum and wherein the alloy has a die soldering factor equivalent to or greater than 1.1, the die soldering factor defined as (10[Sr]+Mn+Fe);
pushing the alloy into the permanent mold casting die under pressure of 3-15 psi to create a permanent mold casting;
cooling the permanent mold casting; and
removing the permanent mold casting from the die without force;
wherein the permanent mold casting does not solder to the permanent mold die; and
wherein the surface roughness of the casting is ±500 microinches or less.

12. The method of claim 11 , wherein a step of heat treating the casting is added after the step of removing the casting from the die, and the steps of preparing, pushing, cooling, heat treating and removing are fully automated.

13. The method of claim 11 , wherein the step of preparing a permanent mold casting die includes preparing a permanent mold casting die having at least one thin walled section, and wherein the step of pushing the alloy into the permanent mold casting die includes pushing the alloy into at least one thin walled section before the alloy solidifies.

Assignees

• Brunswick Corp

Inventors

• Donahue Raymond J
• Monroe Alexander K
• Anderson Kevin R
• Cleary Terrance M

Classifications

• B22D18/04 Primary

  Low pressure casting, i.e. making use of pressures up to a few bars to fill the mould · CPC title

• B22D21/007

  with low melting point, e.g. Al 659 degrees C, Mg 650 degrees C · CPC title

• C22C21/04

  Modified aluminium-silicon alloys · CPC title

• C22C21/12

  with copper as the next major constituent · CPC title

• C22C21/14

  with silicon · CPC title