Method for thermal control of cast-in components during manufacturing

Patent metadata

Field	Value
Publication number	US-10363601-B2
Application number	US-201514865190-A
Country	US
Kind code	B2
Filing date	Sep 25, 2015
Priority date	Sep 25, 2015
Publication date	Jul 30, 2019
Grant date	Jul 30, 2019

Abstract

A method for forming a product having cast-in components provides an insulating barrier of solidified sand formed next to the insider diameter of the cast-in component. The center of the solidified sand is hollow. Before pouring the molten metal into the primary runner/riser system that feeds the portion of the mold that will create the actual part, the molten material is poured into the hollow portion of the solidified sand through a separate runner/riser system. This molten metal provides the energy necessary to heat the cast-in part to an acceptable temperature. The temperature can be controlled by the shape, thickness and material of the insulating member. This controlled time/temperature profile enables the creation of a final cast product that demonstrates good quality properties at the cast/insert interface. The method of the disclosed inventive concept has the added benefit of not altering the resulting part itself.

First claim

What is claimed is:

1. A method of forming a cast part, the method comprising:
forming a part-forming mold having a lower portion and an upper portion;
placing a metal component in said lower portion, said metal component having a hollow area;
placing an insulating material in said hollow area and surrounding said metal component, said insulating material having a cavity formed therein;
melting a quantity of metal to provide a molten metal;
pouring a portion of said molten metal into said cavity;
placing said upper portion over said lower portion to form said mold, said upper portion being separate from said insulating material; and
pouring a remainder of said molten metal into said mold.

2. The method of forming a cast part of claim 1 including identifying a selected temperature for said metal component and pouring the remainder of said molten metal into said mold after said metal component reaches said selected temperature.

3. The method of forming a cast part of claim 1 wherein said upper portion is placed over said lower portion after said portion of said molten metal is placed in said cavity of said insulating material.

4. The method of forming a cast part of claim 1 wherein said metal component is a cast iron metal component.

5. The method of forming a cast part of claim 1 wherein said metal component is a cylinder liner.

6. The method of forming a cast part of claim 1 wherein said insulating material is solidifiable sand.

7. The method of forming a cast part of claim 1 wherein said molten metal is aluminum.

8. A method of forming a cast part, the method comprising:
forming a mold having upper and lower portions;
forming a metal component, said metal component having a hollow area;
placing said metal component in said lower portion;
placing an insulating material having a cavity in said hollow area, said insulating material surrounding said metal component;
pouring molten metal into said cavity to heat said metal component;
placing said upper portion over said lower portion to form said mold, said upper portion being separate from said insulating material; and
pouring molten metal into said mold.

9. The method of forming a cast part of claim 8 including identifying a selected temperature for said metal component and pouring said molten metal into said cavity to heat said metal component after said metal component reaches said selected temperature.

10. The method of forming a cast part of claim 8 wherein said upper portion is placed over said lower portion before said molten metal is poured into said cavity to heat said metal component.

11. The method of forming a cast part of claim 8 wherein said molten metal poured into said cavity and said molten metal poured into said mold are the same metal.

12. The method of forming a cast part of claim 8 wherein said metal component is a cast iron metal component.

13. The method of forming a cast part of claim 8 wherein said metal component is a cylinder liner.

14. The method of forming a cast part of claim 8 wherein said molten metal is aluminum.

15. A method of forming a cast part, the method comprising:
forming a mold having upper and lower portions;
placing a component having a hollow area in said lower portion;
placing an insulating material having a cavity in said area, said insulating material surrounding said component;
placing said upper portion over said lower portion to form a mold package, said upper portion being separate from said insulating material;
pouring a first portion of a molten metal into said cavity; and
pouring a second portion of said molten metal into said mold substantially around said component.

16. The method of forming a cast part of claim 15 including identifying a selected temperature for said component and pouring said first portion of said molten metal into said cavity to heat said component after said component reaches said selected temperature.

17. The method of forming a cast part of claim 15 wherein said component is a metal component.

18. The method of forming a cast part of claim 17 wherein said metal component is a cast iron metal component.

19. The method of forming a cast part of claim 18 wherein said cast iron metal component is a cylinder liner.

20. The method of forming a cast part of claim 15 wherein said molten metal is aluminum.

Assignees

• Ford Global Tech Llc
• Ford Motor Co

Inventors

• Susalla Paul Christopher
• Hassenbusch Ronald H

Classifications

• B22D19/00 Primary

  Casting in, on, or around objects which form part of the product (B22D23/04 takes precedence; alumino-thermic welding B23K23/00; coating by casting molten material on the substrate C23C6/00) · CPC title

• B22D25/02

  by its peculiarity of shape; of works of art {(cylinders, pistons B22D15/02)} · CPC title

• B22D21/04

  Casting aluminium or magnesium {(no material; see B22D21/007)} · CPC title

• B22D19/0009 Primary

  Cylinders, pistons · CPC title

• B22C9/24

  for hollow articles · CPC title