Shape memory polymer, preparation method therefor, and use thereof

Patent metadata

Field	Value
Publication number	US-10364312-B2
Application number	US-201715795311-A
Country	US
Kind code	B2
Filing date	Oct 27, 2017
Priority date	Apr 28, 2015
Publication date	Jul 30, 2019
Grant date	Jul 30, 2019

Abstract

The present invention relates to the field of shape memory materials. Specifically, a shape memory polymer, a preparation method therefor, and use thereof are provided. The shape memory polymer is formed by polymerizing methyl ally polyethenoxy ether and 2-(dimethylamino)ethyl methacrylate. The synthesis steps of the shape memory polymer are simplified, the preparation method is simple, and the production cost is low. In addition, the shape memory polymer prepared in the present invention has excellent shape memory performance and high hydrophilicity and biocompatibility, and is suitable for preparing biomedical materials in the field of biomedical science.

First claim

The invention claimed is:

1. A shape memory polymer formed by polymerizing methyl allyl polyethenoxy ether and 2-(dimethylamino)ethyl methacrylate, having a structure represented by Formula I:

2. The shape memory polymer according to claim 1 , wherein the weight ratio of the raw materials methyl allyl polyethenoxy ether to 2-(dimethylamino)ethyl methacrylate is 8:2-2:8.

3. The shape memory polymer according to claim 1 , wherein the weight ratio of methyl allyl polyethenoxy ether to 2-(dimethylamino)ethyl methacrylate in the polymer is 8:2-2:8.

4. The shape memory polymer according to claim 1 , wherein the shape memory polymer has a molecular weight of 10000-100000.

5. A method for preparing the shape memory polymer according to claim 1 , comprising: adding methyl allyl polyethenoxy ether, 2-(dimethylamino)ethyl methacrylate, water and an initiator, under the protection of a protective gas, reacting at 50-80° C. for 8-24 hrs with stirring, and drying, to obtain the shape memory polymer.

6. The preparation method according to claim 5 , wherein the protective gas is nitrogen; and the water is added in an amount of 2-3 times of the total weight of the methyl allyl polyethenoxy ether and the 2-(dimethylamino)ethyl methacrylate.

7. The preparation method according to claim 5 , wherein the initiator is ammonium persulfate, and used in an amount of 5-10 mM.

8. The preparation method according to claim 5 , wherein the reaction is stirred at 60° C. for 10 hrs.

9. The preparation method according to claim 5 , wherein the drying is done through a process comprising: adjusting the mass fraction of the polymer in the solution to 10-30% after reaction, then pouring the solution into a mold, drying for 12-24 hrs in an air-blowing drier at 80-100° C., and then drying for 12-24 hrs under vacuum, to obtain the shape memory polymer.

Assignees

• Univ Shenzhen

Inventors

• Chen Shaojun
• Chen Yangyang
• Mo Funian
• Zhuo Haitao

Classifications

• B29C39/003

  characterised by the choice of material · CPC title

• B29C39/38

  Heating or cooling · CPC title

• B29K2033/08

  Polymers of acrylic acid esters, e.g. PMA, i.e. polymethylacrylate · CPC title

• C08F220/34 Primary

  Esters containing nitrogen {, e.g. N,N-dimethylaminoethyl (meth)acrylate} · CPC title

• C08F216/20 Primary

  Monomers containing three or more carbon atoms in the unsaturated aliphatic radical · CPC title